Water-absorbing composite silk fabric and processing method thereof

A processing method and fabric technology, applied in the field of textile weaving, can solve the problem that silk cannot absorb water, etc., and achieve the effect of improving water absorption

Active Publication Date: 2020-01-07
乐清市华尊电气有限公司
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, silk cannot absorb a large amount of moisture, so it ...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A water-absorbing composite silk fabric mainly includes the following raw material components in parts by weight: 32 parts of spidroin, 6 parts of dextran, 8 parts of chitosan and 30 parts of modified silk fiber.

[0034] A method for processing a water-absorbent composite silk fabric, the method for processing a water-absorbent composite silk fabric mainly includes the following preparation steps:

[0035](1) Mix waste cocoons and isopropyl ether at a mass ratio of 1:6, soak at room temperature for 4 hours, and filter to obtain pretreated waste cocoons. Mix pretreated waste cocoons with absolute ethanol at a mass ratio of 1:5 After soaking for 3 hours, filter to obtain filter residue, mix the filter residue and deionized water at a mass ratio of 1:5, heat the mixture of filter residue and deionized water to boiling, and filter at a constant temperature for 6 hours to obtain fibrous silk protein. Silk fibroin is mixed with sodium hydrosulfide solution with a mass fracti...

Embodiment 2

[0045] A water-absorbing composite silk fabric mainly includes the following raw material components in parts by weight: 32 parts of spidroin, 6 parts of dextran and 30 parts of modified silk fiber.

[0046] A method for processing a water-absorbent composite silk fabric, the method for processing a water-absorbent composite silk fabric mainly includes the following preparation steps:

[0047] (1) Mix waste cocoons and isopropyl ether at a mass ratio of 1:6, soak at room temperature for 4 hours, and filter to obtain pretreated waste cocoons. Mix pretreated waste cocoons with absolute ethanol at a mass ratio of 1:5 After soaking for 3 hours, filter to obtain filter residue, mix the filter residue and deionized water at a mass ratio of 1:5, heat the mixture of filter residue and deionized water to boiling, and filter at a constant temperature for 6 hours to obtain fibrous silk protein. Silk fibroin is mixed with sodium hydrosulfide solution with a mass fraction of 60%, and after...

Embodiment 3

[0057] A water-absorbing composite silk fabric mainly includes the following raw material components in parts by weight: 32 parts of spidroin, 6 parts of dextran, 8 parts of chitosan and 30 parts of silk fiber.

[0058] A method for processing a water-absorbent composite silk fabric, the method for processing a water-absorbent composite silk fabric mainly includes the following preparation steps:

[0059] (1) Mix spider silk and hexafluoroisopropanol at a mass ratio of 1:10, and add dextran 0.2 times the mass of spider silk to the mixture of spider silk and hexafluoroisopropanol, at a temperature of 30°C, The rotating speed is 300r / min under the condition of stirring and mixing for 30min to obtain the modified spider silk fiber spinning liquid, after the modified spider silk fiber spinning liquid is subjected to electrospinning, the modified spider silk fiber fibrils are obtained, and the modified spider silk fiber The spider silk fiber fibrils are twisted to a linear density ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of weaving of textiles and discloses a water-absorbing composite silk fabric and a processing method thereof. The method includes steps: subjecting modified polyethylene glycol to mixed reaction with fibroin; spinning and twisting to obtain modified silk fibers; mixing spider silk protein liquid with glucan; spinning and twisting to obtain modified spider silk fibers; blending the obtained modified silk fibers with the modified spider silk fibers to obtain a water-absorbing composite silk gray fabric; subjecting the water-absorbing composite silk gray fabricto mixed reaction with protease solution, performing high-temperature enzyme deactivation, adding chitosan mixed liquid, filtering after stirring reaction, and performing freeze drying to obtain the water-absorbing composite silk fabric. The water-absorbing composite silk fabric prepared according to the method is excellent in water absorbing performance and great in drapability.

Description

technical field [0001] The invention relates to the field of textile weaving, in particular to a water-absorbing composite silk fabric and a processing method thereof. Background technique [0002] Silk is woven from silk fiber as a raw material. Silk fiber is a kind of protein fiber, known as the "fiber queen" and the "national treasure" of our country. Silk fibroin in silk contains 18 kinds of amino acids that are of great nutritional value to the human body, so silk fabrics have a good affinity for human skin, and it has the reputation of "human second skin". The cross-section of silk fiber is triangular, the longitudinal direction is smooth and flat, and it has a layered structure, which makes it have better luster than other fibers. The silk fineness is finer and its moisture absorption capacity is better. In addition, silk also has a strong anti-ultraviolet function and a silky sound that other fibers do not have. The characteristics of silk fiber endow silk fabrics ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06M16/00D06M15/03D03D15/00D03D13/00D01F4/02D01F4/00D01F1/10C08H1/00D06M101/10
CPCD03D15/00D03D13/008D01F4/00D01F1/10D06M16/003D06M15/03D06M2101/10D06B3/10D01D5/003D01D5/0092D01D5/0061D01D5/0069D10B2211/22
Inventor 夏志忠
Owner 乐清市华尊电气有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap