A bending-resistant privacy film

A privacy film, bending-resistant technology, used in instruments, optics, optical components, etc., can solve the problems of slow speed, uneven filling, difficult to control the thickness of vinyl, and achieve excellent adhesion, good toughness, and not easy to peel off. Effect

Active Publication Date: 2021-10-26
ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the presence of solvent in the thermal curing system, the solvent volatilizes during the baking process, the thickness of the black glue is difficult to control, and uneven filling may occur. The solvent will also cause environmental pollution. At the same time, due to the relatively high thermal curing rate Slower, which greatly increases storage costs, and in the process of mass production, manufacturing costs will be relatively high
If the absorbing layer adopts UV curing molding technology, it can avoid solvent pollution, but the black adhesive layer is easy to absorb ultraviolet light, and the structure height of the anti-peeping film is about 100 μm, which is relatively deep, which makes the central part of the black cover rubber more difficult to cure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A bending-resistant privacy film
  • A bending-resistant privacy film
  • A bending-resistant privacy film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] The parts by mass of each component of the glue in the transmission layer are as follows: 40 parts of DR-U029 (manufactured by Changxing) for oligomers, 4 parts of functionality, 40 parts of OPPEA (manufactured by KPX) for monomers, and 184 (double Key Chemical Manufacturing) 4 parts, TPO (Double Bond Chemical Manufacturing) 0.5 parts, release aid is ZG-400 (TEGO Company) 5 parts.

[0045] The parts by mass of each component of the absorbing layer glue are as follows: 30 parts of polyether polyurethane methacrylate BR-202 (DYMAX company) for oligomers, 30 parts of monomer BPA8EODA (DSM), and 30 parts of monomer OPPEA (manufactured by KPX) is 5 parts, the auxiliary agent is 1 part of RAD2200 (TEGO company), the initiator is selected as 1 part of 127 (manufactured by double bond chemical industry), 2 parts of TPO (manufactured by double bond chemical industry), 7 parts of color paste, Thiol accounts for 3 parts.

[0046] The substrate layer is a PET substrate produced by...

Embodiment 2

[0048] The parts by mass of each component of the glue in the transmission layer are as follows: 40 parts of DR-U029 (manufactured by Changxing) for oligomers, 4 parts of functionality, 40 parts of OPPEA (manufactured by KPX) for monomers, and 184 (double Key Chemical Manufacturing) 4 parts, TPO (Double Bond Chemical Manufacturing) 1.5 parts, release aid is ZG-400 (TEGO Company) 3 parts.

[0049] The parts by mass of each component of the absorbing layer glue are as follows: 30 parts of polyether polyurethane methacrylate BR-202 (DYMAX company) for oligomers, 30 parts of monomer BPA8EODA (DSM), and 30 parts of monomer OPPEA (manufactured by KPX) is 5 parts, the additive is 1 part of RAD2200 (TEGO company), the initiator is selected as 1 part of 127 (manufactured by double bond chemical industry), 2 parts of TPO (manufactured by double bond chemical industry), 784 (manufactured by double bond chemical industry) ) 0.2 parts. The color paste accounts for 7 parts, and the mercapt...

Embodiment 3

[0052]The parts by mass of each component of the glue in the transmission layer are as follows: 15 parts of CN8010NS (manufactured by Sartomer) and 35 parts of 6158B-80 (manufactured by Changxing) are selected as the oligomer, and the average functionality of the mixture is 3.5; the monomer is selected from OPPEA (manufactured by KPX) 35 parts; the initiator is selected as 4 parts of 184 (manufactured by double bond chemical industry), 1.5 parts of TPO (manufactured by double bond chemical industry); the demoulding aid is 5 parts of ZG-400 (manufactured by TEGO company).

[0053] The parts by mass of each component of the glue in the absorbing layer are: 30 parts of polyester polyurethane methacrylate XR-741MS (DYMAX company) for oligomer, 30 parts of monomer BPA6EODA (DSM), and 30 parts of monomer OPPEA (KPX company) ratio is 5 parts, auxiliary agent RAD2200 (TEGO company) 1 part, initiator is selected as 127 (manufactured by double bond chemical industry) 1 part, TPO (manufac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Shore hardnessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Shore hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bending-resistant anti-peeping film, which comprises a base material layer, a transmission layer arranged on the surface of the base material layer, the transmission layer comprises a plurality of microstructures, and a A concave cavity, the privacy film further includes an absorbing layer filled in the cavity, and the Shore hardness of the transmissive layer and the absorbing layer are both less than or equal to 80D. The anti-peeping film of the present invention, on the one hand, has good toughness, can withstand bending, and no cracks will appear when it is bent, and the adhesion between the layers of the anti-peeping film is excellent, and it is not easy to peel off; on the other hand, the anti-peeping film Both the transmission layer and the absorbing layer of the anti-peeping film adopt a solvent-free UV curing system, which will not cause environmental pollution, and the UV curing system of the absorbing layer solves the problem that the light-absorbing material of the traditional anti-peeping film is difficult to cure.

Description

technical field [0001] The invention belongs to the technical field of anti-peeping film, and in particular relates to a anti-peeping film resistant to bending. Background technique [0002] With the development of the times, people pay more and more attention to personal privacy, and the anti-spy film was born. The use of anti-spy film can allow people to block the sight of people around them when they use personal computers and mobile phones in public places, and protect personal privacy. In addition, on the ATM machine, the anti-spy film can block the light on the side, so that people on both sides cannot see the screen, which protects the privacy of the ATM machine operator. At present, the application of anti-peeping film has become more and more extensive. [0003] However, the existing anti-spy film has high hardness, and it is unavoidable to bend and curl it during use. Cracks are prone to appear from time to time, affecting the appearance and clarity of the scree...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G02B5/00G02B1/04G02B1/10
Inventor 王开仪李冠毅丁清华
Owner ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com