Wall material protecting film and preparation method thereof

A protective film and wall material technology, applied in the field of wall material protective film and its preparation, can solve the problems of user health hazards, decoration wall materials containing peculiar smell, etc., and achieve the effects of beautifying the environment, purifying indoor air, and having a good hand feeling

Inactive Publication Date: 2019-03-19
秦皇岛美博士新型材料科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, the architectural decoration on the market, whether it is a home or a public place, mostly uses latex paint, shell powder paint, diatom mud paint or wallpaper, etc., all of which have their own functions, but the decoration wall materials contain odor, formaldehyde, Benzene, toluene, xylene, VOC and some bacteria pose a hazard to the health of users

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Wall material protecting film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] The application provides a wall material protective film, which is composed of the following raw materials in parts by weight: emulsion 250, nano photocatalyst 30, formaldehyde scavenger 15, active nano silver ions 70, and some deionized water.

[0024] Optionally, the emulsion is an acrylate styrene emulsion polymer.

[0025] Optionally, the nano photocatalyst is titanium dioxide.

[0026] Optionally, the formaldehyde scavenger is imidazolidinone.

[0027] A preparation method of a wall material protective film, said preparation method comprising the steps of:

[0028] Step 1: After completely dissolving the emulsion, nano-photocatalyst, formaldehyde scavenger, and active nano-silver ions with deionized water, add them to the reaction tank in sequence according to the proportion;

[0029] Step 2: Start the reaction tank, and stir for 30-45 minutes at room temperature at 300-500 rpm.

Embodiment 2

[0031] The application provides a wall material protective film, which is composed of the following raw materials in parts by weight: emulsion 280, nano photocatalyst 35, formaldehyde scavenger 25, active nano silver ions 90, and some deionized water.

[0032] Optionally, the emulsion is an acrylate styrene emulsion polymer.

[0033] Optionally, the nano photocatalyst is titanium dioxide.

[0034] Optionally, the formaldehyde scavenger is imidazolidinone.

[0035] A preparation method of a wall material protective film, said preparation method comprising the steps of:

[0036] Step 1: After completely dissolving the emulsion, nano-photocatalyst, formaldehyde scavenger, and active nano-silver ions with deionized water, add them to the reaction tank in sequence according to the proportion;

[0037] Step 2: Start the reaction tank, and stir for 30-45 minutes at room temperature at 300-500 rpm.

Embodiment 3

[0039] The application provides a wall material protective film, which is composed of the following raw materials in parts by weight: emulsion 300, nano photocatalyst 40, formaldehyde scavenger 130, active nano silver ions 100, and some deionized water.

[0040] Optionally, the emulsion is an acrylate styrene emulsion polymer.

[0041] Optionally, the nano photocatalyst is titanium dioxide.

[0042] Optionally, the formaldehyde scavenger is imidazolidinone.

[0043] A preparation method of a wall material protective film, said preparation method comprising the steps of:

[0044] Step 1: After completely dissolving the emulsion, nano-photocatalyst, formaldehyde scavenger, and active nano-silver ions with deionized water, add them to the reaction tank in sequence according to the proportion;

[0045] Step 2: Start the reaction tank, and stir for 30-45 minutes at room temperature at 300-500 rpm.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of wall material protection and particularly relates to a wall material protecting film and a preparation method thereof. Due to the fact of containing odor, formaldehyde, benzene, methylbenzene, xylene, VOC (volatile organic compounds) and bacteria, existing decorative wall materials can bring harm to users. The wall material protecting film is composed of raw materials including, by weight part, 250-350 parts of emulsion, 30-50 parts of nanometer photocatalysts, 15-250 parts of formaldehyde catching agent, 70-120 parts of active nano-silver ions,and deionized water. The wall material protecting film is less prone to powdering, high in glossiness, good in hand feeling, washable, deodorant, bactericidal and capable of removing formaldehyde, ammonia, benzene, methylbenzene, xylene, VOC and the like, purifying indoor air and beautifying the environment.

Description

technical field [0001] The application belongs to the technical field of building wall material protection, and in particular relates to a wall material protective film and a preparation method thereof. Background technique [0002] As the name implies, "wall material" refers to the materials related to the wall painting construction and the treatment of ordinary mortar surfaces. In the current sense, the "wall material" products we see are all labeled as "environmentally friendly" wall materials, which may also become There is a commonality of wall materials. Common wall materials on the market include ordinary wallpaper, wall covering, liquid wallpaper, diatom mud, volcanic mud, sand painting wall materials, sand painting mud, sand painting paint, etc. [0003] At present, the architectural decoration on the market, whether it is a home or a public place, mostly uses latex paint, shell powder paint, diatom mud paint or wallpaper, etc., all of which have their own functions...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/04C09D5/14
CPCC08K2003/2241C09D5/14C09D133/04C08K3/22
Inventor 于海深安俊峰王德刚赵明华
Owner 秦皇岛美博士新型材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com