Polyurethane self-skinning cushion water-based coating and polyurethane self-skinning cushion

A water-based coating and self-skinning technology, which is applied in the field of polyurethane self-skinning cushions and water-based coatings for polyurethane self-skinning cushions, can solve the problems of polyurethane self-skinning cushions not up to standard, etc. Rubbing color fastness, the effect of wide application prospects

Active Publication Date: 2020-04-28
鹤山市鹤威科技发展有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved in the present invention is to overcome the defect of the existing coating production process and the deficiency that the quality of the polyurethane self-skinning cushion produced by the traditional technology is not up to standard, and provide the water-based coating of the polyurethane self-skinning cushion and the polyurethane self-skinning cushion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyurethane self-skinning cushion water-based coating and polyurethane self-skinning cushion
  • Polyurethane self-skinning cushion water-based coating and polyurethane self-skinning cushion
  • Polyurethane self-skinning cushion water-based coating and polyurethane self-skinning cushion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] The preparation of embodiment 1 polyurethane self-skinning cushion

[0058] A polyurethane self-skinning cushion water-based coating, in parts by mass, comprising the following components: 75 parts of water-emulsifiable bisphenol A type epoxy resin, 13 parts of hyperbranched polyethyleneimine, 12.5 parts of water-based polyurethane prepolymer ;

[0059] Among them, the epoxy equivalent of the water-emulsifiable bisphenol A type epoxy resin is 180g·mol -1 ; The molecular weight of hyperbranched polyethyleneimine is 10600; the solid content of waterborne polyurethane prepolymer is 30%, and its end group is isocyanate group;

[0060] The preparation method of described polyurethane self-crusting cushion water-based coating, comprises the following steps:

[0061] S1. After mixing the water-based epoxy resin and hyperbranched polyethyleneimine according to the above mass parts, add water at 80°C and stir for 35 minutes;

[0062] S2. Add water-based polyurethane prepolyme...

Embodiment 2

[0067] The preparation of embodiment 2 polyurethane self-skinning cushion

[0068] A polyurethane self-skinned cushion water-based coating, in parts by mass, comprising the following components: 66 parts of glycerol triglycidyl ether, 17 parts of hyperbranched polyethyleneimine, 20 parts of water-based polyurethane prepolymer;

[0069] Among them, the epoxy equivalent of glycerol triglycidyl ether is 141g·mol -1 ; The molecular weight of hyperbranched polyethyleneimine is 1200; the solid content of water-based polyurethane prepolymer is 15%, and its terminal group is isocyanate group;

[0070] The preparation method of described polyurethane self-crusting cushion water-based coating, comprises the following steps:

[0071] S1. After mixing the water-based epoxy resin and hyperbranched polyethyleneimine according to the above mass parts, add water at 75°C and stir for 360 minutes;

[0072] S2. Add water-based polyurethane prepolymer to the reaction system of step S1 while sti...

Embodiment 3

[0077] The preparation of embodiment 3 polyurethane from crust cushion

[0078] A polyurethane self-skinned cushion water-based coating, in parts by mass, comprising the following components: 84 parts of propylene glycol diglycidyl ether, 9 parts of hyperbranched polyethyleneimine, and 5 parts of water-based polyurethane prepolymer;

[0079] Among them, the epoxy equivalent of propylene glycol diglycidyl ether is 220g·mol -1 ; The molecular weight of hyperbranched polyethyleneimine is 20000; The solid content of waterborne polyurethane prepolymer is 45%, and its end group is isocyanate group;

[0080] The preparation method of described polyurethane self-crusting cushion water-based coating, comprises the following steps:

[0081] S1. After mixing the water-based epoxy resin and hyperbranched polyethyleneimine according to the above mass parts, add water at 85°C and stir for 30 minutes;

[0082] S2. Add the water-based polyurethane prepolymer at 85° C. for 1 hour while stirr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyurethane self-skinning cushion water-based coating and a polyurethane self-skinning cushion. The coating is prepared from the following components in parts by mass: 66 to84 parts of water-based epoxy resin, 9 to 17 parts of hyperbranched polyethyleneimine and 5 to 20 parts of a water-based polyurethane prepolymer. The water-based coating has good adhesive force and flexibility and good color fastness to rubbing, reagent resistance, low temperature resistance and high temperature resistance, and the preparation method of the water-based coating has the advantagesof no toxicity, no pollution and no residue and has a wide application prospect in preparation of the polyurethane self-skinning cushion. The invention further provides a method for preparing the polyurethane self-skinning cushion by using the water-based coating, and the cushion prepared by the method has good wear resistance, antifouling property, chemical resistance, cleaning agent resistance and aging resistance, and can be produced on a large scale and widely used.

Description

technical field [0001] The invention belongs to the technical field of coating preparation. More specifically, it relates to a polyurethane self-skinning cushion water-based coating and a polyurethane self-skinning cushion. Background technique [0002] With the development of technology, polyurethane materials are widely used in the fields of coatings, adhesives, foam plastics, synthetic fibers and their elastomers, and have achieved diversified production, enriching people's lives. In recent years, the domestic furniture industry has developed rapidly, and the demand for high-end products has increased sharply. In order to improve the comfort of people's lives, office chairs, bar chairs and seats in public places (hospitals, high-speed rail stations and airports, etc.) are also more expensive. Many use polyurethane self-skinning materials. [0003] The traditional technology of producing polyurethane self-skinning cushions usually adopts the method of spraying paint film...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/42C08G18/58C08G18/64C08G18/34C08G18/12C09D175/06C08J9/36C08L75/04
CPCC08G18/12C08G18/348C08G18/4081C08G18/4238C08G18/58C08G18/6423C08G18/6659C08J9/365C08J2375/04C08J2475/08C09D175/06C08G18/40
Inventor 李兆荣
Owner 鹤山市鹤威科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap