A kind of three-dimensional burnt-out double-sided velvet production method and double-sided velvet

A production method and technology of double-faced fleece, applied in the direction of fabric surface trimming, thorn pattern, fiber treatment, etc., can solve problems such as complex process, and achieve the effect of enriching three-dimensional patterns

Active Publication Date: 2019-07-30
SUZHOU FOREVERTEX CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For the burnt-out of double-sided fleece, to form a three-dimensional burn-out effect, usually glue is first applied to the flannelette, and then the fluff is pulled out, and then the fluff on both sides of the double-faced fleece is burnt-out separately, and the process is more complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of three-dimensional burnt-out double-sided velvet production method and double-sided velvet
  • A kind of three-dimensional burnt-out double-sided velvet production method and double-sided velvet
  • A kind of three-dimensional burnt-out double-sided velvet production method and double-sided velvet

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The present embodiment provides a method for producing three-dimensional burnt-out double-sided fleece, comprising the following steps:

[0029] S1: Weaving, use 100% polyester fiber to weave gray cloth, the structure of gray cloth is as follows figure 1 As shown, the gray cloth includes the bottom of the A face and the B face woven with 75D / 36F polyester filament, and the suede that connects the A face and the B face, and the suede is 150D / 288F polyester flat yarn;

[0030] S2: Cut fleece, cut from the middle of gray cloth (such as figure 1 Middle arrow direction), so that the gray cloth forms two single-face flannelettes (composed of the base fabric and the fluff on one side of the base fabric, and the fluff is formed by the cut wool);

[0031] S3: Shearing. Cut the fluff of the single-face flannelette to a uniform height through a shearing machine. Usually, due to the elasticity of the flannelette itself, the height of the fluff after shearing is not uniform. Cut t...

Embodiment 2

[0046] The present embodiment provides a method for producing three-dimensional burnt-out double-sided fleece, comprising the following steps:

[0047] S1: Weaving, use 100% polyester fiber to weave gray cloth, the structure of gray cloth is as follows figure 1 As shown, the gray cloth includes the bottom of the A face and the B face woven with 75D / 36F polyester filament, and the suede that connects the A face and the B face, and the suede is 150D / 288F polyester flat yarn;

[0048] S2: Cut fleece, cut from the middle of gray cloth (such as figure 1 Middle arrow direction), so that the gray cloth forms two single-face flannelettes (composed of the base fabric and the fluff on one side of the base fabric, and the fluff is formed by the cut wool);

[0049] S3: Shearing. Cut the fluff of the single-face flannelette to a uniform height through a shearing machine. Usually, due to the elasticity of the flannelette itself, the height of the fluff after shearing is not uniform. Cut t...

Embodiment 3

[0065] The present embodiment provides a method for producing three-dimensional burnt-out double-sided fleece, comprising the following steps:

[0066] S1: Weaving, use 100% polyester fiber to weave gray cloth, the structure of gray cloth is as follows figure 1 As shown, the gray cloth includes the bottom of the A face and the B face woven with 75D / 36F polyester filament, and the suede that connects the A face and the B face, and the suede is 150D / 288F polyester flat yarn;

[0067] S2: Cut fleece, cut from the middle of gray cloth (such as figure 1 Middle arrow direction), so that the gray cloth forms two single-face flannelettes (composed of the base fabric and the fluff on one side of the base fabric, and the fluff is formed by the cut wool);

[0068] S3: Shearing. Cut the fluff of the single-face flannelette to a uniform height through a shearing machine. Usually, due to the elasticity of the flannelette itself, the height of the fluff after shearing is not uniform. Cut t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production method of stereoscopic burnt-out double-sided plush. The production method comprises steps as follows: burn-out: single-sided plush prepared from 100% polyester is corroded with strong base, so that nap in a specific area is shortened to form patterns; water washing: slurry left during burn-out is washed away; latex coating: the required area of the back side of bottom cloth is coated with white latex, and the white latex is dried; napping: the cloth is coated with a fluffing agent, napping is performed on the reverse side of base cloth with a napping machine, part of nap is napped to the reverse side from the front side, double-sided plush is formed, and the fluffing agent is washed away after napping is finished; carding: carding is performed on the plush, and wool in nap is cleared away; latex washing: white latex is washed away with an organic solvent; lustering: lustering is performed on the plush cloth; sizing of a finished product. According to the production method of the stereoscopic burnt-out double-sided plush, the nap in the coated area cannot be napped to the front side during napping because of latex coating, thus, no nap exists in the area, the latex is just located in the burnt-out area, a no-nap area is added on the basis of burnt-out patterns, and rich and stereoscopic patterns can be formed.

Description

technical field [0001] The invention relates to a production method of three-dimensional burnt-out double-faced fleece and the double-faced fleece, belonging to the technical field of textiles. Background technique [0002] Burnt-out double-sided fleece is a double-sided fleece with double-sided burnt-out patterns. In order to obtain a more attractive fleece effect, it is necessary to form a three-dimensional printing pattern on the fleece, that is, by making some areas on the cloth (usually around the original printing pattern) form a fluff-free region. For the burnt-out of double-faced fleece, to form a three-dimensional burn-out effect, usually glue is first applied on the fleece, and then the fluff is pulled out, and then the fluff on both sides of the double-faced fleece is burnt-out respectively, and the process is relatively complicated. Contents of the invention [0003] The technical problem to be solved in the present invention is: in order to overcome the probl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06C27/00D06C23/04D06C11/00D06B21/00
CPCD06B21/00D06C11/00D06C23/04D06C27/00D06M15/11D06M15/333D06M2101/32D10B2331/04
Inventor 伍允程龚小平
Owner SUZHOU FOREVERTEX CO LTD