A kind of modified activated carbon and preparation method and application thereof

A technology of activated carbon and modification, which is applied in the field of catalyst carrier preparation, can solve the problems that the stability needs to be further improved, and achieve the effects of improving anti-methanation ability, concentrated pore size distribution, and good stability

Active Publication Date: 2019-04-05
FUZHOU UNIV
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ruthenium-based ammonia synthesis catalyst prepared by these methods needs further improvement in its activity and stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified activated carbon and preparation method and application thereof
  • A kind of modified activated carbon and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A preparation method of modified activated carbon, the concrete steps are:

[0021] (1) Pretreatment of activated carbon: 5 g of commercial activated carbon was graphitized at 1900 °C for 10 hours in an argon inert atmosphere, and then subjected to pore expansion treatment at 450 °C for 30 hours in an oxygen atmosphere to obtain pretreated activated carbon, washed, dry and ready for use;

[0022] (2) Modification of graphitized activated carbon: The activated carbon pretreated in step (1) was crushed and screened to obtain 12-16 mesh activated carbon particles, soaked in a nitric acid solution with a concentration of 5 wt% at 70 °C, and kept at a constant temperature for 2 h, take it out, wash it with distilled water until neutral, and dry it in an oven at 110 °C for 12 h; then place the dried sample in an ammonia atmosphere at 1100 °C for heat treatment for 2 h, with a gas flow rate of 75ml / min, and drop it to room temperature in the atmosphere Take it out to get the ...

Embodiment 2

[0024] A preparation method of modified activated carbon, the concrete steps are:

[0025] (1) Pretreatment of activated carbon: 5 g of commercial activated carbon was graphitized at 2000 °C for 2 hours in an inert argon atmosphere, and then subjected to pore expansion treatment at 450 °C for 30 hours in an oxygen atmosphere to obtain pretreated activated carbon, washed, dry and ready for use;

[0026] (2) Modification of graphitized activated carbon: The activated carbon pretreated in step (1) was crushed and screened to obtain 12-16 mesh activated carbon particles, soaked in a nitric acid solution with a concentration of 10 wt% at 60 °C, and kept at a constant temperature for 3 h, take it out, wash it with distilled water until neutral, and dry it in an oven at 90 °C for 16 h; then place the dried sample in an ammonia atmosphere at 1100 °C for 2 h, with a gas flow rate of 100ml / min, and drop it to room temperature in the atmosphere Take it out to get the modified activated ...

Embodiment 3

[0028] A preparation method of modified activated carbon, the concrete steps are:

[0029] (1) 5 g of commercial activated carbon was graphitized at 1800 °C for 5 hours in an argon inert atmosphere, and then subjected to pore expansion treatment at 460 °C for 20 hours in an oxygen atmosphere to obtain pretreated activated carbon, which was washed and dried for later use;

[0030] (2) Modification of graphitized activated carbon: The activated carbon pretreated in step (1) was crushed and screened to obtain 12-16 mesh activated carbon particles, soaked in a nitric acid solution with a concentration of 7 wt% at 75 °C, and kept at a constant temperature for 1 h, take it out, wash it with distilled water until neutral, and dry it in an oven at 100 °C for 14 h; then place the dried sample in an ammonia atmosphere at 900 °C for heat treatment for 2 h, with a gas flow rate of 50 ml / min, and take it out when the atmosphere drops to room temperature , the modified activated carbon carr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a modified activated carbon, a preparation method and an application, belonging to the field of preparation of catalyst carriers. The preparation method is as follows: a graphitized activated carbon is treated with HNO 3 After treatment, high-temperature heat treatment is performed in an ammonia atmosphere to obtain an activated carbon carrier with high mesopores. The carrier has the characteristics of large pore volume, high mesoporosity (≥97%), and good conductivity. When used as a catalyst carrier for ammonia synthesis, it can significantly improve the dispersion of the precious metal ruthenium and improve the methanation resistance, thermal stability and activity of the catalyst. It has broad application prospects in the field of catalysis.

Description

technical field [0001] The invention belongs to the field of catalyst carrier preparation, and in particular relates to a modified activated carbon, a preparation method and an application thereof. Background technique [0002] For various agricultural products, fertilizers are extremely important to their growth and increase in yield. To synthesize various fertilizers suitable for crops, the development of the synthetic ammonia industry has played a huge role. Among them, the invention of synthetic ammonia ferric catalyst has created a catalytic ammonia synthesis industry, and the iron catalyst is cheap and stable, and has become one of the most thorough and successful catalysts in the world. However, when iron catalysts are used, the ammonia synthesis reaction must be carried out under high temperature and high pressure conditions, which consumes a lot of energy and requires more stringent equipment. [0003] The emergence of ruthenium catalysts makes it possible to carry...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J21/18B01J23/58C01C1/04
CPCC01C1/0411B01J21/18B01J23/58B01J35/617B01J35/638B01J35/635B01J35/647Y02P20/52
Inventor 倪军罗小芳林建新江莉龙林炳裕
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com