A laser-weldable resin composition with high metal texture and preparation method thereof

A resin composition and laser welding technology, applied in the field of automobile lamps, can solve the problems of low laser absorption rate, inability to weld two parts and welding strength, etc., and achieve the advantages of simple process operation, good laser welding performance, and effective laser welding. Effect

Active Publication Date: 2021-06-15
HASCO VISION TECHNOLOGY CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, if the opaque plastic is difficult to absorb laser light or its laser absorption rate is not high, it is easy to cause two parts to be welded or the weld strength is too low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A laser-weldable resin composition with high metal texture and preparation method thereof
  • A laser-weldable resin composition with high metal texture and preparation method thereof
  • A laser-weldable resin composition with high metal texture and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0104] A laser-weldable resin composition with high metallic texture is used for injection molding the resin composition into a car lamp bezel, and laser welding is performed on the car lamp bezel and a transparent PC inner light distribution mirror.

[0105] The resin composition preparation method comprises the following steps:

[0106] Prepare raw materials according to the following components and parts by weight:

[0107]

[0108] The laser powder is Sn / In mixed oxide type,

[0109] The metal pigment is aluminum powder with a particle diameter of 0.5 μm to 40 μm.

[0110] The color additive is selected from inorganic toner with a particle size of 0.001 μm to 1 μm rutile titanium dioxide and iron oxide red iron oxide, and pearlescent powder with a particle size of 0.001 μm to 50 μm. The core of the pearlescent powder is mica with a low optical refractive index. The outer layer is coated with titanium dioxide or iron oxide with a high refractive index, and ceramic powd...

Embodiment 2

[0116] A laser-weldable resin composition with high metallic texture is injection-molded into a flat plate, which is laser-welded with a transparent PC plate and used for molding to obtain car lamp parts. Or the resin composition is injection-molded into a car lamp bezel, and the car light bezel is directly laser-welded with a transparent PC inner light distribution mirror. Its preparation method comprises the following steps:

[0117] Prepare raw materials according to the following components and parts by weight:

[0118]

[0119]

[0120]The laser powder is selected from Sn / Sb mixed oxide type (50%)+TiO2 type (50%),

[0121] The metal pigment is zinc powder (50%)+copper powder (50%) with a particle size of 0.5 μm to 40 μm,

[0122] The color additive is selected from carbon black series + iron oxide series + chromium series and metal oxide mixed-phase pigment system with inorganic toner particle size of 0.001 μm ~ 1 μm, pearl powder with particle size of 0.001 μm ~ ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of vehicle materials, in particular to a laser-weldable resin composition with high metallic texture and a preparation method thereof. The present invention includes the following components in parts by weight: matrix resin 100, laser powder 0.05-5.0, metal pigment 0.1-5.0, color additive 0.05-5.0, antioxidant 0.1-1.0; its preparation method comprises matrix resin, laser powder, Metallic pigments, color additives, and antioxidants are fully mixed in a low-speed mixer, and then sent into a twin-screw extruder through a metering device. Through screw conveying, shearing, and mixing, the materials are fully melted and mixed, and then extruded extraction, drawing, cooling, and pelletizing to obtain a laser-weldable resin composition. The resin composition with high metallic texture prepared by the invention can realize excellent laser welding performance.

Description

technical field [0001] The invention relates to a resin composition capable of laser welding and having a high metal texture and a preparation method thereof. The resin composition with a high metal texture of the invention can be used in the fields of car lamps and the like. Background technique [0002] Laser welding technology is now gradually being used in the automotive field, especially for parts on car lights. Laser welding technology has begun to be used to weld plastic parts of car lights together. [0003] The aesthetic resin material with high metallic texture is easy to win the favor of modeling and designers due to its perfect appearance. However, the usual aesthetic resins for car lights do not have enough ability to absorb laser energy, so this type of material cannot be used for car light parts that require laser welding, or when laser welding is performed, the laser welding strength is not enough Lead to low yield. [0004] On the other hand, when laser we...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L69/00C08L55/02C08K3/22C08K3/08
Inventor 文珍稀顾丹吴苏容樊一君陈兆禹李志兵
Owner HASCO VISION TECHNOLOGY CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com