Method for producing converter slugging agent through electrolytic aluminum overhaul slag

A technology of slag removal agent and overhaul slag, which is applied in the direction of manufacturing converters and improving process efficiency, can solve the problems of producing converter slag remover without electrolytic aluminum overhaul slag, reduce bond energy, reduce HF generation, and avoid water effect

Inactive Publication Date: 2019-05-10
新疆中合大正冶金科技有限公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] According to the above literature introduction, it can be seen that there is no technology to produce converter slag agent by using electrolytic aluminum overhaul slag

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0037] According to above finding, a kind of method implementation process of utilizing electrolytic aluminum overhaul slag to produce converter slag agent is as follows:

[0038] 1) Classify the electrolytic aluminum overhaul slag. After the carbon block is picked out, it will be returned to the aluminum factory for recycling. The remaining electrolyte will be processed to a particle size of 1-5mm by a ball mill according to the principle of mechanochemical reaction, so that it has a good chemical reactivity;

[0039] 2) Purchase the vermiculite raw material, the weight percentage content of each component in the vermiculite: SiO 2 30-45, Fe 2 o 3 5-35, Al 2 o 3 <20, MgO 15-26, CaO <1, use a jaw crusher to crush to a particle size of 3-5mm, and use it as aggregate for pelletizing;

[0040] 3) Mix the above materials evenly according to the ratio of 80:17 by mass, and add 3% heavy oil as binder.

[0041] 4) Press the above materials into a 30-50mm spherical slag reduc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for producing a converter slugging agent through electrolytic aluminum overhaul slag. The method comprises the steps that firstly, the electrolytic aluminum overhaul slag is classified, electrolyte left after picking out carbon blocks is processed through a ball mill until the particle sizes are 1 mm-5 mm; secondly, vermiculite raw materials are purchased, the vermiculite raw materials comprise, by weight percent, 30%-45% of SiO2, 5%-35% of Fe2O3, less of 20% of Al2O3, 15%-26% of MgO, less of 1% of CaO, a jaw crusher is used for crushing the raw materials into3 mm-5 mm to serve as aggregate during pelletizing; thirdly, the materials are mixed according to the mass percent of 80: 17 to be uniform, and 3% of heavy oil is added to serve as a binding agent; fourthly, the materials are pressed into the 30 mm-50 mm spherical slugging agent through a dry powder ball press machine, and the spherical slugging agent comprises components including, by weight percent, 2%-10% of Fe2O3, less of 35% of F, less of 5% of MgO, and less or 20% of Na; fifthly, the slugging agent spheres are transported to a converter production line to be used; sixthly, the slugging agent spheres are normally used according to an application method of the slugging agent; and seventhly, the application amount of the slugging agent is 0.8 kg / ton of steel-3 kg / ton of steel.

Description

technical field [0001] The invention relates to a method for producing converter slag reducing agent by using electrolytic aluminum overhaul slag. Electrolytic aluminum overhaul slag is a hazardous waste because it is rich in various fluorides and cyanides. The invention relates to the technical fields of two different industries, the recycling technology of electrolytic aluminum solid waste and the technology of iron and steel smelting converter steelmaking. The electrolyte in the middle of the overhaul slag is mixed with auxiliary materials to produce the slag agent in the converter smelting process, which is used instead of fluorite. technology. Background technique [0002] The aluminum electrolytic cell needs to be overhauled after 4 to 7 years of operation. The waste removed is called overhaul slag, mainly waste cathode carbon blocks, waste refractory materials, waste insulation materials, etc., and a certain amount of waste is also produced during the electrolysis pr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21C5/36
CPCY02P10/20
Inventor 俞海明吴汉元陈红蒲翠娥吴英元
Owner 新疆中合大正冶金科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products