A kind of super gel material based on wet grinding process and its preparation method and application

A technology of cementitious material and wet grinding process, applied in the field of cementitious materials, can solve the problems of low effective utilization rate and high energy consumption of cement, and achieve the effect of improving early strength, high hydration degree and later strength.

Active Publication Date: 2021-09-07
WUHAN UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, the present invention aims to propose a super cementitious material based on wet grinding process to solve the problems of high energy consumption and low effective utilization rate of existing cement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of super gel material based on wet grinding process and its preparation method and application
  • A kind of super gel material based on wet grinding process and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] It should be noted that, in the case of no conflict, the embodiments of the present invention and the features in the embodiments can be combined with each other.

[0024] The present invention will be described in detail below in conjunction with examples.

[0025] Table 1 is the proportion of each component in the supergelled material based on the wet milling process of Examples 1 to 5 of the present invention and the fineness and wet milling parameters of the supergelled material based on the wet milled process in each embodiment, Wherein, the cement in the supercementitious material based on the wet grinding process of embodiments 1 to 5 is P.O 42.5 grade, and the median particle size of the cement is 15.1 μm; the stabilizer is a temperature wheel with a mass concentration of 0.1%. glue.

[0026] Table 1

[0027]

[0028] Table 2 shows the ratio of each component in the surface modifier in Examples 1 to 5 of the present invention. Wherein, the consumption of p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a super-gelled material based on a wet grinding process and its preparation method and application. The super-gelled material based on a wet-milled process consists of 28% to 60% cement, 1% to 3% Surface modifying agent, 0.1-0.2% stabilizer and 37%-70% water are prepared through wet grinding process. The super-cemented material based on the wet grinding process of the present invention uses ordinary Portland cement as the main raw material, and is processed through the wet grinding process, and in the wet grinding process, a surface modifier and a stabilizer are added to obtain a median particle size of 2-5μm super-cemented material, because after the wet grinding process, the whole system is in a "pre-hydration" state, and due to the finer particle size, the super-cemented material of the present invention has higher hydration than the original cement degree and extremely high activity, when part of the cement is replaced, the early strength can be significantly improved, and the gradation can be optimized, so that the later strength can also be improved to a certain extent. Among them, the 12h strength increase ratio can reach 142%.

Description

technical field [0001] The invention relates to the technical field of gelling materials, in particular to a super-gelling material based on a wet grinding process and its preparation method and application. Background technique [0002] Concrete generally requires good construction performance. If no water reducing agent is added, the water ash is relatively large, which is generally greater than the water required for complete hydration of cement. However, with the hydration of cement and the continuous evaporation of free water, the concrete will There are still some unhydrated cement particles. If high-efficiency water reducer is added, the water-cement ratio of concrete will be greatly reduced, the degree of hydration of cement will be reduced, and the hydration will be even more insufficient. At present, the fineness of ordinary cement in my country is generally relatively large, and its specific surface area is more than 300m 2 / kg or so, the 28d hydration degree is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B7/52C04B24/32C04B103/52
CPCC04B7/52C04B40/0039C04B2103/52C04B24/04C04B24/32C04B24/16C04B22/14
Inventor 谭洪波张迅邓秀峰李懋高聂康峻贺行洋苏英
Owner WUHAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products