Mesoporous molybdenum phosphonate material, preparation method and application thereof

A phosphonic acid and mesoporous technology, applied in the field of mesoporous materials, can solve the problems of large residual amount and affect material performance, and achieve the effect of high specific surface area, reducing residual amount and improving stability

Active Publication Date: 2022-05-17
SHENZHEN UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The first object of the present invention is to provide a method for preparing a mesoporous molybdenum phosphonate material, which aims to solve the problem of affecting the performance of the material due to the removal of a large amount of hard template residue when preparing a material with a mesoporous structure in the prior art technical problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The following clearly and completely describes the technical solutions in the embodiments of the present invention. Obviously, the described embodiments are only part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0029] It should be noted that the descriptions involving "first", "second", etc. in the present invention are only for descriptive purposes, and should not be understood as indicating or implying their relative importance or implicitly indicating the number of indicated technical features . Thus, the features defined as "first" and "second" may explicitly or implicitly include at least one of these features. In addition, the technical solutions of the various embodiments can be combined with each other, but it must be based...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is suitable for the field of medium material technology, and the melody and its preparation methods and applications are disclosed.In the ion water water, add the acetomine tethampuaic acid and sodium hydroxide and the water bath to obtain the first solution; solve ammonium molybdenonate in removing ion water, add the first solution and heat the water bath to get the second solution; it will be obtained; it willThe second solution is aging, rinsing, and drying the first powder; mix the first powder with hydrochloric acid and water -free ethanol and perform a water bath to get the third solution, dry and get the second powder;In the first ethanol mixture of chlorine chlorine, the second ethanol mixture with sodium boroside is added to the third powder.The surface of the melody of the memor acid molybdenum material made of the present invention is electrical and loaded with platinum, which has excellent anti -interference ability.

Description

technical field [0001] The invention relates to the technical field of mesoporous materials, in particular to a mesoporous molybdenum phosphonate material and its preparation method and application. Background technique [0002] Mesoporous materials refer to nanoporous materials with pore diameters between 2 nm and 50 nm. Due to their very high pore capacity and specific surface area, high thermal and hydrothermal stability, and easy-to-modulate regular nano Pores (such as pore size, dimension, etc.), abundant and easy-to-design surface groups, and adjustable macroscopic morphology (such as membranes, fibers, spheres, etc.), so in macromolecular separation, biosensors, catalysis, adsorption, microelectronics It has good application prospects in the fields of optics, optics and preparation of new nanomaterials. Phosphonate is a kind of organic-inorganic hybrid material, which has the characteristics of many kinds of skeleton elements, pore or cage structure, etc., and is wid...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): C01B25/37G01N33/00
CPCG01N33/00C01B25/37
Inventor杨海朋王洽杨琴珪王荣颖马翔裕李娜
OwnerSHENZHEN UNIV