Anion far-infrared inorganic artificial stone plate and preparation method thereof

A negative ion far-infrared and artificial stone technology, applied in the field of boards, can solve the problems of unsatisfactory surface decoration, high cost, and large investment in equipment, and achieve the effects of improving body immunity, improving heart function, and reducing radiation

Inactive Publication Date: 2018-11-23
东莞环球经典新型材料有限公司
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, artificial boards and paints contain a large amount of volatile and long-lasting toxic and harmful substances, such as formaldehyde, benzene, toluene, xylene, VOCs, etc.
It will cause great harm to the health of builders and users. Currently, the use of solvent-based coatings is prohibited in the fields of decoration and furniture production.
[0004] The whole industry is developing finishing materials that can replace paints. Water-based paints (water-based resin coatings) have entered the field of furniture production in recent years, but due to problems such as high cost, large equipment investment, high construction difficulty, and unsatisfactory surface decoration effects, etc. lead to promotion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anion far-infrared inorganic artificial stone plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] An anion far-infrared inorganic artificial stone plate, which is composed of the following components in parts by weight: 14 parts of Portland cement, 7 parts of calcined kaolin, 70 parts of calcium carbonate sand, 5 parts of stone powder, 15 parts of water, and 6 parts of water reducer 2 parts, 2 parts of negative ion mineral powder, 6 parts of magnesium oxide pigment.

[0023] During specific preparation, first place calcined kaolin, Portland cement, stone powder, calcium carbonate sand, negative ion mineral powder, and magnesium oxide pigment in the mixing tank for the first stirring, and the first stirring is at a speed of 300 rpm Stir for 5 minutes, stirring well.

[0024] Then add water and water reducer to the mixing tank, and then carry out the second stirring, and the second stirring is stirred at a speed of 1000 rpm for 7 minutes to obtain a well-stirred mixture.

[0025] Put the mixed material in the mold, use a press, press and shape, and shape the correspo...

Embodiment 2

[0029] An anion far-infrared inorganic artificial stone plate, the stone plate is composed of the following components in parts by weight: 20 parts of Portland cement, 5 parts of calcined kaolin, 60 parts of quartz sand, 3 parts of stone powder, and 10 parts of water , 4 parts of water reducer, 1 part of negative ion mineral powder, 3 parts of magnesium oxide pigment.

[0030] During the specific preparation, first put calcined kaolin, Portland cement, stone powder, quartz sand, anion mineral powder, and magnesium oxide pigment in the mixing tank for the first stirring, and the first stirring is at a speed of 500 rpm 4 minutes, stirring well.

[0031] Then add water and water reducer to the mixing tank, and then carry out the second stirring. The second stirring is stirred at a speed of 1500 rpm for 5 minutes to obtain a well-stirred mixture.

[0032] Put the mixed material in the mold, use a press, press and shape, and shape the corresponding stone plate, and shape it into d...

Embodiment 3

[0036] An anion far-infrared inorganic artificial stone plate, the stone plate is composed of the following components in parts by weight: 25 parts of composite portland cement, 1 part of calcined kaolin, 50 parts of quartz sand, 1 part of stone powder, 6 parts of water 2 parts, 2 parts of superplasticizer, 2 parts of negative ion mineral powder, 0.1 part of magnesium oxide pigment.

[0037] During specific preparation, first put calcined kaolin, composite Portland cement, stone powder, quartz sand, negative ion mineral powder, and magnesium oxide pigment in the mixing tank for the first stirring, and the first stirring is at a speed of 1000 rpm Stir for 2 minutes, stirring well.

[0038] Then add water and water reducing agent into the stirring tank, and then carry out the second stirring. The second stirring is stirred at a speed of 2000 rpm for 3 minutes to obtain a uniformly stirred mixture.

[0039] The mixture is placed in a mold and pressed into shape using a press.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an anion far-infrared inorganic artificial stone plate and a preparation method thereof. The artificial stone plate is prepared from the following components in parts by weight: 14-25 parts of cement, 1-7 parts of calcined kaolin, 50-70 parts of sand, 1-5 parts of stone powder, 6-15 parts of water, 2-6 parts of a water reducing agent, 1-2 parts of anion mineral powder and 0.1-6 parts of magnesium oxide pigment. The anion far-infrared inorganic artificial stone plate is capable of releasing anions, purifying air, removing odor, eliminating formaldehyde and reducing radiation, so that the functions of the stone plate are enriched.

Description

technical field [0001] The invention belongs to the field of plates, in particular to an anion far-infrared inorganic artificial stone plate and a preparation method thereof. Background technique [0002] Due to the deteriorating environment and the country's emphasis on environmental protection, especially in recent years, the increase in the control of air pollution, the emission of organic volatiles in the production process of wood-based panels and furniture has been included in the scope of key control. [0003] The surface decoration materials of wood-based panels for furniture and decoration include melamine-impregnated film paper, PVC, fireproof board, water-based paint and solvent-based paint (commonly known as paint), among which solvent-based paint and melamine-impregnated film paper are the most widely used. wide. Solvent-based coatings have been widely used in furniture manufacturing and decoration engineering for the past 50 years because of their full coating...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/54
CPCC04B28/04C04B2111/00017C04B2111/00025C04B2111/542C04B14/106C04B14/06C04B14/02C04B14/304C04B14/36C04B2103/302C04B14/28
Inventor 谭淑仪郭栋郗毅戎延团吴勇杰
Owner 东莞环球经典新型材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com