A method for synchronous desulfurization of molten steel and slag in rh vacuum furnace for non-oriented silicon steel

A technology of oriented silicon steel and vacuum furnace, which is applied in the field of simultaneous desulfurization of molten steel and slag in RH vacuum furnace of non-oriented silicon steel, can solve the problem of a large amount of sulfur returning to molten steel, reduce the cost of steelmaking, increase the desulfurization reaction interface, and reduce T.Fe The effect of content

Active Publication Date: 2019-04-19
INST OF RES OF IRON & STEEL JIANGSU PROVINCE +2
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] 2) During the smelting process of the converter, a large amount of sulfur is brought into by adding steel scrap and slagging materials, coupled with the oxidizing atmosphere in the converter, resulting in a large amount of sulfur returning to the molten steel after smelting

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for synchronous desulfurization of molten steel and slag in rh vacuum furnace for non-oriented silicon steel
  • A method for synchronous desulfurization of molten steel and slag in rh vacuum furnace for non-oriented silicon steel
  • A method for synchronous desulfurization of molten steel and slag in rh vacuum furnace for non-oriented silicon steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] This implementation discloses a technical scheme adopted by a method for synchronous desulfurization of molten steel and slag in a RH vacuum furnace for non-oriented silicon steel:

[0038] (1) The sulfur content of molten iron after deep desulfurization is lower than 0.0015%, and the slag after desulfurization is removed at the same time;

[0039] (2) The converter uses clean raw and auxiliary materials to reduce the resulfurization of molten steel. Clean raw and auxiliary materials mainly include clean scrap steel, lime, light-burned dolomite, pellets, magnesium balls, sludge balls and other high-sulfur content auxiliary materials are strictly prohibited; converter tapping When the temperature is higher than 1650°C, the slag-stopping cone is used to stop the slag during the tapping process, and the slag is strictly controlled, and the low-carbon steel slag surface deoxidizer and lime are added according to the following methods:

[0040] m 1 =(x [O] -0.06%)×10 6 ·η...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for synchronously desulphurizing molten steel and slag of a non-oriented silicon steel RH vacuum oven. The method mainly comprises the following steps: molten steel pretreatment (a KR method), converter smelting and RH vacuum refining, wherein the RH vacuum refining comprises the steps of carrying out vacuumizing and decarbonization on RH entering a station, after the decarbonization of RH is finished, adding a low-carbon steel slag surface deoxidant into the surface of the steel slag, simultaneously carrying out steel ladle bottom blowing to promote the reduction of the low-carbon steel slag surface deoxidant to steel ladle slag, after the low-carbon steel slag surface deoxidant is added, adding metal aluminum, silicon iron and manganese metal into molten steel, carrying out deoxygenation and alloying, carrying out circular processing for 4-7 minutes, adding a desulphurizing agent in different stages, simultaneously adjusting the steel ladle bottom blowing flow to promote slag-metal reaction to realize desulphurization, carrying out desulphurizing molten steel by virtue of the desulphurizing agent and the steel ladle slag so as to improve the desulphurization efficiency, after the desulphurization is finished, carrying out clean circulation for more than 8 minutes, and carrying out vacuum breaking and steel tapping. The sulfur content of an RH end point is less than 30ppm, and the standardized rate is increased from original about 22% to 95% or above.

Description

technical field [0001] This application relates to the technical field of refining and desulfurization of molten steel outside the furnace, in particular to a method for synchronous desulfurization of molten steel and slag in a non-oriented silicon steel RH vacuum furnace. Background technique [0002] The main purpose of cold-rolled non-oriented silicon steel sheet is for the manufacture of generators, so it is also called cold-rolled electrical silicon steel. Its silicon content is 0.5% to 3.0%. After cold rolling, the finished product thickness is mostly 0.35mm and 0.5mm thick steel strip. Due to the relatively low technical barriers of non-oriented silicon steel, there are many production capacities under construction and proposed. The silicon steel market competition is intensifying. At the same time, from the point of view of energy saving, the trend of technological development is to improve the efficiency of electrical equipment. One of the main means is to improve ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/10C21C7/06C21C7/064
CPCC21C7/06C21C7/0645C21C7/10
Inventor 赵家七邹长东刘飞耿涛皇祝平
Owner INST OF RES OF IRON & STEEL JIANGSU PROVINCE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com