Zn-Li-Mn-based zinc alloy and preparation method and application thereof

A zn-li-mn, zinc alloy technology, used in medical science, prosthesis, etc., can solve the problems of loss of mechanical integrity of implants, toxic and side effects of degradation products, etc., and achieve excellent mechanical properties, excellent performance, and simplified components. Effect

Active Publication Date: 2018-07-24
PEKING UNIV
View PDF5 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In view of the fact that iron-based alloys degrade too slowly in the human body, and the degradation products will have certain toxic and side effects on the human body, the research focus of medical degradable metals in recent years is mainly on medical degradable magnesium alloys, such as AZ31, WE43, Mn- Ca et al. Although magnesium alloys have attractive application prospects as biomaterials, studies have found that magnesium alloys corrode too quickly, and the implant will soon lose its mechanical integrity before the tissues and organs are fully healed. It is necessary to develop new degradable alloys to meet clinical needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Zn-Li-Mn-based zinc alloy and preparation method and application thereof
  • Zn-Li-Mn-based zinc alloy and preparation method and application thereof
  • Zn-Li-Mn-based zinc alloy and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0068] Embodiment 1, preparation as-cast Zn-Li-Mn series zinc alloy

[0069] Using pure zinc (99.99wt.%), zinc-lithium intermetallic compound, zinc-manganese intermetallic compound as raw materials, according to the mass ratio in the following table:

[0070] Zn

[0071] mixed, in CO 2 +SF 6 Under the protection of the atmosphere, smelt at 600 ° C, stir evenly, and after standing, pouring and cooling, the Zn-Li-Mn series zinc alloy (such as figure 1 shown).

Embodiment 2

[0072] Embodiment 2, preparation extruded state Zn-Li-Mn series zinc alloy

[0073] First, according to the steps in Example 1 of the present invention, the as-cast Zn-Li-Mn alloy ingot is prepared, and the Zn-Li-Mn alloy rod is prepared by extrusion (such as figure 2 shown), using radial extrusion, ingot heat preservation for 2h, heat preservation temperature 260°C or 220°C, extrusion temperature 260°C or 220°C, extrusion ratio 36 or 16, extrusion speed 1mm / s to prepare the diameter It is a 10mm Zn-Li-Mn alloy rod.

Embodiment 3

[0074] Embodiment 3, preparation rolling state Zn-Li-Mn series zinc alloy

[0075] First, the as-cast Zn-Li-Mn zinc alloy ingot is prepared according to the steps in Example 1, and the Zn-Li-Mn zinc alloy plate is prepared by rolling (such as image 3 shown), using unidirectional rolling, followed by hot rolling and finish rolling. Before rolling, keep warm at the rolling temperature for 15 minutes. Carry out down-rolling, down-rolling 0.5mm in each pass, the amount of reduction in each pass is 2%, and the final thickness of the plate is 2mm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a Zn-Li-Mn-based zinc alloy and a preparation method and application thereof. The Zn-Li-Mn-based zinc alloy comprises, by mass, greater than 0 and less than or equal to 1% of Li, greater than 0 and less than or equal to 1% of Mn and the balance of Zn. The Zn-Li-Mn-based zinc alloy has excellent mechanical properties, can provide long-term effective support in the human body, has excellent cell compatibility and blood compatibility and can be used for preparation of biomedical implants.

Description

technical field [0001] The invention relates to a Zn-Li-Mn series zinc alloy and its preparation method and application, belonging to the technical field of medical metal material preparation. Background technique [0002] Once a medical device made of biomaterials is implanted in the body, it will interact with the body to promote the diagnosis and treatment of the organism, or complete the repair and replacement of damaged tissues or organs in the body. Obviously, during the interaction with the living body, some devices are suitable for long-term existence in the body, and long-term service to promote curative effect, but some devices are not suitable for long-term existence, only need temporary or short-term effect, with the repair or regeneration of tissues or organs , these devices are gradually degraded and absorbed. In the same way, biological materials can be roughly divided into permanent biological materials and degradable biological materials according to their ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C18/00C22C1/02A61L27/04A61L27/58
CPCA61L27/047A61L27/58C22C1/02C22C18/00
Inventor 郑玉峰杨宏韬张泽川
Owner PEKING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap