Water-based anticorrosion coating composition

A composition, water-based coating technology, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems of increasing the complexity and duration of the formation process of anti-corrosion coatings

Active Publication Date: 2021-03-09
SOLVAY SA
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] Indeed, multi-step coating increases the complexity and duration of the corrosion resistant coating formation process on such large parts

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water-based anticorrosion coating composition
  • Water-based anticorrosion coating composition
  • Water-based anticorrosion coating composition

Examples

Experimental program
Comparison scheme
Effect test

example 3

[0118] Use water (17.25 parts by weight), defoamer 035 (0.2 parts by weight), dispersant 151 (0.51 parts by weight), and A mixture of PE F87 surfactant (2.03 parts by weight) and AMP 95 neutralizer (0.51 parts by weight) was used as the liquid base. Will 10M0 (20.05 parts by weight), K-white 450H (5.07 parts by weight) and 130M (1.52 parts by weight) is dispersed therein and then supplemented with 52.76 parts by weight of P580 Latex.

[0119] Viscosity was adjusted by adding rheology modifier Rheolate 255 (0.1 parts by weight).

[0120] The PVC of this formulation is 30% vol, with a density of 1.39 g / l and a solids content of 60% wt.

[0121] The viscosity of this formulation was 3000 cP, its pH was 6.89, and its CCT was found to exceed 500 μm.

[0122] This example shows that a copolymer (VDC) latex which is very stable to dehydrochlorination and thus contains free chlorine in an amount less than 1000 ppm and which does not crystallize under coalescence / heating c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The present invention relates to an aqueous coating composition comprising: - an aqueous latex of a copolymer [copolymer (A)] consisting essentially of repeating units derived from: (i) vinylidene chloride (VDC), (ii) vinyl chloride (VC), (iii) one or more than one alkyl (meth)acrylates [monomer (MA)] having from 1 to 12 carbon atoms in the alkyl group and (iv ) one or more than one aliphatic α-β-unsaturated carboxylic acid [monomer (AA)], relative to the total weight of the copolymer, the proportion of recurring units derived from monomer (AA) is at least 1.0 % by weight, wherein: (A) said copolymer (A) is stabilized to dehydrochlorination in such a way that after heat treatment at about 120° C. for 2 hours, relative to the total weight of the copolymer (A), the The total chloride content of the solid residue of the aqueous latex is less than 1000 ppm; (B) said copolymer (A) does not undergo any significant crystallization when heated in such a way that (j) it The ratio of the crystallinity index (CI) after a heat treatment of 48 hours of heating to (jj) its crystallinity index before such heat treatment (CI 热处理之后 / CI 热处理之前 ) is less than 1.15; and - at least one anticorrosion pigment [pigment (P)] comprising an aluminum salt of (poly)phosphoric acid modified with an alkaline earth metal oxide; - at least one nonionic surfactant [surfactant (NS)]; and - at least one inorganic filler different from the pigment (P) [filler (I)] in an amount such that when measured relative to the dry coating composition, comprises from 20% vol. to 40% Total pigment volume concentration (PVC) of vol. including pigment (P) and filler (I).

Description

[0001] Cross References to Related Applications [0002] This application claims priority from European Application No. 16305299.6 filed on March 18, 2016, the entire content of which is hereby incorporated by reference for all purposes. technical field [0003] The present invention relates to aqueous coating compositions and methods for forming protective coatings on substrates, especially metal-containing substrates. More specifically, the present invention relates to coating compositions, methods, and coating systems involving aqueous coating compositions that can be applied at high coating thicknesses as a direct-to-metal coat, providing excellent finishing and corrosion protection. Background technique [0004] Aqueous or water-based coating compositions for protective coatings of substrates, such as preventing corrosion or rusting of ferrous metals, are well known. [0005] Particularly advantageous are compositions that do not require any "baking" periods at temper...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D127/08C08K3/32C09D5/08
CPCC09D5/084C08K2003/327C09D127/08C08K3/32C08K5/32C09D7/61C09D7/70C09D7/45
Inventor 潘延中A.查普托特Y.范德维肯
Owner SOLVAY SA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com