Anti-flash-rust agent for water-based paint and preparation method thereof

A water-based coating, anti-flash rust technology, applied in anti-corrosion coatings, polyester coatings, epoxy resin coatings and other directions, can solve the problems of not meeting the development trend of environmentally friendly coatings, toxic and carcinogenic, and achieve low production costs, anti-flash The effect of good rust performance and simple synthesis process

Active Publication Date: 2020-11-03
HUAQIAO UNIVERSITY
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing technology mainly uses nitrite as an anti-flash rust agent, which has a good anti-flash rust effect. However, nitrite is a toxic and carcinogenic substance, which does not meet the development trend of environmentally friendly coatings, and has been clearly restricted in European and American countries. Added to some varieties of paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-flash-rust agent for water-based paint and preparation method thereof
  • Anti-flash-rust agent for water-based paint and preparation method thereof
  • Anti-flash-rust agent for water-based paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Add 20g of 1,4-butynediol and 20g of tetrasodium hydroxyethylidene diphosphonate to 1L of deionized water in sequence, stir at 25°C for 0.5h, then add 50g of [CTA][Cl] in sequence , 50g of [BTA][NSA] and 50g of [DSA][Cl], stirred at 25°C for 0.5h to obtain an anti-flash rust agent for water-based coatings.

Embodiment 2

[0034] Add 10 g of propynyl alcohol and 10 g of tetrasodium hydroxyethylidene diphosphonate to 1 L of deionized water in sequence, stir at 25°C for 0.5 h, then add 25 g of [CTA][NSA], 25 g of [BTA ][Cl] and 25g of [DSA][Cl], stirred at 25°C for 0.5h to obtain an anti-flash rust agent for water-based coatings.

Embodiment 3

[0036] Add 5 g of 1,4-butynediol and 5 g of tetrasodium aminotrimethylene phosphonate in sequence to 1 L of deionized water, stir at 25°C for 0.5 h, then add 45 g of [CTA][NSA], Stir 45g of [BTA][Cl] and 45g of [DSA][Cl] at 25°C for 0.5h to obtain an anti-flash rust agent for water-based coatings.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an anti-flash-rust agent for water-based paint and a preparation method of the anti-flash-rust agent. The anti-flash-rust agent is formed by compounding imidazoline ionic liquid, triazole ionic liquid, quaternary ammonium salt ionic liquid, organic phosphate, alkynol and deionized water according to the mass ratio of 20-60 : 20-60 : 20-60 : 4-25 : 4-25 : 1000. According tothe method, a uniform and compact adsorption film is easily formed on the metal surface, electrochemical corrosion on the metal surface is effectively prevented, and the effect of inhibiting corrosionis achieved. The anti-flash-rust agent is applied to the water-based paint, the anti-flash-rust performance is good, the use amount is small, and it can be guaranteed that rust spots do not appear onthe metal surface only by adding 0.7 to 1.2 wt% of the anti-flash-rust agent.

Description

technical field [0001] The invention belongs to the technical field of organic materials, and in particular relates to an anti-flash rust agent for water-based paint and a preparation method thereof. Background technique [0002] Water-based paint is one of the five green paint products clearly stipulated by the national standard. It has the characteristics of small environmental hazards, convenient construction, good safety, and easy storage and transportation. However, when water-based coatings are used on the steel surface, due to the presence of water and oxygen during the drying process, it is very easy to corrode the steel surface, that is, flash rust. Especially when water-based paint is applied on high carbon steel or cast iron parts, the problem of flash rust is difficult to avoid. Therefore, adding an anti-flash rust agent to water-based paint is an important method to solve the problem of flash rust in the metal coating process. [0003] The existing technology ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/08C09D133/04C09D163/00C09D167/08C09D175/04
CPCC09D5/08C09D133/04C09D163/00C09D167/08C09D175/04
Inventor 胡鹏程周树锋柴瑞敏赖傲楠
Owner HUAQIAO UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap