A kind of in-situ nano copper paste and its preparation process and application

A preparation process, nano-copper technology, applied in nanotechnology, nanotechnology, nanotechnology for materials and surface science, etc., to avoid oxidation problems, good dispersion, and avoid agglomeration problems.

Active Publication Date: 2021-08-31
GUANGDONG UNIV OF TECH
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above improvements did not fundamentally solve the problem of agglomeration and oxidation of nano-copper particles.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of in-situ nano copper paste and its preparation process and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] This embodiment provides an in-situ nano-copper paste, and using the in-situ nano-copper paste for sintering interconnection, such as figure 1 As shown, the preparation process is as follows:

[0046] S1. Preparation of nano-copper solution

[0047] Under the condition of 50°C, copper acetate and ascorbic acid were put into 500mL ethylene glycol solvent for reaction according to the molar ratio of 1:6, and the nano-copper solution was obtained after 20 minutes of reaction;

[0048] S2. Preparation of in-situ nano copper paste

[0049] Pour the nano-copper solution obtained in S1. into a centrifuge tube, centrifuge in a centrifuge for 5 minutes under the condition of 12000r / min, and then stir to obtain a uniform mass fraction of 80% in-situ nano-copper paste, nano-copper particles The particle size is 50-100nm.

[0050] Coat the paste on the copper substrate, cover the coated copper paste with the interconnect chip, put it into a hot-press furnace, and sinter it at 300°...

Embodiment 2

[0052] This embodiment provides an in-situ nano-copper paste, and using the in-situ nano-copper paste for sintering interconnection, such as figure 1 As shown, the preparation method is as follows:

[0053] S1. Preparation of nano-copper solution

[0054] Under the condition of 80°C, copper hydroxide and ascorbic acid were put into 400mL terpineol solvent for reaction according to the molar ratio of 1:10, and the nano-copper solution was obtained after reaction for 30 minutes;

[0055] S2. Preparation of in-situ nano copper paste

[0056] Pour the nano-copper solution obtained in S1 into a rotary evaporator and evaporate it for 30 minutes at a rotation speed of 120r / min, an evaporation temperature of 200°C, and a vacuum of 180Pa, take it out and stir to obtain a uniform mass fraction of 85% in situ The nano-copper paste, the particle diameter of the nano-copper particles is 50-100nm.

[0057] Coat this paste on a silicon substrate, cover the coated copper paste with an inte...

Embodiment 3

[0059] This embodiment provides an in-situ nano-copper paste, and using the in-situ nano-copper paste for sintering interconnection, such as figure 1 As shown, the preparation process is as follows:

[0060] S1. Preparation of nano-copper solution

[0061] Under the condition of 65°C, put copper acetylacetonate and glucose into 300mL ethylene glycol solvent for reaction according to the molar ratio of 2:1, and obtain nano-copper solution after 10 minutes of reaction;

[0062] S2. Preparation of in-situ nano copper paste

[0063] Filter the nano-copper solution obtained in S1. through a microfiltration membrane, take out the filtered nano-copper solution and stir to obtain an in-situ nano-copper paste with a uniform mass fraction of 78%, and the particle size of the nano-copper particles is 50-100nm .

[0064] Coat this paste on a silicon carbide substrate, cover the coated copper paste with an interconnection chip, put it into a hot-press furnace, and sinter it at 260°C and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides an in-situ nanometer copper paste and its preparation process and application. The preparation process of the in-situ nano-copper paste of the present invention is that the copper salt and the reducing agent are reacted in a solvent to obtain a nano-copper solution, and after concentration, the in-situ nano-copper paste is obtained, and the obtained in-situ nano-copper paste can be directly coated on the substrate Sintering is performed to realize in-situ interconnection. The nano-copper particles have good dispersion in the solution, and the original solution is directly concentrated to obtain the in-situ nano-copper paste, which can avoid the oxidation problem caused by the contact of the nano-copper particles with air, and can also avoid the agglomeration problem caused by the drying of the nano-copper particles , breaking the conventional thinking, and simplifying the preparation process of nano-copper paste, which is convenient, fast and efficient, and is conducive to large-scale production.

Description

technical field [0001] The invention relates to the technical field of material engineering, in particular to an in-situ nano copper paste and its preparation process and application. Background technique [0002] Traditional electronic packaging and interconnection materials mainly use solder paste or conductive adhesive, but none of them can meet the requirements of high-power devices. Therefore, nano-metal materials with unique physical and chemical properties have become a research hotspot for packaging and interconnection materials. After low-temperature sintering, nano-metals are close to the melting point, electrical conductivity and thermal conductivity of bulk metals, which can better meet the working environment of high-temperature service. Among them, nano-copper metal paste stands out for its advantages of low cost, easy availability of materials, and low electrical mobility. [0003] At present, the preparation of nano-copper paste generally adopts a two-step m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & AuthorityPatents(China)
IPC IPC(8): B22F9/24B22F1/00H01L21/60B82Y40/00B82Y30/00
CPCB22F9/24H01L24/80B82Y40/00B82Y30/00H01L2224/8084B22F1/0545B22F1/10
Inventor张昱刘强崔成强
OwnerGUANGDONG UNIV OF TECH