A kind of preparation method of modified tourmaline powder

A technology of tourmaline powder and tourmaline, which is applied in the field of preparation of modified tourmaline powder, can solve the problems such as the performance of tourmaline has not been achieved yet, and the performance of tourmaline has not been exerted accurately and effectively, and the dipole moment is increased, the pyroelectric performance is enhanced, Enhance the effect of radiation

Active Publication Date: 2022-02-18
大连明盛生物科技开发有限公司 +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the limitations of technical means, tourmaline health products are almost all used extensively at present, and the due effectiveness of tourmaline has not been fully and effectively exerted. In medical practice, the ideal and practical effect has not yet been achieved. So far Not yet effectively used in medical and preventive care

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of modified tourmaline powder
  • A kind of preparation method of modified tourmaline powder
  • A kind of preparation method of modified tourmaline powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of preparation method of modified tourmaline powder comprises the following steps:

[0034] 1) Femagnesian tourmaline and transition metal oxides are graded and pulverized respectively, and passed through a 400-mesh sieve, and the pulverized and sieved tourmaline powder and transition metal oxides are mixed at a mass ratio of 20:1 to obtain a mixed powder;

[0035] 2) Put the mixed powder in a muffle furnace, heat up to 550°C at 5°C / min, continue calcining for 2 hours, cool to room temperature, pulverize and pass through a 400-mesh sieve to obtain doped composite tourmaline powder;

[0036] 3) With the assistance of 20Hz ultrasonic vibration, place the doped composite tourmaline powder in 8% chitosan aqueous solution at a ratio of 10:5 (g / ml), wherein the degree of polymerization of chitosan is 6-10, and continue to ultrasonicate 2h, filtered, aged for 12h, placed in a 60°C decompression oven, dried until the moisture content was less than 10%, ultra-finely groun...

Embodiment 2

[0038] A kind of preparation method of modified tourmaline powder comprises the following steps:

[0039] 1) Femagnesian tourmaline and transition metal oxides are graded and crushed respectively, and passed through a 200-mesh sieve, and the pulverized and sieved tourmaline powder and transition metal oxides are mixed at a mass ratio of 15:1 to obtain a mixed powder;

[0040] 2) Put the mixed powder in a muffle furnace, heat up to 550°C at 8°C / min, continue calcining for 4 hours, cool to room temperature, pulverize and pass through a 300-mesh sieve to obtain doped composite tourmaline powder;

[0041] 3) With the assistance of 20Hz ultrasonic vibration, place the doped composite tourmaline powder in 8% chitosan aqueous solution at a ratio of 10:8 (g / ml), wherein the degree of polymerization of chitosan is 3-7, and continue to ultrasonicate 2h, filtered, aged for 12h, placed in a 60°C decompression oven, dried until the moisture content was less than 10%, ultra-finely ground, p...

Embodiment 3

[0043] A kind of preparation method of modified tourmaline powder comprises the following steps:

[0044] 1) Femagnesian tourmaline and transition metal oxides are graded and pulverized respectively, and passed through a 400-mesh sieve, and the pulverized and sieved tourmaline powder and transition metal oxides are mixed at a mass ratio of 18:1 to obtain a mixed powder;

[0045] 2) Put the mixed powder in a muffle furnace, heat up to 400°C at 4°C / min, continue calcining for 6 hours, cool to room temperature, pulverize and pass through a 200-mesh sieve to obtain doped composite tourmaline powder;

[0046] 3) With the assistance of 20Hz ultrasonic vibration, place the doped composite tourmaline powder in 8% chitosan aqueous solution at a ratio of 10:8 (g / ml), wherein the degree of polymerization of chitosan is 6-10, and continue to ultrasonicate 2h, filtered, aged for 12h, placed in a 60°C decompression oven, dried until the moisture content was less than 10%, ultra-finely groun...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The embodiment of the invention discloses a preparation method of modified tourmaline powder, which belongs to the technical field of tourmaline fine deep processing. The preparation method of the modified tourmaline powder comprises three steps of material preparation, transition metal element doping modification in crystal lattice, and chitosan external surface embedding modification. The prepared modified tourmaline powder can significantly improve pyroelectricity and mid-frequency infrared (MWIR) radiation performance, presents obvious biological efficacy, and has higher application value for human health.

Description

technical field [0001] The embodiment of the present invention relates to the technical field of fine deep processing of tourmaline, in particular to a preparation method of modified tourmaline powder. Background technique [0002] Tourmaline, the general term for tourmaline minerals, is a ring silicate crystal mineral composed of elements such as Al, Na, Ca, Mg, B and Fe, containing water and fluorine. In the 1980s, Japanese scholar Kubo discovered for the first time that there were permanent spontaneous electrodes in tourmaline, which aroused people's great attention to tourmaline. Tourmaline has unique functions such as piezoelectricity and pyroelectricity, and can release far-infrared rays and negative ions. At the same time, it exhibits weak bioluminescence and bioelectricity effects on living organisms. [0003] Experimental research has revealed: (1) The spontaneous polarization and pyroelectric properties of tourmaline can make the crystal spontaneously generate wea...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): A61K33/22A61K47/61C01B33/20A61P39/06A61P37/04A61P31/04A61P25/00
CPCA61K33/22A61K47/61A61K9/0014C01B33/20A61P31/04A61P37/04A61P39/06A61P25/00C01P2004/03C01P2004/61
Inventor 李春盛徐长明张建群徐光辉
Owner 大连明盛生物科技开发有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap