High-performance stainless steel surfacing nickel-based special welding wire and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A stainless steel, high-performance technology, applied in welding equipment, welding medium, manufacturing tools, etc., can solve problems such as reverse osmosis, excessive iron content in welding surface materials, etc., to reduce the tendency of cold cracks, improve intergranular corrosion resistance, The effect of good plasticity and toughness
Inactive Publication Date: 2018-08-17
DANYANG HUALONG SUPERIOR STEEL
View PDF18 Cites 14 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
In addition, because the iron of carbon steel is prone to reverse osmosis during the surfacing process, the iron content of the welding surface material component exceeds the standard
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0029] The present invention is described in further detail now in conjunction with embodiment.
[0030] The mass percentages of the constituent chemical elements in the welding wires of each of Examples 1-5 and Comparative Examples 1-4 (compared with Example 1) of the present invention are shown in Table 1:
[0031] Table 1
[0032]
[0033] The preparation method of a kind of high-performance stainless steel surfacing welding nickel-based special welding wire of embodiment 1-5 and comparative example 1-4 specifically comprises the following steps:
[0034] (1) According to the designed welding wire ingredients, use a vacuum electric furnace to smelt at a temperature of 1210-1250 ° C, keep warm for 1-1.5 hours, decarburize, dephosphorize and remove harmful impurities to the molten steel, so that C < 0.1%, tap the steel The temperature T ≥ 1250°C, the composition of the designed welding wire is shown in Table 1;
[0035] (2) Use VOD to carry out refining outside the furna...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
diameter
aaaaa
aaaaa
Login to view more
Abstract
The invention belongs to the field of welding materials and particularly relates to a high-performance stainless steel surfacing nickel-based special welding wire and a preparation method thereof. Thewelding wire comprises chemical elements including, by mass, not greater than 0.04% of C, 0.1-0.5% of Mn, not greater than 0.001% of P, not greater than 0.001% of S, 0.05-0.1% of Si, 20-25% of Cr, 8-12% of Mo, 2-6% of Nb, 0.2-0.5% of Ti, not greater than 0.001% of Cu, 0.1-0.3% of Al, not greater than 1% of Fe, 0.03-0.08% of Co, 0.05-0.1% of the rare earth element RE, 30-80 ppm of N and the balance Ni and inevitable impurity elements. The preparation method comprises the steps of (1) vacuum electric-furnace smelting; (2) VOD external refining; (3) horizontal continuous casting; (4) tandem rolling; and (5) tandem drawing. The welding wire provided by the invention has the good properties of active gas resistance and reducing acid medium corrosion resistance, the electric arc stability and slag stripping performance are excellent during welding, and welding metal with high strength, good tenacity, flaw resistance, high temperature cracking resistance and corrosion resistance is obtained;and the preparation technology is simple, the raw material and manufacturing cost is low, environmental friendliness is achieved, no pollution is generated, and the welding wire and the preparation method are suitable for industrial volume production and remarkable in economic benefit.
Description
technical field [0001] The invention belongs to the field of welding materials, and in particular relates to a high-performance stainless steel surfacing welding nickel-based special welding wire and a preparation method thereof. Background technique [0002] Nickel-based alloy welding wire has good properties of resistance to active gas, caustic medium and reducing acid medium corrosion, and has the characteristics of high strength, good plasticity, cold and hot deformation, processing and welding, so it is widely used in In petrochemical, metallurgy, atomic energy, marine development, aviation, aerospace and other industries, it is a very important corrosion-resistant metal material to solve engineering corrosion problems that cannot be solved by general stainless steel and other metals and non-metallic materials. Nickel-based alloys refer to alloys that are based on nickel and contain alloying elements, and are corrosion-resistant in some media. [0003] Welding material...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.