Co-firing method of full-body ink-jet black golden flower full-polished bricks and common archaized bricks

An antique brick and whole body technology, applied in the field of architectural ceramics, can solve the problems of low product quality, low production capacity, white spots, etc., and achieve the effect of improving product qualification rate and reducing production costs

Active Publication Date: 2020-09-22
广西蒙娜丽莎新材料有限公司
View PDF11 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, on the one hand, the traditional whole-body black gold flower production process is prone to defects such as watermarks, white spots, and low production capacity, which affects the aesthetics, and the process is complicated, consuming manpower and material resources, and the waste printing glaze produced is highly polluted, and the product's excellent rate is low.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A co-firing method of full-body inkjet black gold flower full-throw bricks and ordinary antique bricks, comprising the following steps:

[0042] (1) Henglitai YP4205 single-chip pressure 30,000KN press forms the whole body of the full-throwing brick body, grinds it flat, and then enters the drying kiln for drying, and the moisture content of the drying kiln is within 0.5%; Wherein the blank made of the full-throwing brick body includes the following chemical components by weight percentage: Si0 2 : 67%, A1 2 o 3 :21.5%, K 2 0:3.5%, Na 2 0: 2%, MgO: 0.5%, CaO: 0.3%, Fe 2 O3: 0.5%, IL4.7%; the blanks made of full-thrown brick bodies are made of Guangxi stone powder, Beiliu stone powder, Guangxi potash sand, Guilin medium temperature sand, Beiliu black mud, Guangxi washed mud, Guangxi bauxite, and Guangxi talc The mud is mixed and prepared; the powder made into the full-thrown brick body is sieved through a 250-mesh sieve, and the remaining 0.6%; the blank made of the...

Embodiment 2

[0062] A co-firing method of full-body inkjet black gold flower full-throw bricks and ordinary antique bricks, comprising the following steps:

[0063] (1) Henglitai YP4205 single-chip pressure 30,000KN press forms the whole body of the full-throwing brick body, grinds it flat, and then enters the drying kiln for drying, and the moisture content of the drying kiln is within 0.5%; Wherein the blank made of the full-throwing brick body includes the following chemical components by weight percentage: Si0 2 : 67%, A1 2 o 3 :21.5%, K 2 0:3.5%, Na 2 0: 2%, MgO: 0.5%, CaO: 0.3%, Fe 2 O3: 0.5%, IL4.7%; the blanks made of full-thrown brick bodies are made of Guangxi stone powder, Beiliu stone powder, Guangxi potash sand, Guilin medium temperature sand, Beiliu black mud, Guangxi washed mud, Guangxi bauxite, and Guangxi talc The mud is mixed and prepared; the powder made into the full-thrown brick body is sieved through a 250 mesh sieve, and the remaining 0.8%; the blank made into t...

Embodiment 3

[0083] A co-firing method of full-body inkjet black gold flower full-throw bricks and ordinary antique bricks, comprising the following steps:

[0084] (1) Henglitai YP4205 single-chip pressure 30,000KN press forms the whole body of the full-throwing brick body, grinds it flat, and then enters the drying kiln for drying, and the moisture content of the drying kiln is within 0.5%; Wherein the blank made of the full-throwing brick body includes the following chemical components by weight percentage: Si0 2 : 67%, A1 2 o 3 :21.5%, K 2 0:3.5%, Na 2 0: 2%, MgO: 0.5%, CaO: 0.3%, Fe 2O3: 0.5%, IL4.7%; the blanks made of full-thrown brick bodies are made of Guangxi stone powder, Beiliu stone powder, Guangxi potash sand, Guilin medium temperature sand, Beiliu black mud, Guangxi washed mud, Guangxi bauxite, and Guangxi talc The mud is mixed and prepared; the powder made into the full-thrown brick body is sieved through a 250 mesh sieve, and the remaining 0.7%; the blank made of the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a co-firing method of full-body ink-jet black golden flower full-polished bricks and common archaized bricks. It is required by co-firing process that the brick types of the full-body ink-jet black golden flower full-polished bricks and the common archaized bricks are within the national standard range; generally case, the brick type of the common archaized bricks is easy to tilt; the invention relates to a full-body ink-jet black golden flower full-polished brick, in particular to a full-body ink-jet black golden flower full-polished brick with a deep-color layout. Toavoid such circumstances, full-body ink-jet black golden flower full-polished brick surface glaze and common archaized brick surface glaze with different expansion coefficients are selected to realizebasic consistency of the shapes of the bricks discharged out of a kiln; the method comprises the following steps: adjusting the expansion coefficient of surface glaze for the full-body ink-jet blackgolden flower full-polished bricks to 250 * 10 <-7 > m / K-300 * 10 <-7 > m / K; adjusting the expansion coefficient of the surface glaze used by the common archaized bricks to 190 * 10 <-7 > m / K-230 * 10<-7 > m / K; the brick shape of the full-body ink-jet black golden flower full-polished bricks is close to that of common archaized bricks, the product percent of pass of co-firing of the full-body ink-jet black golden flower full-polished bricks and the common archaized bricks is greatly increased, the product quality is stable, the transfer rate is low, and meanwhile the productivity is improved.

Description

technical field [0001] The invention relates to the technical field of architectural ceramics, in particular to a co-firing method of full-body inkjet black gold flower full-throw bricks and ordinary antique bricks. Background technique [0002] The whole body black gold flower glazed tile has the characteristics of no fading, no pollution, no radioactivity, gorgeous texture and noble luster, which can restore the texture of real stone; it not only conforms to the development trend of low-carbon green economy in modern society, but also A durable decorative material that can enjoy the decoration of a beautiful home. However, on the one hand, the traditional whole-body black gold flower production process is prone to defects such as water marks, white spots, and low production capacity, which affects the aesthetics, and the process is complicated, consuming manpower and material resources, and the waste printing glaze produced is polluted and the product has a low excellent r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/14C04B41/89C04B35/64
CPCC04B35/14C04B35/64C04B41/009C04B41/52C04B41/89C04B2235/3201C04B2235/3206C04B2235/3208C04B2235/3217C04B2235/3272C04B2235/96C04B41/504C04B41/4543C04B41/0072C04B41/5022C04B41/4535
Inventor 萧志强赵勇邓勇军冼桂昌秦永杰周杏棠李政覃斌锦
Owner 广西蒙娜丽莎新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com