Solvent-free graphene oxide loaded silica nano fluid and applications
A silicon dioxide, fluid-like technology, used in additives, petroleum industry, lubricating compositions, etc., to achieve the effect of promoting high performance, good anti-friction and anti-wear performance, and improving lubricating performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0038]In parts by mass, 100 parts of silica nanoparticles (8 nm) were dispersed in a mixed solution of 550 mL of deionized water (50 mL) and ethanol (500 mL), ultrasonicated for 1 h, and 100 parts of % of 3-aminopropyltriethoxysilane surfactant, stirred and refluxed at 90 °C for 24 h, centrifuged at 10,000 rpm, washed with deionized water and ethanol, and dried in vacuum at 80 °C for 24 h to obtain surfactant-modified of silica nanoparticles. In parts by mass, 10 parts of graphene oxide were dispersed in 300 mL of deionized water, ultrasonically stripped for 2 h, 20 parts of modified silica nanoparticles were added, reacted at 80 °C for 12 h, and the product was centrifuged at 10,000 rpm and washed with deionized water and Wash and purify with ethanol, and dry in vacuum at 80 °C for 24 h to obtain graphene oxide-supported silica nanoparticles; in parts by mass, take 20 parts of graphene oxide-supported silica nanoparticles and disperse them in 100 mL deionized water , sonicat...
Embodiment 2
[0041] In parts by mass, 40 parts of silica nanoparticles (12 nm) were dispersed in a mixed solution of 300 mL of deionized water (20 mL) and ethanol (280 mL), ultrasonicated for 1 h, and 100 parts of % of 3-aminopropyltriethoxysilane surfactant, stirred and refluxed at 120 °C for 24 h, the product was centrifuged at 10,000 rpm, washed and purified with deionized water and ethanol, and dried in vacuum at 80 °C for 24 h to obtain surface active Agent-modified silica nanoparticles. In parts by mass, 10 parts of graphene oxide were dispersed in 300 mL of deionized water, ultrasonically stripped for 1 h, 40 parts of modified silica nanoparticles were added, reacted at 100 ° C for 12 h, and the product was washed with deionized water and ethanol after centrifugation Purify and dry in vacuum at 80 °C for 24 h to obtain graphene oxide-supported silica nanoparticles; according to the mass fraction, take 10 parts of graphene oxide-supported silica nanoparticles, disperse them in 100 mL...
Embodiment 3
[0043] In parts by mass, disperse 10 parts of silica nanoparticles (25 nm) in a mixed solution of 210 mL deionized water (10 mL) and ethanol (200 mL), sonicate for 1 h, and add 100 parts with a mass fraction of 65 % of 3-aminopropyltriethoxysilane surfactant, stirred and refluxed at 150 °C for 8 h, centrifuged at 10000 rpm, washed with deionized water and ethanol, and dried in vacuum at 80 °C for 24 h to obtain surfactant-modified Silica nanoparticles. In parts by mass, 10 parts of graphene oxide were dispersed in 300 mL of deionized water, ultrasonically stripped for 1 h, 150 parts of modified silica nanoparticles were added, reacted at 160 °C for 8 h, and the product was centrifuged at 10,000 rpm and washed with deionized water Wash and purify with ethanol, and vacuum-dry at 80 °C for 24 h to obtain graphene oxide-supported silica nanoparticles; in parts by mass, take 10 parts of graphene oxide-supported silica nanoparticles and disperse them in 100 mL deionized water , son...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
Login to view more - R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap