A method for improving the yield of titanium alloy wire rod by rotary forging

A titanium alloy and yield technology, applied in the field of titanium alloy wire preparation, can solve problems such as low yield, poor finish, scratches, etc., and achieve the effects of improving surface quality, improving efficiency, and reducing lateral flow

Active Publication Date: 2021-08-17
CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the problems of surface damage, especially scratches, poor finish and low yield in the preparation process of titanium alloy wire existing in the prior art, and to provide a method for improving the yield of titanium alloy wire by swaging method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] This embodiment is used to illustrate the swaging reducing method of Φ8mm→Φ6mm TA1 wire rod.

[0044] A. Adjust the heat-treated Φ8mm wire with the straightening device equipped at the entrance of the swaging machine until the straightness is less than 10mm / m, and then get stuck at the entrance of the swaging machine;

[0045] B. Replace the rotary forging machine with a Φ7mm mold, and use the rotary forging machine to reduce the diameter of the Φ8mm wire straightened in step A to Φ7mm at one time;

[0046] C. After adjusting the Φ7mm wire rod obtained in step B until the straightness is less than 10mm / m, it is stuck at the entrance of the swaging machine;

[0047] D. Replace the swaging machine with a Φ6mm mold, and use the swaging machine to reduce the diameter of the Φ7mm wire straightened in step C to Φ6mm at one time;

[0048] E. During the reducing process described in step B and step D, use DTE46 anti-wear hydraulic oil to lubricate and cool the wire rod.

[00...

Embodiment 2

[0051] This embodiment is used to illustrate the diameter reduction method of the TA1 wire rod of Φ6mm→Φ4.5mm by swaging.

[0052] A. Adjust the heat-treated Φ6mm wire with the straightening device equipped at the entrance of the swaging machine until the straightness is less than 8mm / m, and then get stuck at the entrance of the swaging machine;

[0053] B. Replace the swaging machine with a Φ5mm mold, and use the swaging machine to reduce the diameter of the Φ6mm wire straightened in step A to Φ5mm at one time;

[0054] C. After adjusting the Φ5mm wire rod obtained in step B until the straightness is less than 9mm / m, it is stuck at the entrance of the swaging machine;

[0055] D. Replace the swaging machine with a Φ4.5mm mold, and use the swaging machine to reduce the diameter of the Φ5mm wire straightened in step C to Φ4.5mm at one time;

[0056] E. During the reducing process described in step B and step D, use DTE46 anti-wear hydraulic oil to lubricate and cool the wire r...

Embodiment 3

[0059] This embodiment is used to illustrate the diameter reduction method of the TB14 wire rod of Φ8mm→Φ6mm by swaging.

[0060] A. After the heat-treated Φ8mm wire is adjusted to a straightness of less than 9mm / m by the straightening device equipped at the entrance of the swaging machine, it is stuck at the entrance of the swaging machine;

[0061] B. Replace the swaging machine with a Φ7mm mold, and use the swaging machine to reduce the diameter of the Φ8mm wire straightened in step A to Φ7mm at one time;

[0062] C. After adjusting the Φ7mm wire rod obtained in step B until the straightness is less than 9mm / m, it is stuck at the entrance of the swaging machine;

[0063] D. Replace the swaging machine with a Φ6mm mold, and use the swaging machine to reduce the diameter of the Φ7mm wire straightened in step C to Φ6mm at one time;

[0064] E. During the reducing process described in step B and step D, use DTE46 anti-wear hydraulic oil to lubricate and cool the wire rod.

[...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongationaaaaaaaaaa
elongationaaaaaaaaaa
elongationaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of titanium alloy wire preparation, and discloses a method for improving the yield of titanium alloy wire by swaging. The method includes: A. Straightening the wire rod after heat treatment, and clamping it at the entrance of the swaging machine; B. Swirling the straightened wire rod for the first time by using a swaging machine; C. Swinging the straightened wire rod for the first time; The wire rod is straightened and stuck at the entrance of the swaging machine; D. The straightened wire rod is swaged for the second time with the swage machine; E. During the diameter reduction process, the wire rod is lubricated and repaired with anti-wear hydraulic oil cool down. In this method, the diameter of the wire rod is reduced by swaging twice, and by controlling the deformation amount and the total deformation amount of each swaging pass, the surface quality of the material after swaging is effectively improved; the use of a mold with a size similar to the target not only improves the The efficiency of swaging is improved, and the surface of the swaged material is smoother; during the reduction process, the cold swaging process avoids the serious oxidation of the material surface and improves the yield of the material.

Description

technical field [0001] The invention relates to the technical field of preparation of titanium alloy wires, in particular to a method for improving the yield of titanium alloy wires by swaging. Background technique [0002] Titanium alloys have been widely used in aerospace and energy fields because of their high specific strength, good oxidation resistance and thermal corrosion resistance. [0003] As a method of titanium alloy diameter reduction, swaging has many advantages: there is additional compressive stress on the surface of the material after swaging, and the bending strength of the material is improved; the surface of the material after swaging is smooth; the precision advantage of swaging products; The lateral flow of material in the swaging processing area is restricted, which improves the axial extension efficiency of the material, and the stress state of the three-dimensional compression in the material processing area is conducive to the deformation of the mat...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21F5/00B21F1/02
CPCB21F1/02B21F5/00
Inventor 申学良唐新新王立亚郑帮智
Owner CHENGDU ADVANCED METAL MATERIALS IND TECH RES INST CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com