Epoxy resin anti-rust paint with rust for steel and preparation method thereof
A technology of epoxy resin tape and anti-rust coating, which is applied in the direction of epoxy resin coating, anti-corrosion coating, coating, etc., can solve the problems of poor impact resistance, slow drying, poor flexibility, etc., and achieve the effect of smooth and bright appearance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0025] Take by weight 100 parts of epoxy resin, 4 parts of polyvinyl butyral, 0.8 part of tannic acid, 1 part of zinc dihydrogen phosphate, 6 parts of dibutyl phthalate, 40 parts of ethanol, 2 parts of n-trichloroethane, 3 parts of sodium dodecylsulfonate, 5 parts of potassium dichromate, 30 parts of trichloroethane, 8 parts of tung oil, 0.5 parts of glycerin rosin ester, 1 part of soybean oil, 10 parts of polystyrene .
[0026] Put epoxy resin, polyvinyl butyral, tannic acid, zinc dihydrogen phosphate, dibutyl phthalate, ethanol and n-trichloroethane into a reaction kettle equipped with a stirrer and a thermometer, and heat up to 80 ℃, stirred for 30 min, and the stirring speed was 400 rpm.
[0027] Lower the temperature to 40°C, add the remaining raw materials, and grind once in a grinder with a fineness of 20 μm.
[0028] The appearance of the coating film is smooth and bright, the surface is dry for 25 minutes, and the hard work is 10 hours; the flexibility is 130mm, the...
Embodiment 2
[0030] Take by weight 100 parts of epoxy resin, 8 parts of polyvinyl butyral, 1.2 parts of tannic acid, 1.4 parts of zinc dihydrogen phosphate, 10 parts of dibutyl phthalate, 80 parts of ethanol, 6 parts of n-trichloroethane, 7 parts of sodium dodecylsulfonate, 9 parts of potassium dichromate, 50 parts of trichloroethane, 12 parts of tung oil, 4.5 parts of glycerin rosin ester, 5 parts of soybean oil, 30 parts of polystyrene .
[0031] Put epoxy resin, polyvinyl butyral, tannic acid, zinc dihydrogen phosphate, dibutyl phthalate, ethanol and n-trichloroethane into a reaction kettle equipped with a stirrer and a thermometer, and heat up to 120 ℃, stirred for 50min, and the stirring speed was 400-600 rpm.
[0032]Lower the temperature to 60°C, add the remaining raw materials, and grind twice in a grinder with a fineness of 60 μm.
[0033] The appearance of the coating film is smooth and bright, the surface is dry for 20 minutes, and the hard work is 9 hours; the flexibility is ...
Embodiment 3
[0035] Take by weight 100 parts of epoxy resin, 5 parts of polyvinyl butyral, 0.9 part of tannic acid, 1.1 parts of zinc dihydrogen phosphate, 7 parts of dibutyl phthalate, 50 parts of ethanol, 3 parts of n-trichloroethane, 4 parts of sodium dodecylsulfonate, 6 parts of potassium dichromate, 35 parts of trichloroethane, 9 parts of tung oil, 1.5 parts of glycerin rosin ester, 2 parts of soybean oil, 15 parts of polystyrene .
[0036] Put epoxy resin, polyvinyl butyral, tannic acid, zinc dihydrogen phosphate, dibutyl phthalate, ethanol and n-trichloroethane into a reaction kettle equipped with a stirrer and a thermometer, and heat up to 80 ℃, stirred for 30 min, and the stirring speed was 400 rpm.
[0037] Lower the temperature to 40°C, add the remaining raw materials, and grind once in a grinder with a fineness of 20 μm.
[0038] The appearance of the coating film is smooth and bright, the surface is dry for 15 minutes, and the hard work is 8 hours; the flexibility is 150mm, ...
PUM
Property | Measurement | Unit |
---|---|---|
hardness | aaaaa | aaaaa |
hardness | aaaaa | aaaaa |
hardness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com