High-performance acid mist absorption filter ball

A filter ball, high-performance technology, applied in gas treatment, membrane technology, dispersed particle separation, etc., can solve the problems of easy breakage, poor stability, etc., and achieve the effect of solving easy dispersion, improving firmness, and increasing firmness and stability

Inactive Publication Date: 2020-05-19
蒋黎婷
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Aiming at the problems in the prior art, the present invention provides a high-performance acid mist absorption filter ball, which solves the problems of poor stability and easy breakage of the existing absorption materials, uses the silicon-oxygen structure to form a surface frame, and uses sepiolite and polyacrylic acid The dissolution characteristics of salt realize stable acid mist absorption, and at the same time form a cross structure to achieve the effect of structural complementarity

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0021] A method for preparing a high-performance acid mist absorption filter ball, comprising the steps of:

[0022] Step 1, adding sepiolite powder into distilled water and stirring at a constant temperature to form a uniform solution; the particle size of the sepiolite powder is 50-100 μm, and the mass concentration of the sepiolite powder in distilled water is 100-300g / L, stirring at a constant temperature The temperature is 40-60°C, and the stirring speed is 1000-2000r / min; the sepiolite itself is easily dispersed in water, forming a porous network structure; the sepiolite powder is added to distilled water, supplemented by constant temperature stirring, to achieve The effect of rapid dispersion and the formation of a uniform solution;

[0023] Step 2: Slowly add polyacrylate to the homogeneous solution and vibrate and disperse at a constant temperature to form a uniform viscous liquid, then put the viscous liquid into a spherical mold for a constant temperature reaction f...

Embodiment 1

[0028] A high-performance acid mist absorption filter ball, the filter ball includes an inner core and a cladding layer, the cladding layer is made of porous silicon-oxygen material, and the inner core is made of an inorganic-organic hybrid material.

[0029] The inorganic-organic mixed material is a mixed material of sepiolite and polyacrylate.

[0030] A method for preparing a high-performance acid mist absorption filter ball, comprising the steps of:

[0031] Step 1, adding sepiolite powder into distilled water and stirring at a constant temperature to form a uniform solution; the particle diameter of the sepiolite powder is 50 μm, the mass concentration of sepiolite powder in distilled water is 100 g / L, and the temperature of constant temperature stirring is 40 ℃, the stirring speed is 1000r / min;

[0032] Step 2: Slowly add polyacrylate to the homogeneous solution to vibrate and disperse at a constant temperature to form a uniform viscous liquid, then put the viscous liqu...

Embodiment 2

[0037] A high-performance acid mist absorption filter ball, the filter ball includes an inner core and a cladding layer, the cladding layer is made of porous silicon-oxygen material, and the inner core is made of an inorganic-organic hybrid material.

[0038] The inorganic-organic mixed material is a mixed material of sepiolite and polyacrylate.

[0039] A method for preparing a high-performance acid mist absorption filter ball, comprising the steps of:

[0040] Step 1, adding sepiolite powder into distilled water and stirring at a constant temperature to form a uniform solution; the particle size of the sepiolite powder is 100 μm, the mass concentration of sepiolite powder in distilled water is 300 g / L, and the temperature of constant temperature stirring is 60 ° C , the stirring speed is 2000r / min;

[0041] Step 2: Slowly add polyacrylate to the homogeneous solution to vibrate and disperse at a constant temperature to form a uniform viscous liquid, then put the viscous liqu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention belongs to the field of environmental protection, and particularly relates to a high-performance acid mist absorption filter ball which comprises an inner core and a coating layer. The coating layer is made of a porous silica material, and the inner core is made of an inorganic-organic mixed material. The problem that an existing absorbing material is poor in stability and prone to breakage is solved, a surface frame is formed by means of a silica structure, stable acid mist absorption is achieved by means of the dissolution characteristic of sepiolite and polyacrylate, and meanwhile a cross structure is formed to achieve the effect of structural complementation.

Description

technical field [0001] The invention belongs to the field of environmental protection, and in particular relates to a high-performance acid mist absorption filter ball. Background technique [0002] The pickling process is one of the indispensable production units in the metal products industry (including electroplating, hot-plating, steel mills, etc.), and its principle is to use acid solution (usually hydrochloric acid) to remove scale and rust on the steel surface The chemical method is one of the most commonly used methods for cleaning metal surfaces. The current pickling process mostly uses hydrochloric acid as the acid solution. However, hydrochloric acid is highly volatile and forms hydrochloric acid mist. Hydrochloric acid mist is highly corrosive to workshop buildings, production equipment, and metal infrastructure, and is highly dangerous to workshop operators. Contacting its vapor or smog can cause Acute poisoning, conjunctivitis, nasal and oral mucosa burning se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01D53/02
CPCB01D53/02B01D2257/2045
Inventor 蒋黎婷李婷
Owner 蒋黎婷
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap