Multifunctional mineral ceramic hot compress material and preparation method and application thereof

A functional material and multi-functional technology, applied in the field of multi-functional mineral ceramic hot compress material and its preparation, can solve the problems of lack of dehumidification and antibacterial, single function, and relatively expensive price, so as to avoid secondary infection, relieve body pain, Energy Saving Effect

Active Publication Date: 2019-05-24
陈滨
View PDF11 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These products are more expensive, have a single function, and lack functions such as dehumidification and antibacterial

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional mineral ceramic hot compress material and preparation method and application thereof
  • Multifunctional mineral ceramic hot compress material and preparation method and application thereof
  • Multifunctional mineral ceramic hot compress material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A multifunctional mineral ceramic hot compress material is made of the following raw materials in weight percentage: 56% of hygroscopic material, 3% of antibacterial material, 30% of functional material, 10% of inorganic binder and 1% of graphene.

[0045] in:

[0046] The hygroscopic material is made of raw materials with the following weight percentages: sepiolite 40%, attapulgite 20%, bentonite 10% and zeolite 30%.

[0047] The antibacterial material is made of the following raw materials in percentage by weight: 95% of nano-zinc oxide, 1% of silver powder and 4% of copper-zinc alloy, and the particle size of nano-zinc oxide is 20-100 nanometers.

[0048] The functional material is made of the following raw materials in weight percentage: 30% of terahertz powder, 50% of meteorite powder, 10% of far-infrared powder and 10% of germanium powder.

[0049] The inorganic binder is a mixture of water glass and sodium metasilicate, and the mass ratio of water glass and sodi...

Embodiment 2

[0055] A multifunctional mineral ceramic hot compress material is made of the following raw materials in weight percentage: 60% of hygroscopic material, 2% of antibacterial material, 28% of functional material, 9% of inorganic binder and 1% of graphene.

[0056] in:

[0057] The hygroscopic material is made of raw materials with the following weight percentages: sepiolite 45%, attapulgite 20%, bentonite 10% and zeolite 25%.

[0058] The antibacterial material is made of the following raw materials in percentage by weight: 94% of nano-zinc oxide, 1% of silver powder and 5% of copper-zinc alloy, and the particle size of nano-zinc oxide is 20-100 nanometers.

[0059] The functional material is made of the following raw materials in weight percentage: 34% of terahertz powder, 46% of meteorite powder, 8% of far-infrared powder and 12% of germanium powder.

[0060] The inorganic binder is a mixture of water glass and sodium metasilicate, and the mass ratio of water glass and sodium...

Embodiment 3

[0066] A multifunctional mineral ceramic hot compress material is made of the following raw materials in weight percentage: 65% of hygroscopic material, 1% of antibacterial material, 25% of functional material, 8% of inorganic binder and 1% of graphene.

[0067] in:

[0068] The hygroscopic material is made of raw materials with the following weight percentages: sepiolite 35%, attapulgite 25%, bentonite 8% and zeolite 32%.

[0069] The antibacterial material is made of the following raw materials in percentage by weight: 96% of nano-zinc oxide, 1% of silver powder and 3% of copper-zinc alloy, and the particle size of nano-zinc oxide is 20-100 nanometers.

[0070] The functional material is made of the following raw materials in weight percentage: 25% of terahertz powder, 55% of meteorite powder, 12% of far-infrared powder and 8% of germanium powder.

[0071] The inorganic binder is a mixture of water glass and sodium metasilicate, and the mass ratio of water glass and sodium ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a hot compress material, in particular to a multifunctional mineral ceramic hot compress material and a preparation method and application thereof. The raw materials of the material are as follows: 56-70% of a hygroscopic material, 1-3% of an antibacterial material, 16-30% of a functional material, 1-10% of an inorganic binder and 0.1-1% of graphene; wherein the hygroscopic material is prepared from sepiolite, attapulgite, bentonite and zeolite; the antibacterial material is prepared from nano zinc oxide, silver powder and copper-zinc alloy; the functional material isprepared from terahertz powder, stone needle powder, far infrared ray powder and germanium powder; the inorganic binder is a mixture of water glass and sodium metasilicate. The hot compress material has the functions of superstrong permeability, moisture absorption and bacteriostasis, high temperature resistance, long-acting property and safety, and better effects of dredging channels and collaterals, promoting metabolism and relieving pain; the preparation method is simple in process, energy-saving and environment-friendly; has wide application and can be applied to hot compress bags, porcelain blankets, functional pillows, mattresses and cushions.

Description

technical field [0001] The invention relates to a heat compress material, in particular to a multifunctional mineral ceramic heat compress material and its preparation method and application. Background technique [0002] Hot compress has a history of thousands of years in China, and hot compress therapy belongs to a kind of "ironing method" in external treatment of traditional Chinese medicine. It has the effect of dilating capillaries and accelerating blood circulation, so that muscles are slowly relaxed, muscles and bones are flexible, and it has the effect of eliminating fatigue, dispelling cold and dampness, and improving neck and shoulder pain. [0003] With the enhancement of people's health awareness and the rejuvenation of the sub-health state of the body, more and more hot compress products are welcomed by people. Hot compress products sold on the market mainly include products such as salt packs and red bean bags. Salt bags are generally made of sea salt, which ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26A47G9/00A47G9/06A47G9/10A47C21/04A61N5/06C04B111/20
Inventor 王家胜
Owner 陈滨
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap