A kind of preparation method of candy glaze made from raw material glaze and candy glaze ceramic tile
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A raw material and candy technology, applied in the field of preparation of candy glaze and candy glaze ceramic tiles, can solve the problem of high cost and achieve the effect of cost reduction
Active Publication Date: 2021-03-30
广东永航新材料实业股份有限公司
View PDF2 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] But the candy glaze that uses in the existing candy glaze ceramic tile all adopts above-mentioned candy dry granule to prepare, and this mode has following defect: the market price of candy dry granule is about 5000 yuan / ton, and the cost is too high
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
preparation example Construction
[0029] The preparation method of the candy glaze ceramic tile comprises:
[0030] The step of preparing the embryo body: ball milling, pressing, and firing the embryo body raw material of the formula to form an embryo body; the embryo body raw material is composed of the following components by weight: 6-8 parts of medium white sodium sand, water mill 6-10 parts of potassium sand, 12-17 parts of medium temperature white sand, 6-8 parts of washed mud, 2.5-4 parts of Guangxi sodium stone, 8-12 parts of high potassium sand, 4.5-6 parts of medium temperature sand, 5-8 parts of bentonite, 10-14 parts of Huaiji sand, 14-18 parts of Yangshan stone powder, 2-4 parts of talc mud, 12-15 parts of mixed mud, 4-7 parts of high alumina stone powder. The time of the ball milling is 8-12h; the pressing condition is to use a pressure of 28000-30000N for pressing, and the pressing frequency is 4.6 times / min; the firing conditions are as follows: under the condition of 1175°C-1180°C, Firing for...
Embodiment 1-5
[0037] Example 1-5 candy glaze
[0038] Weigh the raw materials according to the ratio in Table 1 respectively, see Table 1 for details:
[0039] Table 1: Raw material ratio table of embodiment 1-5
[0040]
[0041]
Embodiment 6-10
[0042] Example 6-10 Candy Glazed Porcelain Tiles
[0043] The preparation method of the candy glaze ceramic tile of embodiment 6-10, comprises:
[0044] The step of preparing the embryo body: ball milling, pressing, and firing the embryo body raw material of the formulated amount to form an embryo body; the embryo body raw material is composed of the following components in parts by weight: 7 parts of medium white sodium sand, water milled potassium sand 8 parts, 15 parts of medium temperature white sand, 7 parts of washed mud, 3 parts of Guangxi sodium stone, 10 parts of high potassium sand, 5 parts of medium temperature sand, 7 parts of bentonite, 12 parts of Huaiji sand, 16 parts of Yangshan stone powder, 3 parts of talc mud , 14 parts of mixed mud, 6 parts of high alumina stone powder. The time for the ball milling is 10 hours; the pressing condition is to press with a pressure of 28000-30000N, and the pressing frequency is 4.6 times / min; the firing conditions are as foll...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Login to View More
Abstract
The invention discloses granulated sugar-type glaze prepared from raw glaze and a preparation method of a granulated sugar-type glazed brick. The granulated sugar-type glaze is prepared from 30-40 parts by weight of potassium feldspar, 50-70 parts by weight of quartz, 10-15 parts of barium carbonate, 5-10 parts of wollastonite, 3-8 parts of aluminum powder, 7-10 parts of Qidao clay, 1-5 parts of zinc oxide, 70-100 parts of printing paste and 30-50 parts of water. The preparation method comprises preparing printing decorative pattern glaze directly from raw glaze powder, carrying out printing with the printing decorative pattern glaze through small spot-type net pattern printing and sintering the blank so that the granulated sugar-type granular sensation decorative effect is obtained. The granulated sugar-type glaze can completely replace the expensive dry candy particles in the prior art and has a cost reduced by 2 / 3 compared with that of the prior art using candy dry granules.
Description
technical field [0001] The invention relates to a building ceramic technology, in particular to a candy glaze prepared from raw material glaze and a preparation method of the candy glaze ceramic brick. Background technique [0002] Candy glaze is a special decorative material that has recently emerged in the ceramic industry. It has a fine particle texture like sugar and is a transparent dry granule that has been fired at a high temperature of about 1080-1200 ℃ after a special glaze process. The sugar-like fine particles are evenly distributed on the brick surface. Under the action of the light, it is shining, and it feels delicate to the touch, like rolling fine sand, with a natural sandstone texture, thereby achieving a special decorative effect. [0003] However, the candy glaze used in the existing candy glaze ceramic tiles is prepared by using the above-mentioned dry candy granules. This method has the following defects: the market price of the dry candy granules is abo...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More 
Login to View More