A kind of inkjet bleeding marble tile

A technology for marble and infiltration, applied in the field of marble tiles and inkjet infiltration marble tiles, can solve the problems of high production cost, poor wear resistance, anti-slip resistance, and poor antifouling ability of inkjet full-polished glazed tiles, and achieves decoration. Works well with application, with clear texture and complete pattern

Active Publication Date: 2018-07-31
四川省新万兴瓷业有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Compared with the bleed polished tiles, the inkjet fully polished glazed tiles have richer patterns, brighter colors, and clearer textures, but their wear resistance and anti-slip properties are poor, and during processing, glazed pores are very easy to occur, thus As a result, its antifouling ability is poor, and the production cost of inkjet fully glazed tiles is relatively high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] (1) Evenly mix ceramic green body powder feldspar, quartz, kaolin with 5% ammonia water, ethylenediamine, trisodium citrate dihydrate, wherein ammonia water, ethylenediamine, lemon dihydrate The mass ratio of trisodium acid is 3:3:4, and after mixing uniformly, it is compressed into a ceramic green body at 30Mpa in a brick press;

[0034] (2) Spray 200g / m² of nano-penetration aid on the surface of the ceramic green body. The nano-penetration aid is a mixture of active water, sodium carboxymethyl cellulose (CMC) and ethylene glycol. The mass ratio of cellulose sodium (CMC) to ethylene glycol is 6:1:3;

[0035] (3) After 5 minutes, the nano-penetration aid is dried, and the bleed glaze is printed with 8-channel computer inkjet using a 5D inkjet machine. The bleed glaze contains a colorant and a modified starch binder, and the modified starch binder is ethylene glycol. , the viscosity of the oozing glaze after the two are blended is 200mPa.s;

[0036] (4) Spray a nano-co...

Embodiment 2

[0040] (1) Mix the ceramic green body powder feldspar, quartz, kaolin and the mixture consisting of 10% ammonia water, ethylenediamine and trisodium citrate evenly, wherein the ammonia water, ethylenediamine and trisodium citrate The mass ratio is 1:1:1, and after mixing evenly, press it in a brick press at 30Mpa to form a ceramic green body;

[0041] (2) Spray 250g / m² of nano-penetration aid on the surface of the ceramic green body. The nano-penetration aid is a mixture of active water, sodium carboxymethyl cellulose (CMC) and ethylene glycol. The mass ratio of cellulose sodium (CMC) and ethylene glycol is 6:2:3 respectively;

[0042] (3) After 10 minutes, the nano-penetration aid is dried, and the bleed glaze is printed with 8-channel computer inkjet 5D inkjet machine. The bleed glaze contains colorant and modified starch binder, and the modified starch binder is ethylene glycol. , the viscosity after the two are blended is 300mPa.s;

[0043] (4) Spray a nano-coloring agen...

Embodiment 3

[0047](1) Evenly mix ceramic green body powder feldspar, quartz, kaolin with 10% ammonia water, ethylenediamine, trisodium citrate dihydrate, wherein ammonia water, ethylenediamine, lemon dihydrate The mass ratio of trisodium acid is 2:1:2, and after mixing uniformly, it is compressed into a ceramic green body at 30Mpa in a brick press;

[0048] (2) Spray 300g / m² of nano-penetration aid on the surface of the ceramic green body. The nano-penetration aid is a mixture of active water, sodium carboxymethyl cellulose (CMC) and ethylene glycol. The mass ratio of cellulose sodium (CMC) to ethylene glycol is 6:3:2;

[0049] (3) After 10 minutes, the nano-penetration aid is dried, and the bleed glaze is printed with 8-channel computer inkjet 5D inkjet machine. The bleed glaze contains colorant and modified starch binder, and the modified starch binder is ethylene glycol. , the viscosity after the two are blended is 250mPa.s;

[0050] (4) Spray a nano-coloring agent with a quality of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
thicknessaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ink jet pattern seeping marble tile, which consists of a blank body and enamel seeped into the blank body, and is formed by firing a ceramic raw blank containing a nanometer stabilizing agent and the enamel layer containing a nanometer seeping aid, pattern seeping enamel and a nanometer color former. The color and the patterns of the ink jet pattern seeping marble tile are generated in a position being 1.5 to 2.0mm inside the ceramic blank body; the veins are clear; the colors are rich; the patterns are complete; the pattern effect is good; meanwhile, the surface wear-resistant performance of the ceramic tile is good; the anti-stain performance is good, so that the decoration and application effects are very good; the production steps are simple; the manufacturing cost is low.

Description

technical field [0001] The invention relates to marble tiles, especially the technical field of inkjet bleeding marble tiles. Background technique [0002] Marble tiles refer to ceramic tiles with marble surface characteristics, their appearance is close to marble, and the decorative effect is good, but in some main properties, such as impact resistance, abrasion resistance, flexural strength, water absorption, etc. are superior to natural tiles. Marble has relatively low maintenance costs. [0003] Due to the above-mentioned characteristics of marble tiles, it is more and more widely used in the construction industry, and people's requirements for its performance and decorative effects are also constantly improving. According to the different processing methods of marble tiles, the common ones include bleed polished tiles, inkjet fully polished glazed tiles, etc. [0004] Among them, the bleed polished tile is a polished tile combined with bleed technology. It is a cerami...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/13C04B33/16C04B33/00C04B41/89
CPCC04B33/00C04B33/1305C04B33/131C04B33/16C04B41/009C04B41/52C04B41/89C04B2235/3463C04B2235/96C04B2235/963C04B41/4803C04B41/46C04B41/5022C04B41/5012
Inventor 杨建明费正权
Owner 四川省新万兴瓷业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com