A kind of preparation technology of multi-layer structure 3D abrasive tool

A multi-layer structure and preparation technology, which is applied in the direction of grinding/polishing equipment, grinding devices, manufacturing tools, etc., can solve the problems of grinding debris clogging, and achieve the goal of avoiding grinding debris clogging, ensuring continuity and low production cost Effect

Active Publication Date: 2019-11-12
DONGGUAN GOLDEN SUN ABRASIVES
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above-mentioned purpose of the present invention, the purpose of the present invention is to aim at the deficiencies in the prior art, provide a kind of preparation technology of multi-layer structure 3D abrasive tool, the abrasive tool that the preparation process of this multi-layer structure 3D abrasive tool makes has abrasive force The advantages of stability, and can avoid the problem of clogging of abrasive debris

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation technology of multi-layer structure 3D abrasive tool
  • A kind of preparation technology of multi-layer structure 3D abrasive tool
  • A kind of preparation technology of multi-layer structure 3D abrasive tool

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A kind of preparation technology of multi-layer structure 3D grinding tool, it comprises the following steps:

[0036] Step 1. Coating primer on the elastic film: apply a primer layer on the surface of the elastic film, and then initially cure and keep the primer layer with a certain viscosity; in this embodiment, the curing temperature for initial curing is 90°C , the curing time is 22s;

[0037] Step 2. Compression of the frame: place a frame with a height of 0.50mm on the primer layer, and then compress it;

[0038] Step 3. Scratch abrasive: scrape the abrasive into the frame according to the thickness of the frame;

[0039] Step 4. Preliminary curing of the abrasive: Preliminarily solidify the abrasive in step 3 to form an abrasive layer with a thickness of 0.30 mm, and make the abrasive layer in a thick and non-sticky state; in this embodiment, the curing temperature for the preliminary curing is 110°C. The curing time is 4min;

[0040] Step 5, compression moldi...

Embodiment 2

[0050] A kind of preparation technology of multi-layer structure 3D grinding tool, it comprises the following steps:

[0051] Step 1. Coating primer on the elastic film: apply a primer layer on the surface of the elastic film, and then initially cure and keep the primer layer with a certain viscosity; in this embodiment, the curing temperature for initial curing is 80°C , curing time is 30s;

[0052] Step 2. Compression of the frame: place a frame with a height of 0.10mm on the primer layer, and then compress it;

[0053] Step 3. Scratch abrasive: scrape the abrasive into the frame according to the thickness of the frame;

[0054] Step 4. Preliminary curing of the abrasive: Preliminarily solidify the abrasive in step 3 to form an abrasive layer with a thickness of 0.05 mm, and make the abrasive layer thick and not sticky; in this embodiment, the curing temperature for the preliminary curing is 100°C. The curing time is 5 minutes;

[0055] Step 5, compression molding: place ...

Embodiment 3

[0065] A kind of preparation technology of multi-layer structure 3D grinding tool, it comprises the following steps:

[0066] Step 1. Coating primer on the elastic film: apply a primer layer on the surface of the elastic film, and then initially cure and keep the primer layer with a certain viscosity; in this embodiment, the curing temperature for initial curing is 100°C , curing time is 15s;

[0067] Step 2. Compressing the frame: place a frame with a height of 1.0mm on the primer layer, and then compress it;

[0068] Step 3. Scratch abrasive: scrape the abrasive into the frame according to the thickness of the frame;

[0069] Step 4. Preliminary curing of the abrasive: Preliminary curing of the abrasive in step 3 to form an abrasive layer with a thickness of 0.50 mm, and make the abrasive layer in a thick and non-sticky state; in this embodiment, the curing temperature for the preliminary curing is 120°C. The curing time is 3 minutes;

[0070] Step 5, compression molding:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of grinding tools, in particular to a preparation process of a multilayer-structured 3D grinding tool. The preparation process comprises the steps of: (1)coating of a primer on an elastic membrane; (2) pressing of a square frame; (3) scraping of an abrasive; (4) primary curing of the abrasive; (5) stamping; (6) mold shifting and curing; and (7) compounding of a sponge layer. The multilayer-structured 3D grinding tool is prepared by the preparation process of the multilayer-structured 3D grinding tool; an abrasive layer achieves self sharpness; in the grinding process, abrasive grains can fall layer by layer; and new abrasive grains are exposed constantly after falling, so that the grinding force is stable. In addition, in the prepared multilayer-structured 3D grinding tool, a groove is formed in the middle part of the abrasive layer, so that abrasive chips generated in the grinding process can be easily discharged from the groove, and the blockage problem of the abrasive chips can be prevented; and the prepared multilayer-structured 3D grinding tool is particularly suitable for a wet grinding procedure.

Description

technical field [0001] The invention relates to the technical field of abrasive tools, in particular to a preparation process of a multi-layer structure 3D abrasive tool. Background technique [0002] Sponge sand abrasives are widely used in manufacturing, repairing, furniture, decoration and other industries, and have brought great convenience to the above industries, and are still an industrial necessity. [0003] In the prior art, there are mainly two types of sponge sand abrasives. The first one is obtained by mixing adhesives and abrasive grains and then coated. The second is to apply adhesives on the base material before using Electrostatic sand planting is obtained. There is common defect in above-mentioned these two types of existing sponge abrasive tools: (1) because of its grit easily blunt or come off, therefore cause its abrasive force to be unstable; When the tool is used to grind the workpiece, it is easy to cause the problem of grinding debris clogging. Co...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B24D18/00
Inventor 方红杨伟
Owner DONGGUAN GOLDEN SUN ABRASIVES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products