Low-shrinkage HIPS composite material for solving abnormal sound, and preparation method thereof

A composite material, low shrinkage technology, applied in the field of polymer materials, can solve the problems of poor dimensional stability, large shrinkage rate changes, easy deformation of parts, etc., and achieve the effect of low linear expansion coefficient, improved mechanical properties, and reduced noise sources.

Pending Publication Date: 2020-05-15
合肥圆融新材料有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] High-impact polystyrene (HIPS) material is a two-phase system polymer composed of elastomeric rubber and continuous styrene rubber. Because of its low price, excellent processing performance and mechanical properties, HIPS is widely used in various household appliances. However, the shrinkage rate of HIPS changes greatly in the alternating cold and hot environment, the parts are easy to deform, and the dimensional stability is poor, which seriously limits its application range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Low-shrinkage HIPS composite material for solving abnormal sound, and preparation method thereof
  • Low-shrinkage HIPS composite material for solving abnormal sound, and preparation method thereof
  • Low-shrinkage HIPS composite material for solving abnormal sound, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A low-shrinkage HIPS composite material for solving abnormal noise, including the following raw materials in parts by weight: 60 parts of HIPS resin, 3 parts of rubber composite material, 8 parts of reinforcing agent, 3 parts of barrier agent, 0.3 part of weather resistance agent, and 0.1 part of antioxidant , 0.1 part of lubricant.

[0030] The preparation method of the low-shrinkage HIPS composite material for solving abnormal sound comprises the following steps:

[0031] S1. Premix HIPS resin, rubber composite material, barrier agent, weather resistance agent, antioxidant and lubricant for 8 minutes to obtain a mixture;

[0032] S2. Add the compound described in step S1 into the twin-screw extruder from the main feeding port, and add the reinforcing agent into the twin-screw extruder from the side feeding port to melt, knead and extrude to obtain the solution to the abnormal sound. Low Shrinkage HIPS Composite.

[0033] Wherein, the rubber composite material compri...

Embodiment 2

[0036] A low-shrinkage HIPS composite material for solving abnormal noise, including the following raw materials in parts by weight: 80 parts of HIPS resin, 10 parts of rubber composite material, 10 parts of reinforcing agent, 10 parts of barrier agent, 1.5 parts of weather resistance agent, and 0.6 parts of antioxidant , 0.6 part of lubricant.

[0037] The preparation method of the low-shrinkage HIPS composite material for solving abnormal sound comprises the following steps:

[0038]S1. Premixing HIPS resin, rubber composite material, barrier agent, weather resistance agent, antioxidant and lubricant for 15 minutes to obtain a mixture;

[0039] S2. Add the compound described in step S1 into the twin-screw extruder from the main feeding port, and add the reinforcing agent into the twin-screw extruder from the side feeding port to melt, knead and extrude to obtain the solution to the abnormal sound. Low Shrinkage HIPS Composite.

[0040] Among them, the rubber composite mate...

Embodiment 3

[0043] A low-shrinkage HIPS composite material for solving abnormal noise, including the following raw materials in parts by weight: 78 parts of HIPS resin, 7 parts of rubber composite material, 10 parts of reinforcing agent, 5 parts of barrier agent, 0.5 part of weather resistance agent, and 0.3 part of antioxidant , 0.5 part of lubricant.

[0044] The preparation method of the low-shrinkage HIPS composite material for solving abnormal sound comprises the following steps:

[0045] S1. Premix HIPS resin, rubber composite material, barrier agent, weather resistance agent, antioxidant, and lubricant for 10 minutes to obtain a mixture;

[0046] S2. Add the compound described in step S1 into the twin-screw extruder from the main feeding port, and add the reinforcing agent into the twin-screw extruder from the side feeding port to melt, knead and extrude to obtain the solution to the abnormal sound. Low Shrinkage HIPS Composite.

[0047] Among them, the rubber composite material ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a low-shrinkage HIPS composite material for solving abnormal sound, and a preparation method thereof. The material comprises, by weight, 60-80 parts of HIPS resin, 3-10 parts of a rubber composite material, 8-20 parts of a reinforcing agent, 3-10 parts of a blocking agent, 0.3-1.5 parts of a weather-proof agent, 0.1-0.6 part of an antioxidant and 0.1-0.6 part of a lubricant. The material not only has excellent strength, toughness and dimensional stability, but also can play a role in vibration and noise reduction, can solve the common abnormal sound problem of current household appliances and improve the living environment of people, and is low in comprehensive cost and wide in application range.

Description

technical field [0001] The invention relates to the technical field of polymer materials, in particular to a low-shrinkage HIPS composite material for solving abnormal noise and a preparation method thereof. Background technique [0002] High-impact polystyrene (HIPS) material is a two-phase system polymer composed of elastomeric rubber and continuous styrene rubber. Because of its low price, excellent processing performance and mechanical properties, HIPS is widely used in various household appliances. However, the shrinkage rate of HIPS changes greatly in the alternating cold and hot environment, the parts are easy to deform, and the dimensional stability is poor, which seriously limits its application range. [0003] Air-conditioning products cause noise pollution due to size changes, vibration and resonance of different parts of the product when they alternate between hot and cold. Noise pollution has become a contemporary worldwide problem and is endangering people's ph...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L51/04C08L23/22C08L83/04C08L9/02C08L53/02C08K13/04C08K7/14C08K3/30C08K3/34C08K5/3475C08K5/20C08K7/26C08K5/12C08K5/13C08K13/06C08K9/06C08K9/04
CPCC08L51/04C08K2201/003C08K2201/004C08K2003/3045C08K2201/014C08L23/22C08L83/04C08K13/04C08K7/14C08K3/30C08K5/3475C08K5/20C08L9/02C08K3/34C08K7/26C08K5/12C08K5/13C08L53/02C08K13/06C08K9/06C08K9/04
Inventor 杨亚娣邢纪普吴摞李荣群
Owner 合肥圆融新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap