Conjugated polymer with AIE properties and preparation method thereof

A technology of conjugated polymers and properties, applied in the field of conjugated polymers and their preparation, can solve the problems of poor polymer solubility, expensive experimental conditions, difficult processing, etc., achieve cheap film thickness, simple preparation, and good application prospects Effect

Inactive Publication Date: 2019-12-27
JIANGXI SCI & TECH NORMAL UNIV
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most of the polymers obtained by chemical polymerization have poor solubility, are difficult to process, and require expensive catalysts and harsh experimental conditions, which limit their application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Conjugated polymer with AIE properties and preparation method thereof
  • Conjugated polymer with AIE properties and preparation method thereof
  • Conjugated polymer with AIE properties and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A conjugated polymer with AIE properties, the name of the conjugated polymer is poly(1,1,2,2-(tetra(4-9 hydrogen-carbazole)phenyl)ethylene) (PTCPE), Its chemical structural formula is as follows:

[0021]

[0022] A kind of preparation method of the above-mentioned conjugated polymer with AIE property, comprises the following steps:

[0023] (1) Determination of oxidation potential:

[0024] The working system is a three-electrode system, the Ag / AgCl electrode is the reference electrode, the platinum wire is the counter electrode, and the other platinum wire is the working electrode. The 0.4mmol / L TCPE monomer was studied in CH containing BFEE volume fraction 0%, 10%, 20%. 2 Cl 2 LSV in solution. When there is no electrolyte, TCPE in pure CH 2 Cl 2 It cannot be oxidized in solution (LSV is a straight line); when adding 10% and 20% BFEE, the oxidation onset potentials of TCPE are 0.60V and 0.54V, respectively. Obviously, after the introduction of BFEE, TCPE can...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a conjugated polymer with AIE properties and a preparation method thereof. The invention belongs to the technical field of AIE material preparation and performance research. According to the invention, a PVDF membrane is modified by adopting a blending method; then the PVDF membrane is prepared by copolymerization of alkali-treated PVDF and a sulfydryl polymer with zwitterions, wherein the zwitterionic polymer contains sulfydryl and can generate a sulfydryl-alkenyl click reaction with double bonds of the alkali-treated PVDF, so that the amphoteric polymer can stably exist on the membrane. Zwitterions are introduced into PVDF, so that the hydrophilicity, pollution resistance and the like of the PVDF membrane are greatly improved, and the PVDF membrane has a good application prospect.

Description

technical field [0001] The invention belongs to the technical field of preparation and performance research of AIE materials, and in particular relates to a conjugated polymer with AIE properties and a preparation method thereof. Background technique [0002] Organic solid fluorescent materials have a wide range of applications in light-emitting devices, data recording and storage, sensors and other fields, thus attracting more and more people's attention. Among them, fluorescent materials based on conjugated polymers have a fluorescent signal amplification effect and are easy to form films, showing excellent performance in these application fields. In devices, organic solid fluorescent materials are often in the form of crystals or thin films. However, in the aggregated state of fluorescent molecules, due to the π-π overlap between molecules, the intensified dipole-dipole interaction between molecules causes the fluorescence quenching problem in the aggregated state. This ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G61/12C25B3/10C09K11/06C25B3/29
CPCC08G61/124C09K11/06C08G2261/3241C08G2261/44C08G2261/18C08G2261/522C09K2211/1466C09K2211/1425C25B3/29
Inventor 张革徐景坤张新新柴晶党邹列辛星刘芳李斐
Owner JIANGXI SCI & TECH NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap