A kind of preparation method of flaky cu9fe9s16 nanometer flower

A cu9fe9s16 and nanoflower technology, which is applied in the preparation and application of photothermal conversion materials, can solve the problem of high temperature in pyrolysis, and achieve the effects of easy availability of raw materials, simple operation process and broad application prospects.

Inactive Publication Date: 2018-04-20
DONGHUA UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the temperature of the pyrolysis method used in the synthesis is relatively high, and the obtained product is hydrophobic and needs further hydrophilic modification

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of flaky cu9fe9s16 nanometer flower
  • A kind of preparation method of flaky cu9fe9s16 nanometer flower
  • A kind of preparation method of flaky cu9fe9s16 nanometer flower

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Take 0.67mmol FeCl 3 ·6H 2 O and 0.33 mmol MnCl 2 4H 2 Disperse O in 10mL of diethylene glycol, stir at 80°C, add 0.4mmol trisodium citrate dihydrate, stir for 1h, add 3mmol sodium acetate, after 30min, transfer to a polytetrafluoroethylene reactor, 200°C Under the reaction 6h. Centrifuged and washed 3 times with deionized water to obtain Fe 2 MnO 4 Nanocrystalline. Such as figure 1 Shown is the scanning electron microscope image of the sample, the particle size is 200–400nm. figure 2 is the XRD picture of the sample, with Fe 2 MnO 4 (PDFno.10-0319) standard XRD peak one-to-one correspondence, indicating that the prepared sample is Fe 2 MnO 4 .

[0034] Fe obtained by taking 2.5mg 2 MnO 4 Nanocrystals, dispersed in 10mL water, add 10μL (NH 4 ) 2 S solution (22wt%), ultrasonically dispersed for 5min. Centrifuge, wash with deionized water 3 times, and disperse in 10 mL of water.

[0035] Take 2mL CuCl 2 The dispersion liquid (5.425mmol / L) was added to...

Embodiment 2

[0038] Take 0.67mmol FeCl 3 ·6H 2 O and 0.33 mmol MnCl 2 4H 2 Disperse O in 20mL of diethylene glycol, stir at 80°C, add 0.4mmol trisodium citrate dihydrate, stir for 1h, add 3mmol sodium acetate, after 30min, transfer to a polytetrafluoroethylene reactor, 240°C Under the reaction 6h. Centrifuged and washed 3 times with deionized water to obtain Fe 2 MnO 4 Nanocrystalline.

[0039] Fe obtained by taking 2.5mg 2 MnO 4 Nanocrystals, dispersed in 10mL water, add 10μL (NH 4 ) 2 S solution (22wt%), ultrasonically dispersed for 8min. Centrifuge, wash with deionized water 3 times, and disperse in 10 mL of water.

[0040] Take 2mL CuCl 2 The dispersion liquid (5.425mmol / L) was added to the dispersion liquid obtained above, and ultrasonically dispersed for 8min. Centrifuged and washed 3 times with deionized water to obtain flake Cu 9 Fe 9 S 16 nanoflowers.

Embodiment 3

[0042] Take 0.67mmol FeCl 3 ·6H 2 O and 0.33 mmol MnCl 2 4H 2 Disperse O in 10mL of diethylene glycol, stir at 80°C, add 0.4mmol trisodium citrate dihydrate, stir for 1h, add 3mmol sodium acetate, after 30min, transfer to a polytetrafluoroethylene reactor, 200°C Under the reaction 6h. Centrifuged and washed 3 times with deionized water to obtain Fe 2 MnO 4 Nanocrystalline.

[0043] Fe obtained by taking 2.5mg 2 MnO 4 Nanocrystals, dispersed in 10mL water, add 20μL (NH 4 ) 2 S solution (22wt%), ultrasonically dispersed for 10 minutes. Centrifuge, wash with deionized water 3 times, and disperse in 10 mL of water.

[0044] Take 2mL CuCl 2 The dispersion liquid (5.425mmol / L) was added to the dispersion liquid obtained above, and ultrasonically dispersed for 5min. Centrifuged and washed 3 times with deionized water to obtain flake Cu 9 Fe 9 S 16 nanoflowers.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
concentrationaaaaaaaaaa
sizeaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of flaky Cu9Fe9S16 nanoflowers. The preparation method includes dispersing a ferric salt and a manganese salt into a solvent with stirring, adding trisodium citrate dihydrate with stirring, adding sodium acetate with mixing uniformly, performing solvothermal reaction for 6-8 hours at 180-240 DEG C prior to centrifuging and washing so as to obtain Fe2MnO4 nanocrystalline; dispersing the Fe2MnO4 nanocrystalline into water, adding a (NH4)2S solution, conducting ultrasonic dispersion and centrifugal washing, and dispersing a product into water so as to obtain dispersion liquid; adding a copper salt solution into the dispersion liquid, and conducting ultrasonic dispersion and centrifugal washing so as to obtain the flaky Cu9Fe9S16 nanoflowers. The preparation method has the advantages of simplicity, safety, environment friendliness, low cost and easiness in operation. The flaky Cu9Fe9S16 nanoflowers are capable of effectively converting near-infrared light into heat and have a nuclear magnetic imaging effect, thereby being quite promising in application prospect for photothermal therapy and diagnosis of cancers.

Description

technical field [0001] The invention belongs to the field of preparation and application of photothermal conversion materials, in particular to a flaky Cu 9 Fe 9 S 16 Preparation method of nanoflowers. Background technique [0002] Photothermal ablation therapy, as an emerging method for the treatment of cancer, has received extensive attention in recent years. It is particularly important to choose a suitable light-to-heat conversion material. At present, there are four main categories of light-to-heat conversion materials: metal-based light-to-heat conversion materials, carbon-based light-to-heat conversion materials, organic compound light-to-heat conversion materials, and semiconductor light-to-heat conversion materials. Semiconductor light-to-heat conversion materials have been greatly developed due to their low price, good stability, high light-to-heat conversion efficiency, and adjustable absorption spectrum. [0003] Especially a class of ternary compounds based...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G49/12B82Y40/00A61K41/00A61K49/18A61P35/00
CPCA61K41/0052A61K49/18C01G49/12C01P2002/72C01P2002/84C01P2004/03C01P2004/30C01P2004/62
Inventor 胡俊青黄小娟廖丽军邹儒佳关国强张文龙张剑华彭宇璇徐超霆方竹
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More