A technology of non-woven fabrics and spunlace non-woven fabrics, which is applied in the direction of melt spinning, non-woven fabrics, and rayon manufacturing, and can solve the problem of poor mechanical properties such as breaking strength of antibacterial non-woven fabrics, loss of antibacterial effect, and application range Restricted problems, to achieve excellent antibacterial performance, good antibacterial effect, high bonding strength

Active Publication Date: 2020-01-10
FUJIAN GUAN HONG IND
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] 1. The antibacterial effect is poor, and the extensive use of antibacterial fillers leads to poor mechanical properties such as the breaking strength of the prepared antibacterial non-woven fabric, and the scope of application is limited;
[0015] 2. The surface is impregnated with antibacterial agent, or the added small molecule antibacterial agent is easy to seep out and dissolve in solvent or water, which will easily weaken the antibacterial effect or even lose the antibacterial effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Antibacterial non-woven fabric and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A kind of antibacterial nonwoven fabric, described antibacterial nonwoven fabric is made by composite fiber through spunlace nonwoven fabric production process;

[0052] The composite fiber has a skin-core structure, including a core layer and a skin layer; the cross-sectional profile of the core layer is a regular pentagon, the skin layer is wrapped on the outer surface of the core layer, and the cross-sectional profile of the skin layer is a circle shape; the ratio of the cross-sectional area of ​​the core layer and the cortex is 1: (0.28~0.35);

[0053] The core layer is made of the following raw materials in parts by weight: 95-100 parts of polyethylene terephthalate, 2-5 parts of hydroxyl-terminated polysiloxane emulsion, 2-3.5 parts of pentaerythritol adipate, 10-15 parts of filler;

[0054] The skin layer is made of the following raw materials in parts by weight: 55-65 parts of polyethylene terephthalate, 30-35 parts of polyether polyurethane elastomer, 10 parts...

Embodiment 2

[0077] A kind of antibacterial nonwoven fabric, described antibacterial nonwoven fabric is made by composite fiber through spunlace nonwoven fabric production process;

[0078] The composite fiber has a skin-core structure, including a core layer and a skin layer; the cross-sectional profile of the core layer is a regular pentagon, the skin layer is wrapped on the outer surface of the core layer, and the cross-sectional profile of the skin layer is a circle shape; the ratio of the cross-sectional area of ​​the core layer and the skin layer is 1:0.28;

[0079] The core layer is made of the following raw materials in parts by weight: 95 parts of polyethylene terephthalate, 2 parts of hydroxyl-terminated polysiloxane emulsion, 2 parts of pentaerythritol adipate, and 10 parts of filler;

[0080] The skin layer is made of the following raw materials in parts by weight: 55 parts of polyethylene terephthalate, 30 parts of polyether polyurethane elastomer, 10 parts of maleic anhydride...

Embodiment 3

[0099] A kind of antibacterial nonwoven fabric, described antibacterial nonwoven fabric is made by composite fiber through spunlace nonwoven fabric production process;

[0100] The composite fiber has a skin-core structure, including a core layer and a skin layer; the cross-sectional profile of the core layer is a regular pentagon, the skin layer is wrapped on the outer surface of the core layer, and the cross-sectional profile of the skin layer is a circle shape; the ratio of the cross-sectional area of ​​the core layer and the skin layer is 1:0.35;

[0101] The core layer is made of the following raw materials in parts by weight: 100 parts of polyethylene terephthalate, 5 parts of hydroxyl-terminated polysiloxane emulsion, 3.5 parts of pentaerythritol adipate, and 15 parts of filler;

[0102] The skin layer is made of the following raw materials in parts by weight: 65 parts of polyethylene terephthalate, 35 parts of polyether polyurethane elastomer, 13 parts of maleic anhydr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
degree of graftingaaaaaaaaaa
degree of graftingaaaaaaaaaa
degree of graftingaaaaaaaaaa
Login to view more

Abstract

The invention discloses an antibacterial non-woven fabric and a manufacturing process thereof. The antibacterial non-woven fabric is prepared from composite fibers through a spunlace non-woven fabricproduction process; the composite fibers have a skin-core structure and comprises a core layer and a skin layer; the cross section outline of the core layer is regular pentagon, the skin layer wraps the outer surface of the core layer, and the cross section outline of the skin layer is circular; the cross section area ratio of the core layer to the skin layer is 1: (0.28-0.35); and the core layeris prepared from the following raw materials in parts by weight: 95-100 parts of polyethylene terephthalate, 2-5 parts of hydroxyl-terminated polysiloxane emulsion, 2-3.5 parts of pentaerythritol adipate and 10-15 parts of filler. The antibacterial non-woven fabric is excellent in antibacterial performance and good in antibacterial effect; the fracture strength is high, and the mechanical propertyis good; and furthermore, the antibacterial non-woven fabric has good elasticity and softness.

Description

technical field [0001] The invention relates to the technical field of non-woven fabrics, in particular to an antibacterial non-woven fabric and a manufacturing process thereof. Background technique [0002] The fibers used in the production of non-woven fabrics are mainly polypropylene (PP) and polyester (PET). In addition, there are nylon (PA), viscose fiber, acrylic fiber, polyethylene fiber (HDPE), and chlorine fiber (PVC). According to application requirements, non-woven fabrics are divided into two categories: disposable application type and durable type. [0003] According to the production process, it is divided into: [0004] 1. Spunlace non-woven fabric: The spunlace process is to spray high-pressure fine water flow onto one or more layers of fiber nets, so that the fibers are entangled with each other, so that the fiber nets can be reinforced and have a certain strength. [0005] 2. Heat-bonded non-woven fabric: heat-bonded non-woven fabric refers to adding fib...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H1/4382D04H1/492D01D5/098D01D5/34D01F1/10D01F8/14D01F8/16
CPCD04H1/492D04H1/4382D01D5/34D01D5/098D01F8/14D01F8/16D01F1/10D01F1/103D10B2401/13
Inventor 陈解忧黄冠儒张洛泓
Owner FUJIAN GUAN HONG IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap