Polyvinyl alcohol-ethylene copolymer honeycomb porous membrane and preparation method thereof

A technology of ethylene copolymer and polyvinyl alcohol, which is applied in the direction of chemical instruments and methods, membranes, membrane technology, etc., can solve the problems that are difficult to accurately control the morphology, pore size and uniformity of porous membranes, and achieve uniformity and repeatability Good performance and high controllability

Active Publication Date: 2021-10-01
武汉维晨科技有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Based on this principle, it can be known that changes in solvent type, solution concentration, and environmental humidity will affect the morphology of the porous membrane, so it is difficult to accurately control the morphology, pore size, and uniformity of the porous membrane.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyvinyl alcohol-ethylene copolymer honeycomb porous membrane and preparation method thereof
  • Polyvinyl alcohol-ethylene copolymer honeycomb porous membrane and preparation method thereof
  • Polyvinyl alcohol-ethylene copolymer honeycomb porous membrane and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0034] The invention provides a kind of preparation method of polyvinyl alcohol-ethylene copolymer honeycomb porous membrane, comprises the following steps:

[0035] S1. Add polyvinyl alcohol-ethylene copolymer to a mixed solvent of isopropanol and water with a mass ratio of 1:2 to 2:1, heat it to 70 to 85°C, and dissolve it completely to obtain a mass fraction of 7 %~12% polyvinyl alcohol-ethylene copolymer solution.

[0036] The polyvinyl alcohol-ethylene copolymer molecular chain includes a hydrophilic polyvinyl alcohol segment and a hydrophobic polyethylene segment, which is soluble in hot aqueous solution. It is difficult to dissolve polyvinyl alcohol with isopropanol alone. The volatility of water is poor, which is not conducive to the formation of honeycomb porous structure when removing the solvent phase. And because isopropanol and water are miscible, so choose volatile isopropene and water as mixed solvent, utilize the difference of both to polyvinyl alcohol-ethylen...

Embodiment 1

[0049] A polyvinyl alcohol-ethylene copolymer honeycomb porous membrane is prepared by a phase separation spin coating method, comprising the following steps:

[0050] S1. Add polyvinyl alcohol-ethylene copolymer to a mixed solvent of isopropanol and water with a mass ratio of 1:1, heat to 80°C to dissolve it completely, and obtain polyvinyl alcohol with a mass fraction of 8%- Ethylene copolymer solution;

[0051] The molecular weight of the polyvinyl alcohol-ethylene copolymer is about 50,000; the content of polyvinyl alcohol in the polyvinyl alcohol-ethylene copolymer is 80%; the alcohol content of polyvinyl alcohol in the polyvinyl alcohol-ethylene copolymer The resolution is 88%.

[0052] S2. Put the silicon wafer on the turntable of the homogenizer, set the rotating speed to 2000 rpm, and the rotation time is 60s, start the homogenizer, and drop 0.05ml of the polyvinyl alcohol-ethylene copolymer solution obtained in step S1 On the silicon chip, until the glue homogenize...

Embodiment 2～8 and comparative example 1～5

[0057] The polyvinyl alcohol-ethylene copolymer honeycomb porous membrane that embodiment 2~8 and comparative example 1~5 provide, compare with embodiment 1, difference is that, preparation condition is as shown in table 1, other and embodiment 1 They are basically the same and will not be repeated here.

[0058] The preparation conditions of table 1 embodiment 2~8 and comparative examples 1~5

[0059]

[0060]

[0061] see Figure 4 As shown, it can be seen that when the mass fraction of the polyvinyl alcohol-ethylene copolymer solution was 6%, the polyvinyl alcohol-ethylene copolymer film prepared in Comparative Example 3 did not form a honeycomb porous structure, which may be because the solution concentration was too high. When the viscosity is low, the viscosity decreases and the content of the solvent phase is large. When the solvent phase is removed, a large amount of solvent volatilizes, resulting in an increase in the content of condensed water, making it diffi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
Login to view more

Abstract

The invention provides a polyvinyl alcohol-ethylene copolymer honeycomb porous membrane and a preparation method thereof. First, dissolve the polyvinyl alcohol-ethylene copolymer in a mixed solvent of isopropanol and water with a mass ratio of 1:2 to 2:1, and prepare a polyvinyl alcohol-ethylene copolymer solution with a mass fraction of 7% to 12%. ; Then, after the polyvinyl alcohol-ethylene copolymer film is prepared by spin coating, heat treatment is carried out at a temperature 1-10°C lower than the boiling point of the azeotrope of isopropanol and water, and the solvent phase is removed to form a honeycomb porous film Carry out annealing treatment at last, obtain polyvinyl alcohol-ethylene copolymer honeycomb porous film. The polyvinyl alcohol-ethylene copolymer molecular chain that the present invention chooses comprises hydrophilic polyvinyl alcohol segment and hydrophobic polyethylene segment, utilizes isopropanol and water to polyvinyl alcohol-ethylene copolymer solubility and boiling point Difference, through multi-stage solvent volatilization, a honeycomb porous membrane with uniform distribution, small pore size and uniform pore size is prepared.

Description

technical field [0001] The invention belongs to the technical field of porous membrane preparation, and relates to a polyvinyl alcohol-ethylene copolymer honeycomb porous membrane and a preparation method thereof, in particular to a polyvinyl alcohol-ethylene copolymer honeycomb porous membrane prepared by a phase separation spin coating method The method and polyvinyl alcohol-ethylene copolymer honeycomb porous membrane. Background technique [0002] Because of the extremely high specific surface area, large roughness and uniform pore structure, the honeycomb porous membrane has very broad application prospects in various aspects such as optoelectronic devices, biomaterials, sensors, template materials, separation and filtration, etc. In recent years, it has received a lot of research attention. At present, the preparation methods of porous membranes mainly include breathing pattern method, emulsion droplet template method, colloidal crystal template method, surfactant sel...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01D71/44B01D69/02B01D67/00
CPCB01D67/0013B01D69/02B01D71/44B01D2325/026
Inventor 王栋吴建美赵青华梅涛毛秦岑宋银红尤海宁
Owner 武汉维晨科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap