A kind of polyoxymethylene monofilament for fishing and its preparation method and application

A polyoxymethylene, monofilament technology, applied in the manufacture of rayon, conjugated synthetic polymer rayon, single-component synthetic polymer rayon, etc., can solve the problems of low impact strength, notch sensitivity, etc., to reduce friction Damaged, no broken filaments, good spinnability and comprehensive performance

Active Publication Date: 2022-02-08
EAST CHINA SEA FISHERIES RES INST CHINESE ACAD OF FISHERY SCI
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to prepare high-performance polyoxymethylene fibers and make them have sufficient tensile breaking strength, they must be subjected to high-speed thermal drawing in the production process, and high-modulus and high-strength polyoxymethylene fiber samples can be obtained, but polyoxymethylene fibers After super-stretching, it will show greater brittleness, and has the disadvantages of notch sensitivity and low impact strength.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A polyoxymethylene monofilament for fishing is made of the following components by weight: 75 parts of N60520922 polyoxymethylene, 3 parts of FH-661 graphene, 17 parts of 9380A polyether thermoplastic polyurethane, 3 parts of antioxidant 1010, 0.5 Formaldehyde absorbent 660, formic acid absorbent calcium dodecylbenzenesulfonate 0.5 part, RLC 657 polyethylene wax lubricant 1 part.

[0034] A preparation method of the polyoxymethylene monofilament for fishing comprises the following steps:

[0035] Pre-mix polyoxymethylene, graphene, thermoplastic polyurethane, antioxidant, formaldehyde absorbent, formic acid absorbent, and lubricant, and then pour it into a high-speed kneader, kneading at a high speed at a speed of 750r / min-800r / min After 30-60 minutes, raise the temperature of the mixture in the high-speed kneader to 80°C to discharge, and obtain a polyoxymethylene modified compound;

[0036] The polyoxymethylene modified composite material is melt-spun by a twin-screw...

Embodiment 2

[0042] A polyoxymethylene monofilament for fishing is made of the following components by weight: 80 parts of MC90 polyoxymethylene, 2 parts of XF002-1 graphene, 15 parts of T370A polyether thermoplastic polyurethane, 1 part of antioxidant 1010, 0.5 Formaldehyde absorbent 660, formic acid absorbent calcium dodecylbenzenesulfonate 0.5 part, RLC 657 polyethylene wax lubricant 1 part.

[0043] A preparation method of the polyoxymethylene monofilament for fishing comprises the following steps:

[0044] Pre-mix polyoxymethylene, graphene, thermoplastic polyurethane, antioxidant, formaldehyde absorbent, formic acid absorbent, and lubricant, and then pour it into a high-speed kneader, kneading at a high speed at a speed of 750r / min-800r / min After 30-60 minutes, raise the temperature of the mixture in the high-speed kneader to 80°C to discharge, and obtain a polyoxymethylene modified compound;

[0045] The polyoxymethylene modified composite material is melt-spun by a twin-screw extr...

Embodiment 3

[0051] A polyoxymethylene monofilament for fishing is made of the following components by weight: 85 parts of 300PNC polyoxymethylene, 1 part of HGP-2 graphene, 11 parts of 1190A polyether thermoplastic polyurethane, 0.5 part of antioxidant 1010, 1 Formaldehyde absorbent 660, formic acid absorbent calcium dodecylbenzenesulfonate 1 part, RLC 657 polyethylene wax lubricant 0.5 part.

[0052] A preparation method of the polyoxymethylene monofilament for fishing comprises the following steps:

[0053] Pre-mix polyoxymethylene, graphene, thermoplastic polyurethane, antioxidant, formaldehyde absorbent, formic acid absorbent, and lubricant, and then pour it into a high-speed kneader, kneading at a high speed at a speed of 750r / min-800r / min After 30-60 minutes, raise the temperature of the mixture in the high-speed kneader to 80°C to discharge, and obtain a polyoxymethylene modified compound;

[0054] The polyoxymethylene modified composite material is melt-spun by a twin-screw extru...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
diameteraaaaaaaaaa
brittleness temperatureaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyoxymethylene monofilament for fishing, which is made of the following components in parts by weight: 75-90 parts of polyoxymethylene, 0.5-3 parts of graphene, 7.5-17 parts of thermoplastic polyurethane, and 0.5 parts of antioxidant 3 parts, 0.5-1 part of formaldehyde absorbent, 0.5-1 part of formic acid absorbent, 0.5-1 part of lubricant. The polyoxymethylene monofilament for fishery provided by the present invention uses graphene and thermoplastic polyurethane to blend and then strengthens and toughens the polyoxymethylene. Polyoxymethylene monofilament has the advantages of simple operation process and low production cost. The reinforced and toughened polyoxymethylene monofilament for fishery prepared by the invention can be used in polyoxymethylene rope nets, ocean-going trawls, breeding nets, polyoxymethylene ropes and the like.

Description

technical field [0001] The invention belongs to the technical field of fishery materials, and in particular relates to a polyoxymethylene monofilament for fishery and its preparation method and application. Background technique [0002] In the early days, the development of fishery benefited from the use of natural fibers, but there are many deficiencies in natural fibers. The strength cannot meet the use of some nets, and the wear resistance and weather resistance cannot meet the use of some environments. With the development of science and technology and the emergence of synthetic fibers, it makes up for the shortage of natural fibers and meets the needs of large-scale, modern and special deep-water operations in modern fishery production. Fiber, new fishery synthetic fiber materials such as polyarylate fiber, biodegradable fiber, ultra-high molecular weight polyethylene fiber and high-strength fishery polyethylene monofilament have appeared. As the country continues to d...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F8/16D01F6/94D01F1/10
CPCD01F8/16D01F6/94D01F1/10D01F1/106
Inventor 闵明华王鲁民曾毅成黄洪亮王帅杰刘永利王磊
Owner EAST CHINA SEA FISHERIES RES INST CHINESE ACAD OF FISHERY SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap