Hot melt adhesive for difficult-to-stick base material and preparation method thereof

A technology for hot melt adhesives and substrates, applied in the directions of adhesives, adhesive types, conjugated diene adhesives, etc., which can solve the problems of increasing the complexity of production and failing to meet the requirements of product design and production.

Active Publication Date: 2020-10-30
佛山南宝高盛高新材料有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, conventional hot melt adhesives are currently used to bond bamboo fibers and non-woven fabrics, which cannot meet the requirements of product design and production.
[0005] In addition, in product design, difficult-to-bond substrates such as silk, hot-air cloth, smooth non-woven fabric, cotton fiber, bamboo fiber, and viscose fiber will be combined with a variety of different fabrics for different parts of the product. The use of different hot melt adhesives for fabric compounding will greatly increase the complexity of production and production costs. A hot melt adhesive is required to meet the compounding requirements of different difficult-to-bond substrates and different fabrics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot melt adhesive for difficult-to-stick base material and preparation method thereof
  • Hot melt adhesive for difficult-to-stick base material and preparation method thereof
  • Hot melt adhesive for difficult-to-stick base material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The second object of the present invention is achieved by the following technical solutions: a method for preparing hot melt adhesive for difficult-to-bond substrates, comprising the following steps:

[0040] (1) Add part of the naphthenic oil of formula quantity and the antioxidant of formula quantity in kneader, and heat up;

[0041] (2) Add the formula amount of styrene-based elastomer and stir. After the mixed system is melted, add the formula amount of styrene-butadiene rubber, continue to stir and melt; after the mixed system is melted, add the formula amount of polyolefin elastomer After stirring and mixing evenly, add the amount of tackifying resin in the formula, and stir evenly for 20 minutes;

[0042] (3) Put in the remaining naphthenic oil and ultraviolet absorber, stir evenly for 20 minutes, vacuumize to remove air bubbles, discharge the material, cool to room temperature, and obtain a hot-melt adhesive for difficult-to-stick substrates.

[0043] As a furt...

Embodiment 1

[0049] The raw materials of hot-melt adhesive for difficult-to-bond substrates are composed according to the following parts by weight: naphthenic oil 47135 15 parts, SIS 110513 parts, SIS 4186 5 parts, solution polystyrene butadiene rubber 1205 7 parts, polyolefin elastomer GA-1000R 5 parts 40 parts of semi-hydrogenated petroleum resin C-100R, 10 parts of semi-hydrogenated rosin resin H120, 2 parts of modified terpene resin T160, 0.6 parts of antioxidant 1010 and 0.6 parts of antioxidant 168, 0.8 parts of antioxidant 4120, UV Absorber UV-326H 1 part.

Embodiment 2

[0051] The raw materials of the hot melt adhesive for difficult-to-bond substrates are composed of the following parts by weight: 30 parts of naphthenic oil 47135, SIS 110530 parts, 10 parts of solution polystyrene butadiene rubber 2605, 10 parts of polyolefin elastomer GA-1000R, semi-hydrogenated petroleum 16.7 parts of resin C-100R, 2 parts of modified terpene resin, 0.1 parts of antioxidant 1010 and 168, 0.1 part of antioxidant FT-1126, 1 part of ultraviolet absorber UV-326H.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a hot melt adhesive for a difficult-to-stick base material and a preparation method of the hot melt adhesive. The hot melt adhesive for the difficult-to-stick base material isprepared from the following components in parts by weight: 10 to 30 parts of naphthenic oil, 10 to 30 parts of styrene elastomer, 7 to 20 parts of solution polymerized styrene-butadiene rubber, 3 to 20 parts of polyolefin elastomer, 15 to 70 parts of tackifying resin, 0.35 to 3 parts of an antioxidant and 0.2 to 1 part of an ultraviolet light absorber. The hot melt adhesive disclosed by the invention can be used for well bonding difficult-to-adhere base materials so as to meet the adhesion requirements of different difficult-to-adhere fabrics, so manufacturers of sanitary material products such as paper diapers and sanitary towels can be provided with more options for high-quality fabrics, such as silk fabrics, hot through-air fabrics, smooth non-woven fabrics, cotton fiber fabrics, bamboofiber fabrics and viscose fabrics.

Description

technical field [0001] The invention relates to a hot-melt adhesive technology, in particular to a hot-melt adhesive for a difficult-to-bond base material and a preparation method thereof. Background technique [0002] At present, manufacturers of diapers, sanitary napkins and pet sanitary pads are looking for more and better fabrics to be used in disposable sanitary products; at the same time, more requirements are placed on hot melt adhesives for fabric bonding. At present, silk fabrics, hot air cloths, smooth non-woven fabrics, cotton fiber fabrics, bamboo fiber fabrics, viscose fiber fabrics, etc. are all high-quality fabrics that can be applied to diapers and sanitary napkins, but due to these silk fabrics, hot air cloths, etc. , smooth non-woven fabrics, cotton fiber fabrics, bamboo fiber fabrics, and viscose fiber fabrics, which have a high degree of fibrosis and relatively fluffy volume, are difficult to bond with conventional hot melt adhesives. Currently, there is ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J157/02C09J191/00C09J153/02C09J109/06C09J11/08
CPCC09J157/02C09J191/00C09J153/02C09J11/08C08L91/00C08L53/02C08L9/06C08L57/02
Inventor 袁健韦宝平曹少波吴永升
Owner 佛山南宝高盛高新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap