Modified thermal-oxidative aging resistant nylon and preparation process thereof

A preparation process and modification technology are applied in the field of modified heat-resistant oxygen aging nylon for automobiles and its preparation process, which can solve the problems of low friction coefficient, achieve good corrosion resistance, improve deformation resistance and aging resistance, Strength-enhancing effect

Inactive Publication Date: 2017-06-23
深圳市华盈新材料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the radiator box of prior art mostly adopts nylon 66, although it has the advantages of high fatigue strength and rigidity, good heat resistance, low coefficient of friction, good wear resistance, etc., but when it is used in auto parts, Its heat resistance, aging resistance, mechanical strength and impact resistance still need to be further improved to prolong the service life of auto parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified thermal-oxidative aging resistant nylon and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0025] Modified heat and oxygen aging-resistant nylon for automobiles, including the following components in parts by weight: 6660 parts of nylon, 30 parts of long glass fiber, 1 part of toughening agent, 3 parts of compatibilizer, 2 parts of main antioxidant, auxiliary antioxidant 1.5 parts of oxygen agent, 0.5 parts of heat stabilizer, and 2 parts of coupling agent.

specific Embodiment 2

[0027] Modified heat and oxygen aging-resistant nylon for automobiles, including the following components in parts by weight: 6654 parts of nylon, 35 parts of long glass fiber, 1 part of toughening agent, 3.5 parts of compatibilizer, 2 parts of main antioxidant, auxiliary antioxidant 1.5 parts of oxygen agent, 0.5 parts of heat stabilizer, and 2.5 parts of coupling agent.

specific Embodiment 3

[0029] Modified heat and oxygen aging-resistant nylon for automobiles, including the following components in parts by weight: 6648 parts of nylon, 40 parts of long glass fiber, 1 part of toughening agent, 4 parts of compatibilizer, 2 parts of main antioxidant, auxiliary antioxidant 1.5 parts of oxygen agent, 0.5 parts of heat stabilizer, and 3 parts of coupling agent.

[0030] Control group:

[0031] The high-strength PA66 composite material includes the following components in parts by weight: 6692 parts of nylon, 2 parts of toughening agent, 3 parts of primary antioxidant, 2 parts of secondary antioxidant, and 1 part of heat stabilizer.

[0032] In above-mentioned each embodiment, the length of long glass fiber is 0.6mm; Nylon 66 viscosity is 2.6; Coupling agent is the aminosilane coupling agent that concentration is 5%; Toughening agent is the vinyl octane of maleic anhydride graft modification ethylene copolymer, styrene-butadiene-styrene triblock copolymer, styrene-ethyl...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention relates to the field of novel plastic materials, in particular to modified thermal-oxidative aging resistant nylon for an automobile and a preparation process thereof. The modified thermal-oxidative aging resistant nylon for the automobile comprises the components in parts by weight: 50-60 parts of nylon 66, 30-40 parts of long glass fiber, 0.5-2 parts of a flexibilizer, 2-5 parts of a compatilizer, 1-3 parts of a main antioxidant, 0.5-1.5 parts of a sub antioxidant, 0.5-2 parts of a heat stabilizer and 1-4 parts of a coupling agent. The modified thermal-oxidative aging resistant nylon for the automobile, provided by the invention, has the advantages of good thermal oxidation resistance, good aging resistance, good impact resistance, long service life and so on.

Description

technical field [0001] The invention relates to the field of new plastic materials, in particular to modified heat and oxygen aging-resistant nylon for automobiles and a preparation process thereof. Background technique [0002] Nylon is a general term for thermoplastic resins containing repeated amide groups on the main chain of the molecule. Its name is determined by the specific number of carbon atoms in the synthetic monomer. It has superior mechanical strength, stiffness, toughness, mechanical shock absorption and wear resistance. , has gradually replaced metal and thermosetting materials and is widely used in auto parts, such as car radiator boxes. [0003] The car radiator is a structure specially used for engine heat dissipation, which is composed of water inlet chamber, water outlet chamber, radiator core, radiator box and other parts. Coolant flows inside the radiator core and air passes outside the radiator. The hot coolant cools by dissipating heat to the air, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L77/06C08L51/06C08L51/00C08L35/06C08K13/06C08K9/02C08K9/06C08K7/14C08K5/544C08K5/524
CPCC08L77/06C08K2201/004C08L2201/08C08L2205/035C08L51/06C08L51/006C08L35/06C08K13/06C08K9/02C08K9/06C08K7/14C08K5/544C08K5/524
Inventor 贺鹏勇贺朋波
Owner 深圳市华盈新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap