A kind of graphene characteristic tile glue

A tile adhesive and graphene technology, applied in the field of building materials, can solve the problems of unreachable product quality, unqualified heat-resistant adhesive strength, etc., and achieve the effect of good tensile adhesive strength

Active Publication Date: 2021-07-06
XIAMEN LIKASAM WATERPROOF ENG
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Although there are many tile adhesive products on the market at present, there are a considerable number of products whose quality does not meet the requirements of the tile adhesive industry standard JC / T547-2005 "Ceramic Wall and Floor Tile Adhesives". The heat-resistant adhesive strength of the product is unqualified

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene characteristic tile glue
  • A kind of graphene characteristic tile glue
  • A kind of graphene characteristic tile glue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] The graphene characteristic tile adhesive of the present embodiment, it is powder, and this powder is made up of following components and parts by weight:

[0021]

[0022] When in use, the powder is mixed with water in a weight ratio of 1:0.3 for immediate use.

Embodiment 2

[0024] The graphene characteristic tile adhesive of the present embodiment, it is powder, and this powder is made up of following components and parts by weight:

[0025]

[0026] When in use, the powder is mixed with water in a weight ratio of 1:0.3 for immediate use.

Embodiment 3

[0028] The graphene characteristic tile adhesive of the present embodiment, it is powder, and this powder is made up of following components and parts by weight:

[0029]

[0030] When in use, the powder is mixed with water in a weight ratio of 1:0.3 for immediate use.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a tile adhesive with graphene characteristics, which is a powder, and the powder is composed of the following components and parts by weight: 42-65 parts of cement, 38-60 parts of washed river sand, and 8-15 parts of single-layer graphene 3-9 parts of efflorescence inhibitor, 2-9 parts of cellulose ether, 7-12 parts of rubber powder, 1-5 parts of filler; when in use, the powder and water are mixed in a weight ratio of 1:0.3 and ready to use . The invention has better tensile adhesive strength than the existing tile adhesives.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a tile adhesive with graphene characteristics. Background technique [0002] Tile glue can be used to paste ordinary ceramic tiles, ceramic tiles, glazed tiles, glass mosaics, ceramic mosaics, floor tiles, marble, granite, gypsum board and other wall decoration materials. [0003] Although there are many tile adhesive products on the market at present, there are a considerable number of products whose quality does not meet the requirements of the tile adhesive industry standard JC / T547-2005 "Ceramic Wall and Floor Tile Adhesives". The heat-resistant adhesive strength of the product is unqualified. [0004] Chinese patent document CN104402367B discloses a non-efflorescent high-strength tile adhesive, its composition and weight percentage are as follows: high alumina cement 23-30%, fly ash 42-50%, blast furnace slag 12-16%, double fly powder 6-10% %, redisp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/06C04B111/20
CPCC04B28/06C04B2111/00646C04B2111/2023C04B14/06C04B14/024C04B24/383C04B2103/603
Inventor 刘力嘉
Owner XIAMEN LIKASAM WATERPROOF ENG