Resin plasticization promoter, preparation thereof and method of applying resin plasticization promoter to manufacturing of wood-plastic decoration material

A technology for decorative materials and plasticizers, applied in resin plasticizers and their preparation and application fields, can solve problems such as environmental damage threats, adverse effects on product strength, etc., to improve product quality, solve damage and threats, and plasticize Excellent effect

Active Publication Date: 2017-06-30
黑龙江林海华安新材料股份有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to address the aforementioned problems, provide a PVC resin plasticizer and a preparation method thereof, and simultaneously apply the PVC resin plasticizer to the production of Type 4 and Type 5 PVC resin wood-plastic decorative materials, To replace the plasticizer in the production raw materials, a method for manufacturing PVC resin wood-plastic decorative materials is proposed, which solves the problems of plasticizers in the prior art on human beings, the threat of damage to the environment, and the adverse impact on product strength, etc., and Significantly reduce product cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment 1

[0022] The PVC resin plasticizer is a graft, prepared from the following raw material components according to the weight percentage of each component: high-density oxidized polyethylene wax (OPEW) 30%, initiator (BPO) 1.2% , maleic anhydride (MAH) 14%, ethylene-vinyl acetate (EVA) 9.8%, activated calcium carbonate 45%.

[0023] Described PVC resin plasticizer can be prepared by following method:

[0024] Step 1, according to the raw material components and corresponding proportions of the PVC resin plasticizer, take each raw material component for subsequent use;

[0025] Step 2. Put the raw materials weighed in step 1 into a stirring mixer, and mix them at a temperature of 105-125 °C until they are evenly mixed;

[0026] Step 3. Put the uniformly mixed materials into the extruder, and carry out extrusion and pelletizing operations under the conditions of temperature 80-120°C and rotation speed 30-60 rpm to make graft filler particles.

[0027] The production raw material co...

specific Embodiment 2

[0038] The PVC resin plasticizer was prepared according to the raw material composition and method as described in Example 1.

[0039] The production raw material components of the PVC resin wood-plastic decorative material using the PVC resin plasticizer are as follows in parts by weight: 100 parts of type 4 PVC resin, 30 parts of natural wood powder, 130 parts of calcium carbonate, and 8 parts of stabilizer parts, toughening agent (CPE) 12 parts, foaming agent (AC) 1.2 parts, foaming agent (NC) 1 part, foaming regulator 12 parts, stearic acid 0.9 parts, polyethylene wax 1.1 parts, resin accelerator 1.2 parts of plasticizer and appropriate amount of pigment.

[0040] Apply the manufacturing method of the PVC resin wood-plastic decorative material as described in the first embodiment to manufacture the PVC resin wood-plastic decorative material of this embodiment.

[0041] The manufacturing process of the PVC resin wood-plastic decorative material using the resin plasticizer de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
flexural modulusaaaaaaaaaa
bending strengthaaaaaaaaaa
flexural modulusaaaaaaaaaa
Login to view more

Abstract

A PVC (polyvinyl chloride) resin plasticization promoter is prepared from the following raw materials in percentage by weight: 20-45% of high density oxidized polyethlene wax (OPEW), 0.5-5% of an initiator (BPO), 10-25% of maleic anhydride (MAH), 1-12% of ethylene-vinyl acetate (EVA) and 30-45% of activated calcium carbonate. The PVC resin plasticization promoter is a graft, is nontoxic and harmless, has an excellent PVC resin plastification characteristic, is applied to production of the PVC wood-plastic decoration material, replaces a plasticizer, and can avoid harms and threat caused by the plasticizer to human and an environment in the prior art basically, improve the plastification processability of type 4 and 5 PVC resin and the product quality of the PVC wood-plastic decoration material, and achieve ecologicalization, harmlessness and high strength of a product; at the same time, the production cost of the product can also be lowered greatly.

Description

technical field [0001] The present invention relates to a resin plasticizer and its preparation and application, in particular to a PVC resin plasticizer and its preparation method, and a process of using the PVC resin plasticizer to manufacture PVC resin wood-plastic decorative materials method. Background technique [0002] PVC resin wood-plastic material is a foamed composite material that has both the advantages of wood and plastic. It has high impact resistance and ductility, and has been widely used in the fields of interior decoration and packaging materials. In the current production, PVC resin wood-plastic decoration materials are mostly produced with 7 and 8 types of PVC resin. The melt strength of 7 and 8 types of PVC resin is insufficient, and the viscosity is too low. Bubbles and string bubbles lead to difficulties in material molding and processing, resulting in low product strength, poor toughness, and brittle materials. [0003] Type 4 and Type 5 PVC resins...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F291/06C08F222/06C08L27/06C08L97/02C08L23/28C08L23/06C08L51/06C08K13/02C08K3/26C08K5/09
CPCC08F255/023C08F263/04C08K3/26C08K2003/265C08L27/06C08L2203/14C08L2205/035C08L2205/16C08F222/06C08L51/06C08L97/02C08L23/286C08L23/06C08K13/02C08K5/09
Inventor 宋月成张济民王本永左书彬
Owner 黑龙江林海华安新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap