Tantalum oxide coating both having good biocompatibility and photothermal conversion effects and preparation method and application of tantalum oxide coating

A technology of tantalum oxide and coating, applied in the field of tantalum oxide coating and its preparation, can solve the problem that the coating does not have the light-to-heat conversion effect

Inactive Publication Date: 2019-08-16
SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating does not ha...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tantalum oxide coating both having good biocompatibility and photothermal conversion effects and preparation method and application of tantalum oxide coating
  • Tantalum oxide coating both having good biocompatibility and photothermal conversion effects and preparation method and application of tantalum oxide coating
  • Tantalum oxide coating both having good biocompatibility and photothermal conversion effects and preparation method and application of tantalum oxide coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0050] Choose Ta with a particle size of about 10 μm 2 o 5 Powder (w(Ta 2 o 5 )=99.99%) as raw material (purchased from Jiujiang Fengfu New Material Co., Ltd.), made into slurry with 40% solid content for spray granulation, atomizer speed: 22,000 rpm, feed rate: 770ML / points, the obtained powder morphology is as follows figure 1 shown. Depend on figure 1 It can be seen that most of the powder is in the shape of spherical particles with uniform size, about 20-80 μm, and has good fluidity. The powder was dried at 110°C for 1 hour, and cooled for later use.

[0051] The base material is made of titanium sheet, which is processed into a small disc of Φ10mm×2mm. After sandblasting the surface of the titanium sheet, ultrasonically clean it once in absolute ethanol solution for 3 minutes, then dry it at 100°C for 1 hour, and cool it for later use; the pressure of sandblasting is 0.3MPa.

[0052] Atmospheric plasma vacuum plasma spraying process is used respectively to spray ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention relates to a tantalum oxide coating both having good biocompatibility and photothermal conversion effects and a preparation method and application of the tantalum oxide coating. The tantalum oxide coating is formed by spraying Ta2O5 powder by adopting a plasma spraying method. The tantalum oxide coating has higher bone differentiation facilitating capacity, good biocompatibility andthe photothermal conversion performance.

Description

technical field [0001] The invention relates to a tantalum oxide coating with good biocompatibility and light-to-heat conversion effect, its preparation method and application. Specifically, it relates to a tantalum oxide coating sprayed by plasma spraying technology and a preparation method thereof, belonging to the technical field of medical biological coatings. Background technique [0002] Due to population aging, bone tumors, bone deformities, and traffic accidents, metal bone implant materials have been widely used clinically, such as titanium total joint replacement materials. Tantalum has good corrosion resistance and the function of promoting bone regeneration, and it has attracted widespread attention as a bone implant material. [0003] Tantalum has good biocompatibility, and the dense natural oxide layer on the surface of tantalum metal plays an important role. This layer of natural oxide layer is more stable than titanium oxide, and the presence of tantalum ox...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C4/134C23C4/11A61L27/30
CPCA61L27/30C23C4/11C23C4/134
Inventor 谢有桃丁玎李恺黄利平赵君郑学斌
Owner SHANGHAI INST OF CERAMIC CHEM & TECH CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap