Stamping die surface phosphating processing method

A technology of stamping die and processing method, which is applied in the field of phosphating treatment on the surface of stamping die to achieve the effect of firm adhesion of coating, smooth surface and improved quality

Inactive Publication Date: 2019-07-23
长沙而道新能源科技有限公司
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides a phosphating treatment method for the surface of a stamping die to solve how to optimize the process based on the surface treatment method for a stamping die disclosed in the Chinese patent application document "A Surface Treatment Method for a Stamping Die (Application Publication No.: CN107916430A)" Parameters and composition of phosphating solution, etc., to improve the technical problems of high temperature corrosion resistance of stamping dies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stamping die surface phosphating processing method
  • Stamping die surface phosphating processing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] A method for phosphating the surface of a stamping die, comprising the following steps in sequence:

[0051] (1) Grinding the stamping mold, using sandpaper to polish the surface of the stamping mold, specifically using sandpaper to polish the surface of the mold is as follows: respectively use 200 mesh, 600 mesh, 1200 mesh, and 1800 mesh sandpaper on the surface of the stamping mold Grinding, each grinding time is 40min;

[0052] (2) Heat the stamping die processed in step (1) to 700°C, keep it warm for 7 minutes, then cool it down to room temperature naturally, immerse it in absolute ethanol for 10 minutes at a temperature of 85°C, take it out, and clean it with deionized water. Then dry to constant weight, get final product;

[0053] (3) soak the stamping die after step (2) processing in the phosphating solution, soak for 6min, then take out, the surface adopts deionized water to clean to neutrality, then dry, and described phosphating solution comprises following r...

Embodiment 2

[0061] A method for phosphating the surface of a stamping die, comprising the following steps in sequence:

[0062](1) Grinding the stamping mold, using sandpaper to polish the surface of the stamping mold, specifically using sandpaper to polish the surface of the mold is as follows: respectively use 200 mesh, 600 mesh, 1200 mesh, and 1800 mesh sandpaper on the surface of the stamping mold Grinding, each grinding time is 30min;

[0063] (2) Heat the stamping die processed in step (1) to 800°C, keep it warm for 5 minutes, then cool it down to room temperature naturally, immerse it in absolute ethanol for 10 minutes at a temperature of 90°C, then take it out and clean it with deionized water. Then dry to constant weight, get final product;

[0064] (3) soak the stamping die after step (2) processing in the phosphating solution, soak for 5min, then take out, the surface adopts deionized water to clean to neutrality, then dry, and described phosphating solution comprises followin...

Embodiment 3

[0072] A method for phosphating the surface of a stamping die, comprising the following steps in sequence:

[0073] (1) Grinding the stamping mold, using sandpaper to polish the surface of the stamping mold, specifically using sandpaper to polish the surface of the mold is as follows: respectively use 200 mesh, 600 mesh, 1200 mesh, and 1800 mesh sandpaper on the surface of the stamping mold Grinding, each grinding time is 50min;

[0074] (2) Heat the stamping die processed in step (1) to 600°C, keep it warm for 8 minutes, then cool it down to room temperature naturally, immerse it in absolute ethanol for 10 minutes at a temperature of 80°C, take it out, and clean it with deionized water. Then dry to constant weight, get final product;

[0075] (3) soak the stamping die after step (2) processing in the phosphating solution, soak for 8min, then take out, the surface adopts deionized water to clean to neutrality, then dry, and described phosphating solution comprises following r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a stamping die surface phosphating processing method, and relates to the technical field of mold processing. The stamping die surface phosphating processing method includes thefollowing steps of polishing, heating, phosphating, twice soaking and twice drying processing and pressurizing processing. By means of the stamping die surface phosphating processing method, a uniform and compact phosphating film can be formed on the surface of a stamping die, the surface of the stamping die can be better protected, and the processed stamping die has excellent high-temperature corrosion-resistant performance.

Description

[0001] 【Technical field】 [0002] The invention belongs to the technical field of mold treatment, and in particular relates to a phosphating treatment method for the surface of a stamping mold. [0003] 【Background technique】 [0004] The so-called molds are various molds and tools used in industrial production for injection molding, blow molding, extrusion, casting, forming, smelting, stamping, stretching and other methods to obtain the required products. Stamping die is a special process equipment that applies pressure to the material to cause separation or plastic deformation to obtain the required parts or products. Due to the generally large production batches of stamping parts and the high working temperature of stamping, the surface of the stamping die often suffers from wear, oxidation, or oil contamination, which leads to the quality and appearance of the stamped workpieces not up to standard. It is of great significance to effectively treat the surface to reduce the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C22/44C23C22/82
CPCC23C22/44C23C22/82
Inventor 不公告发明人
Owner 长沙而道新能源科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap