Stone needle composite yarn, cloth and preparation method of stone needle composite yarn

The technology of Bianstone and yarn is applied in the field of magnetic therapy and health care, which can solve the problems of thermal-warm fleece fabrics being unable to release ultrasonic pulses to the human body, difficult to achieve magnetic therapy health care effects, and simple in structure, so as to achieve magnetic therapy health care effects and excellent ultrasonic waves. Pulse and ultra-far-infrared release effect, melting temperature reduction effect

Active Publication Date: 2020-11-03
HEYE HEALTH TECH CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, this warm fleece fabric cannot release ultrasonic pulses and ultra-far infrared rays to the human body, so it is difficult to achieve an effective magnetic therapy health care effect, and its structure is simple and its strength is low, which needs to be improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stone needle composite yarn, cloth and preparation method of stone needle composite yarn

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0032] The present invention also provides a preparation method of meteorite composite yarn, comprising the following steps:

[0033] Step 1. Preparation of polyester core 1: take 10-30% by mass of meteorites, 0.5-1.2% of essential oil and polyester as the balance, and cut them after spinning into tows;

[0034] Step 2, the preparation of cellulose spun yarn 2: take the mountain palm that is 2.4-7.2% by mass percentage and one or more of viscose fiber, bamboo fiber, modal fiber or lyocell fiber as the balance It is obtained after mixing, cleaning, wool top, drawing frame, roving, spun yarn and winding in sequence;

[0035] Step 3. Wrap two polyester cores 1 in a double helix to form one body;

[0036] Step 4, wrapping the cellulose spun yarn 2 on the two polyester cores 1 wound together to obtain a composite yarn.

[0037] It should be noted that, in the preparation of the cellulose spun yarn 2, as the remainder, it is a plurality of viscose fibers, bamboo fibers, modal fibe...

Embodiment 1

[0044] Such as figure 1 As shown, a meteorite composite yarn includes two polyester cores 1 in a double helical winding structure and cellulose staple fiber yarn 2 wrapped around the two polyester cores 1 . The polyester core 1 contains 10% by mass percentage of meteorites; the cellulose staple fiber yarn 2 contains 2.4% by mass of mountain palm. It should be mentioned that the polyester core 1 is a polyester filament. The cellulose spun yarn 2 is composed of viscose fiber, bamboo fiber, modal fiber and lyocell fiber.

[0045] The invention also provides a cloth, which includes and is made of the meteorite composite yarn.

[0046] The present invention also provides a preparation method of meteorite composite yarn, comprising the following steps:

[0047] Step 1. Preparation of polyester thread core 1: take 10% meteorite by mass percentage, 0.5% essential oil and polyester as the balance, and cut it after spinning into tow;

[0048] Step 2, the preparation of cellulose spun ...

Embodiment 2

[0057] Such as figure 1 As shown, a meteorite composite yarn includes two polyester cores 1 in a double helical winding structure and cellulose staple fiber yarn 2 wrapped around the two polyester cores 1 . The polyester core 1 contains 20% of the meteorite by mass percentage; the cellulose staple fiber yarn 2 contains 4.8% of the mountain palm by mass percentage. It should be mentioned that the polyester core 1 is a polyester filament. The cellulose spun yarn 2 consists of viscose fiber, bamboo fiber, modal fiber and lyocell fiber.

[0058] The invention also provides a cloth, which includes and is made of the meteorite composite yarn.

[0059] The present invention also provides a preparation method of meteorite composite yarn, comprising the following steps:

[0060] Step 1. Preparation of polyester thread core 1: take 20% meteorite by mass percentage, 0.8% essential oil and polyester as the balance, and cut it after spinning into tow;

[0061] Step 2, the preparation o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The application discloses a stone needle composite yarn, cloth and a preparation method of the stone needle composite yarn, and relates to the technical field of magnetic therapy health care. The stone needle composite yarn comprises two polyester wire cores of a double-helix winding structure and cellulose staple fiber yarns wrapping and winding the two polyester wire cores; the polyester wire cores contain 10-30% by mass of stone needles; and the cellulose staple fiber yarns contain 2.4-7.2% by mass of arenga engleri. According to the application, 10-30% by mass of the stone needles are added into the two polyester wire cores which are of a double-helix winding structure, so that the stone needles rub against the cellulose staple fiber yarns wrapped and wound on the two polyester wire cores, and the two polyester wire cores rub against each other, thereby achieving the effect of stimulating the release of the stone needles; and besides, 2.4-7.2% by mass of the arenga engleri is addedinto the cellulose staple fiber yarns, so that the structural strength and the distribution uniformity of the yarns are improved through the arenga engleri which is free from fat, low in heat energyand high in fiber, and the magnetic therapy health care effect is improved.

Description

technical field [0001] The application relates to the technical field of magnetic therapy and health care, in particular to a meteorite composite yarn, cloth and a preparation method thereof. Background technique [0002] Fibers and yarns have been the main materials in the traditional textile industry for thousands of years. Fibers and yarns are combined to form composite yarns for knitted fabrics. Therefore, fabrics woven from composite yarns have various advantages, such as high structural strength, wear resistance, and anti-aging properties. [0003] The Chinese patent with the publication number CN209851718U discloses a warm-keeping fleece fabric. The warm-keeping fleece fabric includes a contact layer, and the top surface of the contact layer is adhesively connected with a thermal insulation layer made of cashmere fiber. Hot pressing forms several depressions, the top surface of the thermal insulation layer is adhesively connected with a surface layer, and the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/38D02G3/04D02G3/44D01F8/14D01D5/08D01G1/00
CPCD01D5/08D01F8/14D01G1/00D02G3/045D02G3/38D02G3/448D10B2201/10D10B2201/20D10B2201/24D10B2331/04
Inventor 方彦雯方志财
Owner HEYE HEALTH TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com