A linseed oil and preparation technology, applied in the direction of microcapsule preparation, microsphere preparation, etc., can solve the problems of large dilution of emulsifier, low embedding rate, easy caking, etc., to avoid oil leakage and increase nutrition Value, the effect of improving the embedding rate

Active Publication Date: 2022-04-15
ZHEJIANG UNIV OF TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, in the preparation of linseed oil microcapsules, the most common is to use soybean protein and maltodextrin as wall materials, but the embedding rate of linseed oil microcapsules prepared when the two are used in combination is not ideal; therefore, In the prior art, more emulsifiers are added to improve the stability of the oil-water emulsion to solve the problem of low embedding rate
However, the addition of additional emulsifier not only increases the production cost, but also the emulsifier has high dilution, and the product is easy to agglomerate when stored improperly

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation technology of linseed oil microcapsule and its product

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] Weigh 1.71g soybean protein isolate (concentration in water phase is 0.564%, unless otherwise specified below, all are mass percent concentration) and 1.368g maltodextrin (concentration in water phase is 0.451%) and 0.342g Cordyceps sinensis The polysaccharide (concentration in the water phase is 0.113%) was dissolved in 300 mL of water to fully dissolve in a water bath, the temperature of the water bath was 50° C. to obtain the water phase. The mass ratio of soybean protein isolate, maltodextrin, and Cordyceps polysaccharide is 5:4:1, and the mass percentage concentration of the total wall material is 1.128%.

[0047]The water phase was sheared for 2 minutes with high-speed shearing gear 6 (12000r), and 2.56g of linseed oil (core-to-wall ratio was 0.75) was added to the water phase, and the high-speed shearing machine was sheared for 2 minutes at 6 gears (12000r) to form a uniform stable emulsion. Stir magnetically in a water bath at 40°C, add dropwise 25 wt% acetic a...

Embodiment 2

[0051] Weigh 2.06g soybean protein isolate (concentration in water phase is 0.680%) and 0.618g maltodextrin (concentration in water phase is 0.204%) and 0.412g Cordyceps polysaccharide (concentration in water phase is 0.136%) to dissolve Fully dissolve in 300mL water in a water bath with a water bath temperature of 50°C to obtain an aqueous phase. The mass ratio of soybean protein isolate, maltodextrin, and Cordyceps polysaccharide is 10:3:2, and the mass percentage concentration of the total wall material is 1.02%.

[0052] Cut the water phase with high-speed shear 6 (12000r) for 2 minutes, add 1.545g linseed oil (core-to-wall ratio is 0.5) to the water phase, and shear 2min with high-speed shear 6 (12000r) to form a uniform stable emulsion. Stir magnetically in a water bath at 40°C, while stirring, add 25% acetic acid solution dropwise to adjust the pH of the system to 4.1, stir at a constant temperature for 10 minutes to obtain a suspension of linseed oil microcapsules, an...

Embodiment 3

[0055] Weigh 2.06g soybean protein isolate (concentration is 0.677% in water phase) and 1.236g maltodextrin (concentration is 0.406% in water phase) and 0.824g Cordyceps polysaccharide (concentration is 0.271% in water phase) dissolving Fully dissolve in 300mL water in a water bath with a water bath temperature of 50°C to obtain an aqueous phase. The mass ratio of soybean protein isolate, maltodextrin, and Cordyceps polysaccharide is 5:3:2, and the mass percentage concentration of the total wall material is 1.354%.

[0056] The water phase was sheared for 2 minutes with high-speed shearing gear 6 (12000r), and 3.09g of linseed oil (core-to-wall ratio was 0.75) was added to the water phase, and the high-speed shearing machine was sheared for 2 minutes at 6 gears (12000r) to form a uniform stable emulsion. Stir magnetically in a water bath at 40°C, while stirring, add 25% acetic acid solution dropwise to adjust the pH of the system to 4.1, stir at a constant temperature for 10 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation process of linseed oil microcapsules, comprising: (1) using soybean protein, maltodextrin and Cordyceps polysaccharide as wall materials, mixing with water to prepare an aqueous phase; Cordyceps polysaccharide, maltodextrin and soybean protein The mass ratio of the total wall material is 1:0.5~99:0.3~100; the mass percentage concentration of the total wall material is 0.5~2.0%; (2) Mix the water phase with linseed oil until a uniform and stable emulsion is formed, and adjust to acidity Stirring at constant temperature for a period of time to obtain linseed oil microcapsule suspension, and then spray drying to obtain linseed oil microcapsules. The preparation process not only increases the nutritional value of linseed oil microcapsules by mixing Cordyceps polysaccharide with soybean protein and maltodextrin as the wall material, but also further improves the nutritional value of linseed oil microcapsules without additional emulsifiers. embedding rate.

Description

technical field [0001] The invention relates to the technical field of embedding of linseed oil microcapsules, in particular to a preparation process of linseed oil microcapsules and a product thereof. Background technique [0002] Flaxseed oil is a dry oil obtained from flaxseeds. It is yellow and transparent and has a unique fragrance. The oil content in flaxseed is about 35% to 45%, of which α-linolenic acid is rich in content, which can be converted into eicosapentaenoic acid (EPA) and docosahexaenoic acid (DHA) in animals. Saturated fatty acids have extremely high nutritional value and important physiological functions. They have the effects of lowering blood fat and blood pressure, improving cardiovascular and cerebrovascular diseases, and preventing diabetes, rheumatism, rheumatoid, and tumors. [0003] However, due to the high content of unsaturated fatty acids in linseed oil, linseed oil is easily oxidized and has poor solubility during storage, making it difficult...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): B01J13/04
CPCB01J13/04B01J13/043
Inventor孙培龙田奕彤张凯航张颀宜盛佳露冯思敏
OwnerZHEJIANG UNIV OF TECH