Aluminum alloy material, preparation method and application of aluminum alloy material in solar energy photovoltaic support

An aluminum alloy material and solar photovoltaic technology, applied in the field of chemical materials, can solve problems such as poor corrosion resistance and tensile strength, achieve good corrosion resistance, increase recrystallization temperature, large market value and economic prospects

Inactive Publication Date: 2018-06-15
柏涛涛
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] An object of the present invention is to provide a corrosion-resistant, light-weight and high-strength aluminum alloy material for the technical problems of poor corrosion resistance and tensile strength of the aluminum alloy material existing in the background art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] 1. Preparation of aluminum alloy materials

[0030] Taking 10kg as an example, according to the mass ratio of Al-0.2Si-0.08Cu-0.6Mg-0.15Zr-0.15Ti-0.01Mn as an example, calculate the mass of the master alloy and prepare the material.

[0031] 1) Si powder is used as the raw material of Si element in the alloy, Al-Cu intermediate alloy is used as the raw material of Cu element in the alloy, Al-Mg intermediate alloy is used as the raw material of Mg element in the alloy, and Al-Zr intermediate alloy is used As the raw material of the Zr element in the alloy, the Al-Ti master alloy is used as the raw material of the Ti element in the alloy, the Al-Mn master alloy is used as the raw material of the Mn element in the alloy, and the aluminum ingot is used as the raw material of the Al element in the alloy. ;

[0032] 2) After the surface of the aluminum ingot is cleaned, it is heated and smelted, and the temperature of the molten aluminum is controlled at 690°C; the Al-Cu mas...

Embodiment 2

[0040] 1. Preparation of aluminum alloy materials

[0041] Taking 10kg as an example, according to the mass ratio of Al-0.4Si-0.2Cu-0.8Mg-0.25Zr-0.25Ti-0.15Mn as an example, calculate the mass of the master alloy and prepare the material.

[0042]1) Si powder is used as the raw material of Si element in the alloy, Al-Cu intermediate alloy is used as the raw material of Cu element in the alloy, Al-Mg intermediate alloy is used as the raw material of Mg element in the alloy, and Al-Zr intermediate alloy is used As the raw material of the Zr element in the alloy, the Al-Ti master alloy is used as the raw material of the Ti element in the alloy, the Al-Mn master alloy is used as the raw material of the Mn element in the alloy, and the aluminum ingot is used as the raw material of the Al element in the alloy. ;

[0043] 2) After the surface of the aluminum ingot is cleaned, it is heated and smelted, and the temperature of the molten aluminum is controlled at 690°C; the Al-Cu maste...

Embodiment 3

[0051] 1. Preparation of aluminum alloy mandrel

[0052] Taking 10kg as an example, according to the mass ratio of Al-0.3Si-0.1Cu-0.7Mg-0.15Zr-0.2Ti-0.1Mn as an example, calculate the mass of the master alloy and prepare the material.

[0053] 1) Si powder is used as the raw material of Si element in the alloy, Al-Cu intermediate alloy is used as the raw material of Cu element in the alloy, Al-Mg intermediate alloy is used as the raw material of Mg element in the alloy, and Al-Zr intermediate alloy is used As the raw material of the Zr element in the alloy, the Al-Ti master alloy is used as the raw material of the Ti element in the alloy, the Al-Mn master alloy is used as the raw material of the Mn element in the alloy, and the aluminum ingot is used as the raw material of the Al element in the alloy. ;

[0054] 2) After the surface of the aluminum ingot is cleaned, it is heated and smelted, and the temperature of the molten aluminum is controlled at 690°C; the Al-Cu master a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention belongs to the field of chemical materials and particularly relates to an aluminum alloy material, a preparation method and application of the aluminum alloy material in a solar energy photovoltaic support. The aluminum alloy material is composed of the following components of, by mass, 0.2%-0.4% of Si, 0.08%-0.20% of Cu, 0.6%-0.8% of Mg, 0.15%-0.25% of Zr, 0.15%-0.25% of Ti, 0.01%-0.15% of Mn and the balance aluminum and inevitable impurities. According to the designed aluminum alloy material, by adding metal elements of Si, Cu, Mg, Zr, Ti, Mn and the like, the grain refinementdegree is improved by a large margin, and the effect in the aspect of promoting the comprehensive properties such as tensile strength, the elongation and the corrosion-resistant property of the aluminum alloy material is significant. The aluminum alloy material is used for preparing a solar energy photovoltaic support profile, so that the corrosion-resistant property of the photovoltaic support prepared from the aluminum alloy material is better than that of a traditional aluminum alloy photovoltaic support component.

Description

technical field [0001] The invention belongs to the field of chemical materials, and in particular relates to an aluminum alloy material, a preparation method and an application in a solar photovoltaic support. Background technique [0002] The lively chemical properties of aluminum alloy make it prone to various forms of corrosion during use, such as pitting corrosion, crevice corrosion, intergranular corrosion, stress corrosion, etc. Anodic oxidation of aluminum can improve the corrosion resistance of aluminum alloy. At present, solar photovoltaic frames and bracket systems are generally made of 6063 aluminum profiles, which have the characteristics of light weight, medium strength, easy processing and forming, and easy anodic oxidation surface treatment. [0003] In recent years, the competition in the solar photovoltaic industry has further intensified. In order to shorten the investment payback period of solar power plants, prolong the service life of solar power plant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/08C22C1/03C22C1/06H02S20/00
CPCC22C1/026C22C1/03C22C1/06C22C21/08H02S20/00Y02E10/50
Inventor 柏涛涛
Owner 柏涛涛
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap