Anti-rust coating used for metals and containing iron oxide red
A technology of anti-rust coatings and iron red, applied in anti-corrosion coatings, coatings, etc., can solve the problems of slow drying and salt spray resistance of metal coatings, and achieve the effect of excellent water resistance, simple raw materials, and easy-to-obtain raw materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0017] Step 1: Weigh 100 parts of iron red, 40 parts of calcium carbonate, 15 parts of barium sulfate, 10 parts of dibutyl phthalate, 5 parts of ethyl cellulose, and 10 parts of aluminum stearate according to the ratio of parts by mass , 5 parts of diphenylamine, 1 part of benzotriazole, 2 parts of zinc oxide, 4 parts of tributyl phosphate.
[0018] Step 2: Put iron red, calcium carbonate, barium sulfate, dibutyl phthalate and aluminum stearate into the reaction kettle, heat to 140°C, and stir at 200r / min for 10min.
[0019] Step 3: Let the stirred liquid stand for 120 minutes, add ethyl cellulose, diphenylamine, benzotriazole, zinc oxide and tributyl phosphate, mix well at 170°C, put it into a grinder for 16 hours, and filter After packing.
[0020] The appearance of the coating film is smooth and bright, the viscosity is 80s, and the hiding power is 240g / cm 2 ;Excellent water resistance and anti-rust performance, first-class adhesion, salt spray resistance 15d without abno...
Embodiment 2
[0022] Step 1: Weigh 100 parts of iron red, 60 parts of calcium carbonate, 55 parts of barium sulfate, 50 parts of dibutyl phthalate, 45 parts of ethyl cellulose, and 30 parts of aluminum stearate according to the ratio of parts by mass , 25 parts of diphenylamine, 5 parts of benzotriazole, 6 parts of zinc oxide, and 8 parts of tributyl phosphate.
[0023] Step 2: Put iron red, calcium carbonate, barium sulfate, dibutyl phthalate and aluminum stearate into the reaction kettle, heat to 160°C, and stir at 400r / min for 50min.
[0024] Step 3: Let the stirred liquid stand for 160 minutes, add ethyl cellulose, diphenylamine, benzotriazole, zinc oxide and tributyl phosphate, mix evenly at 190°C, put it into a grinder for 20 hours, and filter After packing.
[0025] The appearance of the coating film is smooth and bright, the viscosity is 85s, and the hiding power is 250g / cm 2 ;Excellent water resistance and anti-rust performance, first-class adhesion, no abnormality in salt spray ...
Embodiment 3
[0027] Step 1: Weigh 100 parts of iron red, 45 parts of calcium carbonate, 25 parts of barium sulfate, 20 parts of dibutyl phthalate, 15 parts of ethyl cellulose, and 15 parts of aluminum stearate according to the ratio of parts by mass , 10 parts of diphenylamine, 2 parts of benzotriazole, 3 parts of zinc oxide, 5 parts of tributyl phosphate.
[0028] Step 2: Put iron red, calcium carbonate, barium sulfate, dibutyl phthalate and aluminum stearate into the reaction kettle, heat to 140°C, and stir at 200r / min for 10min.
[0029] Step 3: Let the stirred liquid stand for 120 minutes, add ethyl cellulose, diphenylamine, benzotriazole, zinc oxide and tributyl phosphate, mix well at 170°C, put it into a grinder for 16 hours, and filter After packing.
[0030] The appearance of the coating film is smooth and bright, the viscosity is 90s, and the hiding power is 260g / cm 2 ;Excellent water resistance and anti-rust performance, first-class adhesion, salt spray resistance 35d without a...
PUM
Property | Measurement | Unit |
---|---|---|
mechanical properties | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com