Composite materials based on tungsten carbide and having noble metal binders, and method for producing said composite materials
A technology of composite materials and precious metals, applied in hypodermic injection devices, blood pumps, suction devices, etc., can solve the problem of undisclosed containing composite materials
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment
[0035] The preparation method of the sintered composite material of tungsten carbide and gold of the present invention is illustrated by way of example below:
[0036] 1. Preparation of sintered composite materials of tungsten carbide and gold.
[0037] 23.75g of tungsten carbide and 1.25g of gold powder were ground in hexane in a ball mill at 200rpm with a ball-to-powder ratio of 10:1 for 2 hours. The mixed powders were dried and transferred into graphite molds with a diameter of 20 mm. The powder is vacuum processed in graphite molds in the FAST chamber. The initial pressure is 10MPa. Over the next 15 minutes, the pressure rose steadily to 100 MPa. The maximum application pulse direct current of FAST method reaches 2kA, and the voltage reaches 5.3V. The sample is heated to 1600°C at a rate of 150K / min. During the sintering process, the residence time at 1600°C was 5min, after which the current was turned off, but the sample pressure was maintained. After the sintering ...
PUM
Property | Measurement | Unit |
---|---|---|
particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com