Anti-ultraviolet microcapsule finishing agent and preparation method thereof
A microcapsule finishing, anti-ultraviolet technology, applied in fiber processing, textile and papermaking, light-resistant fibers, etc., can solve the problems of limited application range and unstable performance of coating agents, and achieve stable anti-ultraviolet, obvious effect, obvious effect. UV protection effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] An anti-ultraviolet microcapsule finishing agent, the finishing agent is spherical or ellipsoidal, with an average particle diameter of 6 μm, and the mass ratio of its core material to wall material is 1:0.3; the core material is composed of graphene and titanium dioxide, The wall material is composed of sericin and hyaluronic acid.
[0021] The core material is composed of graphene and titanium dioxide in a mass ratio of 1:1.
[0022] The wall material is composed of sericin and hyaluronic acid at a ratio of 1:1.
[0023] A preparation method of an anti-ultraviolet microcapsule finishing agent, comprising the following steps:
[0024] (1) dissolving sericin in deionized water to prepare a sericin solution with a mass concentration of 3%;
[0025] (2) Dissolving hyaluronic acid in water to prepare a hyaluronic acid solution with a mass concentration of 0.5%, then adding emulsifier, graphene and titanium dioxide powder, magnetically stirring until uniformly dispersed t...
Embodiment 2
[0032] An anti-ultraviolet microcapsule finishing agent, the finishing agent is spherical or ellipsoidal, with an average particle diameter of 9 μm, and the mass ratio of its core material and wall material is 1:1; the core material is composed of graphene and titanium dioxide, The wall material is composed of sericin and hyaluronic acid.
[0033] The core material is composed of graphene and titanium dioxide in a mass ratio of 1:2.
[0034] The wall material is composed of sericin and hyaluronic acid at a ratio of 2.5:1.
[0035] A preparation method of an anti-ultraviolet microcapsule finishing agent, comprising the following steps:
[0036] (1) dissolving sericin in deionized water to prepare a sericin solution with a mass concentration of 6%;
[0037] (2) Dissolving hyaluronic acid in water to prepare a hyaluronic acid solution with a mass concentration of 1.5%, then adding emulsifier, graphene and titanium dioxide powder, magnetically stirring until uniformly dispersed ...
Embodiment 3
[0044] An anti-ultraviolet microcapsule finishing agent, the finishing agent is spherical or ellipsoid, the average particle diameter is 12 μm, and the mass ratio of its core material and wall material is 1:1.5; the core material is composed of graphene and titanium dioxide, The wall material is composed of sericin and hyaluronic acid.
[0045] The core material is composed of graphene and titanium dioxide in a mass ratio of 1:3.5.
[0046] The wall material is composed of sericin and hyaluronic acid at a ratio of 4:1.
[0047] A preparation method of an anti-ultraviolet microcapsule finishing agent, comprising the following steps:
[0048] (1) dissolving sericin in deionized water to prepare a sericin solution with a mass concentration of 10%;
[0049] (2) Dissolving hyaluronic acid in water to prepare a hyaluronic acid solution with a mass concentration of 2%, then adding emulsifier, graphene and titanium dioxide powder, magnetically stirring until uniformly dispersed to o...
PUM
Property | Measurement | Unit |
---|---|---|
The average particle size | aaaaa | aaaaa |
The average particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap