Steel materials for hot stamping forming, hot stamping forming process and hot stamping forming components

A hot stamping forming and stamping forming technology, applied in hot dip plating process, metal material coating process, substructure and other directions, can solve the problems of difficult control, high cost, low ductility and so on

Active Publication Date: 2018-03-13
NORTHEASTERN UNIV LIAONING +1
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is only proposed to control the sulfur content (sulphur element content is required to be less than 0.002wt%) to ensure ductility and avoid crack propagation caused by sulfide inclusions. However, it is difficult and costly to control the sulfur content below 20ppm in industry, so , the problem of low ductility cannot be completely solved by controlling the content of sulfur element

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel materials for hot stamping forming, hot stamping forming process and hot stamping forming components
  • Steel materials for hot stamping forming, hot stamping forming process and hot stamping forming components
  • Steel materials for hot stamping forming, hot stamping forming process and hot stamping forming components

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] The present invention will be described in more detail below with reference to exemplary embodiments. The following examples or experimental data are intended to illustrate the present invention, and it should be clear to those skilled in the art that the present invention is not limited to these examples or experimental data.

[0024] According to one embodiment of the present invention, there is provided a steel for hot stamping, which comprises the following components by weight: 0.27-0.40% C; 0.2-3.0% Mn; 0.11-0.4% V; 0-0.8 % Si; 0-0.5% Al; 0-2% Cr; 0-0.15% Ti; 0-0.15% Nb; 0-0.004% B; the total content of Mo, Ni, Cu less than 2% And other alloying elements that are beneficial to improve its hardenability, as well as other impurity elements.

[0025] The strength of martensite increases with the increase of carbon content, but high carbon content leads to the formation of twin martensite, which reduces the toughness of the material. Twin martensite must be tempered ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a steel material for hot stamping forming with superfine grains, its manufacturing process, hot stamping forming process and hot stamping forming component. The steel includes the following components by weight: 0.27-0.40% C; 0.2-3.0% Mn; 0.11-0.4% V; 0-0.8% Si; 0-0.5% Al; 0-2% Cr 0-0.15% Ti; 0-0.15% Nb; 0-0.004% B; Mo, Ni, Cu and other alloying elements with a total content of less than 2% are beneficial to improving their hardenability, and other impurity elements.

Description

technical field [0001] The invention relates to a steel material for hot stamping forming with superfine grains, a hot stamping forming process and a hot stamping forming component. Background technique [0002] With the urgent needs of global energy saving, emission reduction and environmental protection economy, the automobile industry is developing in the direction of lightweight, but the lightweight of automobiles does not come at the expense of safety. On the contrary, the requirements for the crash safety of automobiles are getting higher and higher. At present, the application of high-strength and ultra-high-strength steels for vehicles in the automotive industry has attracted more and more attention due to their high strength and light weight. Under high strength, the cold stamping method is used, the formability is reduced, the required stamping force is large, and it is easy to crack. In addition, the part has a large springback after forming, and its shape and d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/12C22C38/02C22C38/06C22C38/18C22C38/14C22C38/08C22C38/16C21D8/02B62D25/04B60R19/03B62D25/06B62D21/00
CPCB60R19/03B62D21/00B62D25/04B62D25/06C21D8/0205C22C38/02C22C38/04C22C38/06C22C38/08C22C38/12C22C38/14C22C38/16C22C38/18C22C38/32C21D8/00C21D8/04C22C38/00C22C38/24C22C38/46C21D8/02C23C2/06C23C2/12C22C38/58C21D8/0405C21D8/0421C22C38/26C22C38/28C22C38/38
Inventor 易红亮刘宏亮常智渊吴迪黄建王国栋
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com