Antirust coating used for steel, and preparation method thereof
An anti-rust paint, steel technology, applied in anti-corrosion paint, coating and other directions, can solve the problems of poor impact resistance, poor flexibility, slow drying, etc., to achieve the effect of smooth and bright appearance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] Weigh 100 parts of epoxy resin, 1 part of isopropanol, 15 parts of butanol, 0.5 part of aluminum paste, 10 parts of butyl acrylate, 6 parts of methyl methacrylate, 4 parts of acrylic acid, benzene 30 parts of ethylene, 2 parts of barium sulfate, 3 parts of zinc phosphate, 5 parts of modified aluminum tripolyphosphate, 0.2 part of sodium bicarbonate, 0.1 part of ammonium persulfate, 6 parts of talcum powder.
[0023] Put epoxy resin, isopropanol, butanol, aluminum powder paste, butyl acrylate, methyl methacrylate and acrylic acid into a reaction kettle equipped with a stirrer and a thermometer, and stir for 10 minutes at a stirring speed of 200 rpm.
[0024] Add the remaining raw materials and grind in a grinder for 15 minutes.
[0025] The appearance of the coating film is smooth and bright, the viscosity is 100s, the surface is dry for 50 minutes, and the hard drying is 19 hours; the flexibility is 1mm, and the adhesion is grade 2; the water resistance is immersed in 3...
Embodiment 2
[0027] Weigh 100 parts of epoxy resin, 5 parts of isopropanol, 35 parts of butanol, 2.5 parts of aluminum paste, 50 parts of butyl acrylate, 14 parts of methyl methacrylate, 8 parts of acrylic acid, benzene 50 parts of ethylene, 6 parts of barium sulfate, 7 parts of zinc phosphate, 9 parts of modified aluminum tripolyphosphate, 0.6 parts of sodium bicarbonate, 0.5 parts of ammonium persulfate, and 10 parts of talcum powder.
[0028] Put epoxy resin, isopropanol, butanol, aluminum powder slurry, butyl acrylate, methyl methacrylate and acrylic acid into a reaction kettle equipped with a stirrer and a thermometer, stir for 30 minutes, and the stirring speed is 300 rpm.
[0029] Add the remaining raw materials and grind in a grinder for 35 minutes.
[0030] The appearance of the coating film is smooth and bright, the viscosity is 105s, the surface is dry for 45 minutes, and the hard drying is 18 hours; the flexibility is 1.5mm, the adhesion is grade 2; the water resistance is imme...
Embodiment 3
[0032]Weigh 100 parts of epoxy resin, 2 parts of isopropanol, 20 parts of butanol, 1 part of aluminum powder paste, 20 parts of butyl acrylate, 8 parts of methyl methacrylate, 5 parts of acrylic acid, benzene 35 parts of ethylene, 3 parts of barium sulfate, 4 parts of zinc phosphate, 6 parts of modified aluminum tripolyphosphate, 0.3 parts of sodium bicarbonate, 0.2 parts of ammonium persulfate, 7 parts of talcum powder.
[0033] Put epoxy resin, isopropanol, butanol, aluminum powder paste, butyl acrylate, methyl methacrylate and acrylic acid into a reaction kettle equipped with a stirrer and a thermometer, and stir for 10 minutes at a stirring speed of 200 rpm.
[0034] Add the rest of the raw materials and grind in a grinder for 15 minutes.
[0035] The appearance of the coating film is smooth and bright, the viscosity is 110s, the surface is dry for 40 minutes, and the hard drying is 17 hours; the flexibility is 2mm, the adhesion is grade 1; the water resistance is immersed...
PUM
Property | Measurement | Unit |
---|---|---|
adhesivity | aaaaa | aaaaa |
adhesivity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap