Ultra-thick coating hot galvanized steel strip for underground pipe gallery corrugated pipe and production method thereof

A technology of underground pipe gallery and production method, which is applied in the direction of coating, hot-dip plating process, metal material coating process, etc., and can solve the problems of high core heat energy of thick steel strip, low air knife injection pressure, and slow production speed, etc. problems, to achieve the effect of suppressing zinc flow lines and edge thickness defects, increasing the air flow at the edge, and reducing the edge thickness of the coating

Active Publication Date: 2020-01-14
TANGSHAN IRON & STEEL GROUP +1
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When producing thick-gauge and thick-coated galvanized steel strips, due to the slow production speed and low air knife injection pressure, and the core heat energy of thick-gauge steel strips is high, defects such as zinc flow marks and edge thickness are prone to occur, especially 600g / m 2 (Double-sided) ultra-thick galvanized layer, the limit for galvanized line design

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultra-thick coating hot galvanized steel strip for underground pipe gallery corrugated pipe and production method thereof
  • Ultra-thick coating hot galvanized steel strip for underground pipe gallery corrugated pipe and production method thereof
  • Ultra-thick coating hot galvanized steel strip for underground pipe gallery corrugated pipe and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The specifications of the ultra-thick coated hot-dip galvanized steel strip for the bellows of the underground pipe gallery in this embodiment are: thickness 1.6mm, width 1396mm, and its chemical composition and mass percentage are shown in Table 1.

[0026] The production method of the ultra-thick coated hot-dip galvanized steel strip for the corrugated pipe of the underground pipe gallery in this embodiment includes converter smelting, LF refining, continuous casting, hot rolling, cold rolling and galvanizing processes, and the specific process steps are as follows:

[0027] (1) LF refining process: After smelting, the molten steel enters LF refining, and the refined molten steel C: 0.045%, Mn: 0.17%;

[0028] (2) Hot rolling process: the heating temperature is 1230°C, the final rolling temperature is 892°C, and the crimping temperature is 660°C;

[0029] (3) Cold rolling process: the hot-rolled strip is cold-rolled after pickling, the total reduction rate of cold-rol...

Embodiment 2

[0033] The specifications of the ultra-thick coated hot-dip galvanized steel strip for the bellows of the underground pipe gallery in this embodiment are: thickness 1.6mm, width 1396mm, and its chemical composition and mass percentage are shown in Table 1.

[0034] The production method of the ultra-thick coated hot-dip galvanized steel strip for the corrugated pipe of the underground pipe gallery in this embodiment includes converter smelting, LF refining, continuous casting, hot rolling, cold rolling and galvanizing processes, and the specific process steps are as follows:

[0035] (1) LF refining process: After smelting, molten steel enters LF refining, and the refined molten steel C: 0.045%, Mn: 0.25%;

[0036] (2) Hot rolling process: the heating temperature is 1235°C, the final rolling temperature is 890°C, and the crimping temperature is 662°C;

[0037] (3) Cold rolling process: the hot-rolled strip is cold-rolled after pickling, the total reduction rate of cold-rolling...

Embodiment 3

[0041] The specifications of the ultra-thick coated hot-dip galvanized steel strip for the bellows of the underground pipe gallery in this embodiment are: thickness 1.3mm, width 1250mm, and its chemical composition and mass percentage are shown in Table 1.

[0042] The production method of the ultra-thick coated hot-dip galvanized steel strip for the corrugated pipe of the underground pipe gallery in this embodiment includes converter smelting, LF refining, continuous casting, hot rolling, cold rolling and galvanizing processes, and the specific process steps are as follows:

[0043](1) LF refining process: After smelting, the molten steel enters LF refining, and the refined molten steel C: 0.050%, Mn: 0.20%;

[0044] (2) Hot rolling process: the heating temperature is 1240°C, the final rolling temperature is 895°C, and the crimping temperature is 656°C;

[0045] (3) Cold rolling process: the hot-rolled strip is cold-rolled after pickling, the total reduction rate of cold-roll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an ultra-thick coating hot galvanized steel strip for an underground pipe gallery corrugated pipe and a production method thereof. The hot galvanized steel strip comprises thefollowing chemical components of, in percentage by mass, 0.045%-0.065% of C, 0.15%-0.25% of Mn, less than or equal to 0.020% of S, less than or equal to 0.020% of P, less than or equal to 0.03% of Si,greater than or equal to 0.020% of Als, and balance iron and inevitable impurities; the production method comprises converter smelting, LF refining, continuous casting , hot rolling, cold rolling andgalvanizing processes. According to the ultra-thick coating hot galvanized steel strip for the underground pipe gallery corrugated pipe and the production method thereof, proper mechanical propertiesof the steel strip are guaranteed through reasonable component design and hot rolling and galvanizing annealing process design; and through reducing the height of an air knife, increasing the distance between a knife lip and the strip steel and sectional control measures of the opening degree of the air knife lip, the generation of zinc rhyolite and edge thickness defects is inhibited, the requirement of the underground pipe gallery industry on the ultra-thick coating hot galvanized steel strip is met, and remarkable economic benefits are achieved.

Description

technical field [0001] The invention belongs to the technical field of hot-dip galvanized steel strip production, and in particular relates to an ultra-thick coated hot-dip galvanized steel strip for corrugated pipes of an underground pipe gallery and a production method thereof. Background technique [0002] Compared with the traditional reinforced concrete form, the corrugated pipe of the underground pipe gallery has the advantages of high strength, good flexibility, light weight, convenient construction, strong seismic and deformation resistance, and more environmental protection. With the development of galvanizing technology, it has a certain strength. The ultra-thick coated hot-dip galvanized steel strip becomes the ideal material for the corrugated pipe of the underground pipe gallery. [0003] The corrugated pipe of the underground pipe gallery requires sufficient strength and rigidity, and the service life is greater than 100 years. The galvanized steel strip curren...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/06C22C38/04C22C38/02C23C2/06C23C2/40C23C2/20C21D8/02
CPCC21D8/0205C21D8/0247C22C38/002C22C38/02C22C38/04C22C38/06C23C2/06C23C2/20C23C2/40
Inventor 梅淑文杨青宋志岗孙恺王力达张健吴旻王超弓俊杰
Owner TANGSHAN IRON & STEEL GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap