Biodegradable product and preparation method thereof

A biodegradable and biodegradable resin technology, applied in the field of biodegradable products and their preparation, can solve the problems of high cost and difficulty in popularization of fully biodegradable garbage bags, and achieve the effect of reducing environmental pressure and cost

Inactive Publication Date: 2019-11-01
SHANGHAI CHANGFA NEW MATERIAL CO LTD
View PDF4 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

This patented technology combines different materials together with paper making waste into one type that can be easily broken down by bacteria or other organisms without causing environmental concerns such as pollution from chemicals used during production processes.

Problems solved by technology

This patented technical problem addressed in this patents relates to finding ways to reduce environmental concerns caused by disposing of harmful chemical substances such as pesticides (pesticides) during production processes without causing negative side effects on human health.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] A biodegradable product of this embodiment consists of the following raw materials in parts by weight:

[0074] 60 parts of poly (butyleneadipate-co-terephthalate), PBAT, 10 parts of polylactic acid (PLA), 15 parts of papermaking waste, 12 parts of corn starch, carbonic acid 3 parts of calcium, 1 part of dicumyl peroxide (DCP), 6 parts of epoxidized soybean oil, and 1 part of calcium stearate.

[0075] The preparation method of the biodegradable product of the present embodiment is as follows:

[0076] Step 1, drying, crushing and sieving the papermaking waste to obtain papermaking waste of 500-2000 mesh;

[0077]Add 60 parts of PBAT, 10 parts of PLA, 15 parts of papermaking waste, 12 parts of corn starch, 3 parts of calcium carbonate, 1 part of DCP, 6 parts of epoxidized soybean oil and 1 part of calcium stearate into the high-speed blender, Mix for 100 minutes at a temperature of 100°C and a rotation speed of 500 rpm to obtain an initial mixture;

[0078] Step 2. A...

Embodiment 2

[0082] A biodegradable product of this embodiment consists of the following raw materials in parts by weight:

[0083] 60 parts of polybutylene adipate / terephthalate (PBAT), 10 parts of polylactic acid (PLA), 15 parts of papermaking waste, 15 parts of corn starch, 1 part of dicumyl peroxide (DCP), cyclic Oxygenated soybean oil 6 parts, calcium stearate 1 part.

[0084] The preparation method of the biodegradable product of the present embodiment is as follows:

[0085] Step 1, drying, crushing and sieving the papermaking waste to obtain papermaking waste of 50 to 5000 mesh;

[0086] Add 60 parts of PBAT, 10 parts of PLA, 15 parts of paper waste, 15 parts of corn starch, 1 part of DCP, 6 parts of epoxidized soybean oil and 1 part of calcium stearate into the high-speed blender at a temperature of 120 ° C 1. Under the condition of rotating speed 600rpm, mix for 300min to obtain the primary mixture;

[0087] Step 2. Add the primary mixture to the twin-screw extruder to extrude...

Embodiment 3

[0091] A biodegradable product of this embodiment consists of the following raw materials in parts by weight:

[0092] 60 parts of polybutylene adipate / terephthalate (PBAT), 10 parts of polylactic acid (PLA), 27 parts of papermaking waste, 3 parts of talcum powder, 1 part of dicumyl peroxide (DCP), glycerin 6 parts, 1 part of calcium stearate.

[0093] The preparation method of the biodegradable product of the present embodiment is as follows:

[0094] Step 1, drying, crushing and sieving the papermaking waste to obtain papermaking waste of 50 to 5000 mesh;

[0095] Add 60 parts of PBAT, 10 parts of PLA, 27 parts of papermaking waste, 3 parts of talc, 1 part of DCP, 6 parts of glycerin and 1 part of calcium stearate into the high-speed blender at a temperature of 50 °C and a speed of 200 rpm Under the condition of mixing for 30min, the primary mixture was obtained;

[0096] Step 2. Add the primary mixture to the twin-screw extruder to extrude and granulate. The temperatures...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a biodegradable product. The biodegradable product is composed of the following components in parts by weight: 40 to 90 parts of biodegradable resin, 5 to 50 parts of papermaking wastes, 0 to 40 parts of starch, 0 to 5 parts of an inorganic mineral substance and 2 to 15 parts of an auxiliary agent. The invention also relates to a preparation method for the biodegradable product. The biodegradable product provided by the invention has the following advantages: the paper wastes, the starch, the inorganic mineral substance and the biodegradable resin are compounded, so the cost of the biodegradable product is greatly reduced; and the papermaking wastes are effectively utilized, so the pressure on the environment is reduced.

Description

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Owner SHANGHAI CHANGFA NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap