All-cotton high-end stretch garment fabric making method

A technology of elasticity and fabric, applied in dyeing, fabric surface trimming, weaving, etc., can solve the problems of poor elasticity of cotton fabrics, and achieve the effect of not easy to fade, good fastness, and good elasticity

Inactive Publication Date: 2018-01-19
石狮市宏兴染整织造有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Therefore, aiming at the above content, the present invention provides a kind of preparation method of all-cotton high-grade elastic garment fabric, solves the problem of poor elasticity of all-cotton fabric of the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A preparation method of high-grade cotton elastic clothing fabric, comprising the following processing steps:

[0018] (1) Prepare raw materials: 100 parts by weight of cotton elastic fabric, 300 parts by weight of pretreatment auxiliary agent; described cotton elastic fabric comprises the following raw materials in parts by weight: 100 parts of natural cotton fiber, 100 parts of elastic cotton fiber, milk protein 20 parts of fiber, the pretreatment aids include the following raw materials in parts by weight: 20 parts of tea saponin, 10 parts of fluorosilicone resin, 10 parts of ethylene glycol, 30 parts of sodium hydroxide, 50 parts of hydrogen peroxide, 3 parts of glycerin share;

[0019] (2) Pretreatment: Put the above-mentioned cotton elastic fabric into the pretreatment auxiliary agent to react, raise the temperature to 100°C, and keep it warm for 90min; the bath ratio is 1:9.

[0020] (3) Dyeing: take out the cotton elastic fabric pretreated through step (2), and...

Embodiment 2

[0022] A preparation method of high-grade cotton elastic clothing fabric, comprising the following processing steps:

[0023] (1) Raw material preparation: 100 parts by weight of cotton elastic fabric, 600 parts by weight of pretreatment auxiliary agent; the cotton elastic fabric includes the following raw materials in parts by weight: 100 parts of natural cotton fiber, 100 parts of elastic cotton fiber, milk protein 25 parts of fiber, the pretreatment aids include the following raw materials in parts by weight: 25 parts of tea saponin, 13 parts of fluorosilicone resin, 15 parts of ethylene glycol, 35 parts of sodium hydroxide, 55 parts of hydrogen peroxide, 4 parts of glycerin share;

[0024] (2) Pretreatment: Put the above-mentioned cotton elastic fabric into the pretreatment auxiliary agent to react, raise the temperature to 105°C, and keep it warm for 105min; the liquor ratio is 1:9.

[0025] (3) Dyeing: take out the cotton elastic fabric pretreated through step (2), and ...

Embodiment 3

[0027] A preparation method of high-grade cotton elastic clothing fabric, comprising the following processing steps:

[0028] (1) Prepare raw materials: 100 parts by weight of cotton elastic fabric, 1000 parts by weight of pretreatment auxiliary agent; described cotton elastic fabric comprises the following raw materials in parts by weight: 100 parts of natural cotton fiber, 100 parts of elastic cotton fiber, milk protein 30 parts of fiber, the pretreatment aids include the following raw materials in parts by weight: 30 parts of tea saponin, 15 parts of fluorosilicone resin, 20 parts of ethylene glycol, 40 parts of sodium hydroxide, 60 parts of hydrogen peroxide, 5 parts of glycerin share;

[0029] (2) Pretreatment: Put the above-mentioned cotton elastic fabric into the pretreatment auxiliary agent to react, raise the temperature to 110°C, and keep it warm for 120min; the liquor ratio is 1:9.

[0030] (3) Dyeing: take out the cotton elastic fabric pretreated through step (2),...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of fabrics, and provides an all-cotton high-end stretch garment fabric making method. The problem that in the prior art, the all-cotton fabric is poor in elasticityis solved. The method comprises the following processing steps that 1, raw materials are prepared, wherein 100 parts by weight of all-cotton stretch fabric and 300-1,000 parts by weight of a pretreatment auxiliary are adopted, the all-cotton stretch fabric is made from, by weight, 100 parts of natural cotton fiber, 100 parts of stretch cotton fiber and 20-30 parts of milk protein fiber, and the pretreatment auxiliary is prepared from, by weight, 20-30 parts of tea saponin, 10-15 parts of fluorosilicon resin, 10-20 parts of ethylene glycol, 30-40 parts of sodium hydroxide, 50-60 parts of hydrogen peroxide and 3-5 parts of glycerin; 2, pretreatment is conducted, wherein the all-cotton stretch fabric is put into the pretreatment auxiliary for a reaction, the temperature rises to 100-110 DEG C, and heat preservation is conducted for 90-120 min; 3, dyeing is conducted.

Description

technical field [0001] The invention relates to the field of fabrics, in particular to a method for preparing high-grade all-cotton elastic clothing fabrics. Background technique [0002] There are many kinds of textile fibers, which are usually divided into two categories: natural fibers and chemical fibers. Cotton is a kind of bulk natural cellulose fiber, and it is the only product among the main agricultural products such as grain, cotton, oil and vegetables that can meet the needs of human beings for wearing and using. Compared with chemical fibers, the fabric made of cotton fibers has good softness and comfort, strong moisture absorption and air permeability, good warmth retention, and there is no adverse reaction such as static electricity, and it is green and healthy, and will not cause adverse reactions on human skin. Spandex is a functional fiber with high elasticity and recovery. As long as a small amount of spandex yarn is added to the fabric, the elasticity and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D03D15/00D03D15/08D04B1/14D04B1/18D04B21/00D06C7/02D06M15/657D06M13/148D06P1/38D06P1/653D06P3/854D06P5/08D06P5/10D06M101/06D03D15/56
Inventor 许志伟陈翠云陈夏渊刘艺云蔡建才苏立才
Owner 石狮市宏兴染整织造有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap